In Jeju Island, red sea bream is mainly caught by long line with a live squid as bait. The movements of artificial jigs in the fishery are supposed to be an important factor for catching the target organism as well as bait. To develop new fishing method for long line fishery, movements of the bait which was squid were tried to be characterized. In a water tank experiment, a live squid was hooked by a fish hook attached to a model long line. And then movements of squids in the water tank were recorded for 20 minutes by a video camera. Recorded movement of the squid was just periodically up-and-down moving, with a dominant frequency of 0.125Hz, and amplitude of 10.8cm.

Mechanochemical synthesis of zinc ferrite, ZnFe2O4, was attempted from a powder mixture of iron (III) oxide, alpha-Fe2O3 and zinc (II) oxide, ZnO. Nanocrystalline zinc ferrite, ZnFe2O4 powders were successfully synthesized only bymilling for 30 hours. Evidence of the ZnFe2O4 formation was absent for the powders milled for 10 and 20 hours; the milling lowered the crystallinity of the starting materials. Heating after milling enhanced the formation of ZnFe2O4, crystal growth of ZnFe2O4 and the unreacted starting materials. The unreacted starting materials decreased their amounts by heating at higher temperatures.

We investigated the mechanism how the high green density can be provided during die lubricated warm compaction (WD). We observed and analyzed the densification processes of iron powders including different contents of an inner lubricant, and measured the lateral pressure at the die wall during WD in comparison with conventional compaction and warm compaction. As a result, the high density in WD was due to not only the particles-deformation enhanced by warming powders but also the particles-rearrangement promoted by reducing an amount of the inner lubricant rather than the die lubrication.

Powder library of pseudo four components Li-Ni-Co-Ti compounds were prepared for exploring the composition region with the single phase of the layer-type structure by using combinatorial high-throuput preparation system "M-ist Combi" based on electrostatic spray deposition method. The new layer-type compounds were found wider composition region than the previous report. This process is promising way to find multi component functional materials.

A developed molybdenum hybrid-alloyed steel powder is based on a molybdenum prealloyed steel powder to which molybdenum powder particles are diffusion bonded. The sintered compact made of this powder has a finer pore structure than that of the conventional molybdenum prealloyed steel powder, because the ferritic iron phase with a high diffusion coefficient is formed in the sintering necks where molybdenum is concentrated resulting in enhanced sintering. The rolling contact fatigue strength of the sintered and carburized compacts made of this powder improved by a factor of 3.6 compared with that of the conventional powder due to the fine pore structures.