We investigated the mechanism how the high green density can be provided during die lubricated warm compaction (WD). We observed and analyzed the densification processes of iron powders including different contents of an inner lubricant, and measured the lateral pressure at the die wall during WD in comparison with conventional compaction and warm compaction. As a result, the high density in WD was due to not only the particles-deformation enhanced by warming powders but also the particles-rearrangement promoted by reducing an amount of the inner lubricant rather than the die lubrication.

The filling property of the binder treated iron based powder made of atomized iron powder was compared with that of the one made of reduced iron powder. The latter one showed a better filling property than the former one, although the original reduced powder showed a worse flow rate. Changing the particle size distribution of the original atomized powder from wide to narrow like the original reduced iron powder, improved the filling property of the binder treated powder. As a result, the particle size distribution of the original iron powder was found to strongly affect the filling property of the binder treated powder.

A developed molybdenum hybrid-alloyed steel powder is based on a molybdenum prealloyed steel powder to which molybdenum powder particles are diffusion bonded. The sintered compact made of this powder has a finer pore structure than that of the conventional molybdenum prealloyed steel powder, because the ferritic iron phase with a high diffusion coefficient is formed in the sintering necks where molybdenum is concentrated resulting in enhanced sintering. The rolling contact fatigue strength of the sintered and carburized compacts made of this powder improved by a factor of 3.6 compared with that of the conventional powder due to the fine pore structures.