The generation of TiO2 nanoparticles by a thermal decomposition of titanium tetraisopropoxide (TTIP) was carried out experimentally using a tubular electric furnace at various synthesis temperatures (700, 900, 1100 and 1300℃) and precursor heating temperatures (80, 95 and 110℃). Effects of degree of crystallinity, surface area and anatase mass fraction of those TiO2 nanoparticles on photocatalytic properties such as decomposition of methylene blue was investigated. Results show that the primary particle diameter obtained from thermal decomposition of TTIP was considerably smaller than the commercial photocatalyst (Degussa, P25). Also, those specific surface areas were more than 134.4 m2/g. Resultant TiO2 nanoparticles showed improved photocatalytic activity compared with Deggusa P25. This is contributed to the higher degree of crystallinity, surface area and anatase mass fraction of TiO2 nanoparticles compared with P25.

Catalytic activities of V2O5/TiO2 catalyst were investigated under reaction conditions such as reaction temperature, catalyst size, inlet concentration and space velocity. A 1,2-dichlorobenzene(1,2-DCB) concentrations were measured in front and after of the heated V2O5/TiO2 catalyst bed, and conversion efficiency of 1,2-DCB was determined from it's concentration difference. The conversion of 1,2-DCB using a pellet type catalyst in the bench-scale reactor was lower than that with the powder type used in the micro flow-scale reactor. However, when the pellet size was halved, the conversion was similar to that with the powder type catalyst. The highest conversion was shown with an inlet concentration of 100 ppmv, but when the concentration was higher or lower than 100 ppmv, the conversion was found to decrease. Complete conversion was obtained when the GHSV was maintained at below 10,000 h-1, even at the relatively low temperature of 250°C. Water vapor inhibited the conversion of 1,2-DCB, which was suspected to be due to the competitive adsorption between the reactant and water for active sites.

In this study, the fundamental experiments were performed for catalytic oxidation of NO (50 ppm) on MnO2 in the presence of ozone. The experiments were carried out at various catalytic temperatures (30-120℃) and ozone concentrations (50-150 ppm) to investigate the behavior of NO oxidation. The honeycomb type MnO2 catalyst was rectangular with a cell density of 300 cells per squuare inch. Due to O3 injection, NO reacted with O3 to form NO2, which was adsorbed at the MnO2 surface. The excessive ozone was decomposed to O* onto the MnO2 catalyst bed, and then that O* was reacted with NO2 to form NO3-. It was found that the optimal O3/NO ratio for catalytic oxidation of NO on MnO2 was 2.0, and the NO removal efficiency on MnO2 was 83% at 30℃. As a result, NO was converted mainly to NO3-.

This study examined the catalytic destruction of 1,2-dichlorobenzene on V2O5/TiO2 nanoparticles. The V2O5/TiO2 nanoparticles were synthesized by the thermal decomposition of vanadium oxytripropoxide and titanium. The effects of the synthesis conditions, such as the synthesis temperature and precursor heating temperature, were investigated. The specific surface areas of V2O5/TiO2 nanoparticles increased with increasing synthesis temperature and decreasing precursor heating temperature. In addition, the removal efficiency of 1,2-dichlorobenzene was promoted by a decrease in heating temperature. However, the removal efficiency of 1, 2-dichlorobenzene was decreased by an anatase to rutile phase transformation at temperatures 1,300℃.