The concrete track has been developed as an alternative to the ballast track due to its excellent maintenance. Recently, QHT(Quick Hardening Track) has been developed to rapidly replace ballast track to slab track. In bridge section, post-installation anchors should be installed at the center of QHT segment in order to unify the behavior of bridge and QHT. In this study, track-bridge interaction analysis was performed to check safety of anchor considering at early age of QHT.

콘크리트에서 염소 이온과 같은 열화물질의 이동은 응력상태 및 재령의 증가에 기인한 공극구조에 따라 변화한다. 본 연구에서는 재령 28일, 91일, 그리고 365일 양생된 OPC 콘크리트의 압축 및 인장 하중조건을 고려하여 촉진탄산화 실험을 실시하였으며, 탄산화 거동을 평가하였다. KS F 2584에 의거하여 탄산화 속도계수를 도출하였는데, 하중을 고려하지 않을 경우 탄산화 속도계수는 재령 28일 대비 재령 91일은 50.0 % 수준으로, 재령 365일에서는 44.8 % 수준으로 감소하였다. 28일 재령 시, 하중의 영향으로 인해 인장재하영역에서는 103.9 ~ 108.8 % 수준으로 압축재하영역에서는 91.9 ~ 104.6 % 수준으로 변화하였다. 재령이 증가함에 따라 탄산화 속도는 크게 감소하였는데, 30 % 인장재하영역에서는 탄산화 속도계수가 1년 경과시 47.3 % 수준으로, 60 % 인장재하영역에서는 52.5 % 수준으로 감소하였으며 30 % 압축재하영역에서는 45.8 %로, 60 % 압축재하영역에서는 44.9 % 수준으로 감소하였다. 압축재하영역 30 %에서는 공극압밀로 인해 탄산화 속도계수가 감소하였으나 하중의 증가에 따라 압축재하영역 60 %에서는 미세균열의 영향으로 탄산화 속도계수가 증가하였다. 또한 인장재하영역은 압축부와는 다르게 탄산화 속도계수가 선형적으로 증가하는 경향을 나타내었다.

In this study, the temperature correction strength (Tn) was conducted to propose (Tn) according to the management age of structural concrete that is separated from the average curing temperature of 4°C to 17°C in cold conditions. After reviewing the strength difference of the concrete using fly ash as a combined material at W/C 50%, the temperature correction strength (Tn) is proposed. The temperature correction strength was proposed to compensate for differences with standard curing conditions due to decrease in curing temperature from 28th, 42nd, 56th and 91st of the models interpreted as equivalent age methods.

This paper presents the findings of the study conducted to evaluate workability and compressive strength characteristics of rapid-setting concrete containing metakaolin. The experimental variable selected was the rate of cement replacement with metakaolin at 0, 5, 10, and 15 percent. The findings are summarized as follows: compared with the control specimens with no replacement rate, the workability and compressive strength of the concrete with 5% of cement replaced with metakaolin were comparable to those of control specimens at 4hours; however, at 72 hours, the compressive strength of the concrete with the same replacement rate was larger than the strength of the control specimens by 4.1%, while no increase in strength was observed at higher replacement rates, implying that the optimum replacement rate of cement with metakaolin is 5%.

In this study, concrete slab with insulation and non-insulated formwork was used to monitor and control its strength using a wireless sensor network with equivalent age method. As a result, the temperature and compressive strength of the structures were monitored without any problems, which revealed a good management tool.

화력발전의 부산물인 플라이 애쉬는 포졸란 반응을 통하여 조직구조를 개선하고 장기 강도 및 염화물 저항성에 매우 효과적이다. 본 연구에서는 28일 및 180일 재령의 보통 포틀랜트 시멘트 및 FA를 혼입한 콘크리트에 대하여 압축강도 및 염화물 저항성을 평가하였으며, 재 령의 증가에 따른 상관성을 평가하였다. 이를 위해, 물-결합재비(W/B)를 37%, 42%, 47%의 3가지 수준, Fly Ash를 시멘트 중량의 0%, 30%, 50%의 3가지 수준으로 나누어 총 9가지 배합을 설정하였으며, 28일 및 180일 재령 시, 압축강도, Tang‘s method에 의한 촉진확산계수, 그리고 ASTM C 1202, KS F 2711을 통한 통과전하량을 측정하였다. Fly Ash 혼입율이 클수록, W/B가 낮을수록 염화물 저항성(확산계수 및 통과전하 량)이 개선되었는데, 모든 FA 50 배합에서 염화물 저항성은 재령 28일 대비 재령 180일에서 약 15% 수준으로 감소하였다. 이는 FA의 포졸란 반응으로 인해 공극구조가 더 치밀해져 나타난 결과이며, 염해 저항성이 강도보다 시간에 더욱 의존적임을 알 수 있다. 재령 180일 이후, FA를 혼입한 배합에서 강도와 염해저항성의 뚜렷한 선형관계가 관측되었다.

This paper presents evaluation of diffusion coefficient, passed charge, and compressive strength considering 3 substitution ratios of fly ash(0%, 30%, and 50%) and 3 different W/B ratios(37%, 42%, and 47%). Also, the relationships among diffusion coefficient, passed charge, and compressive strength are investigated focusing on the results at 28 days and 180 days. With increasing replacement ratio of FA and decreasing W/B, the resistances to chlorides(diffusion coefficient and passed charge) are improved. At 28 days and 180 days, linear relationship are observed between strength and resistance to chloride on the whole.

In the work, HPC (High Performance Concrete) samples are prepared with 3 levels of W/B (water to binder) ratios of 0.37, 0.42, and 0.27 and 3 levels of replacement ratios of 0%, 30% and 50%. Several tests containing chloride diffusion coefficient, passed charge, and compressive strength are performed considering age effect of 28 days and 180 days. Chloride diffusion is more reduced in OPC concrete with lower W/B ratio, and GGBFS concrete with 50% replacement ratio shows significant reduction of chloride diffusion in higher W/B ratio. At the age of 28 days, GGBFS concrete with 50% replacement ratio shows more rapid reduction of chloride diffusion than strength development, which reveals that abundant GGBFS replacement has effective resistance to chloride penetration even in the early-aged condition.

This paper presents evaluation of diffusion coefficient, passed charge, and compressive strength considering 3 substitution ratios of fly ash(0%, 30%, and 50%) and 3 different W/B ratios(37%, 42%, and 47%). Also, the relationships among diffusion coefficient, passed charge, and compressive strength are investigated focusing on the results at 28 days and 180 days. With increasing replacement ratio of FA and decreasing W/B, the resistances to chlorides(diffusion coefficient and passed charge) are improved. At 28 days and 180 days, linear relationship are observed between strength and resistance to chloride on the whole.

In the work, HPC (High Performance Concrete) samples are prepared with 3 levels of W/B (water to binder) ratios of 0.37, 0.42, and 0.27 and 3 levels of replacement ratios of 0%, 30% and 50%. Several tests containing chloride diffusion coefficient, passed charge, and compressive strength are performed considering age effect of 28 days and 180 days. Chloride diffusion is more reduced in OPC concrete with lower W/B ratio, and GGBFS concrete with 50% replacement ratio shows significant reduction of chloride diffusion in higher W/B ratio. At the age of 28 days, GGBFS concrete with 50% replacement ratio shows more rapid reduction of chloride diffusion than strength development, which reveals that abundant GGBFS replacement has effective resistance to chloride penetration even in the early-aged condition.

본 논문은 폴리머 모르타르로 보수된 철근콘크리트 보의 휨거동을 실험적 ·해석적으로 분석한 결과를 제시한다. 실험적 연구에서 는 보수위치, 모르타르 재령을 실험변수로 고려하여 제작된 13개의 보에 대한 3점 휨실험이 실시되었다. 인장측 및 압축측을 보수한 실험체들 의 파괴는 모르타르와 콘크리트의 계면에서 발생하지 않았으며, 폴리머 모르타르의 인장변형률이 극한변형률을 초과하는 순간 발생하였다. 압축측을 보강한 실험체들은 기준실험체의 최대하중과 유사하였다. 그들의 연성지수는 기준실험체보다 훨씬 컸다. 인장측을 보수한 실험체 는 매우 취성적으로 파괴되었으며, 연성지수가 크게 감소하였다. 폴리머 모르타르로 보수된 철근콘크리트의 보의 휨거동을 예측하기 위해 Opensees을 사용한 재료비선형 해석을 진행하였다. 해석 모델을 단순화하기 위해 2차원 골조요소를 적용하였으며, 재료 비선형성을 고려하기 위해 파이버 모델을 적용하였다. 해석결과는 비선형 구조해석은 압축측 보수 실험체의 휨거동을 적절하게 예측하나, 인장측 휨거동는 다소 과 대 평가하는 것으로 나타났다.

본 연구에서는 산업부산물인 TDFA를 혼입한 콘크리트에 대하여 초기재령의 공학적 특성을 분석하였다. 물-결합재비 0.5, FA 치환 율 20%인 콘크리트를 대상으로 TDFA를 3~12%치환하여 경화 전 및 경화 후의 특성을 분석하였다. TDFA 혼입율 6% 이후의 배합에서는 작업 성이 현저하게 감소하였고 공기량 확보가 어려웠으며, 이로 인해 감수제 및 공기연행제를 추가하여 작업성을 개선시켰다. TDFA 혼입율 6~12% 까지는 콘크리트의 강도에 큰 영향은 없었으며, 탄산화저항성 및 염해저항성에서는 FA 20% 치환 배합보다 우수한 성능을 나타내었다. 그러나 공기량이 부족한 TDFA 혼입율 6%배합에서는 동결융해 저항성이 크게 감소하였다. 공기량 및 작업성이 확보된다면 FA를 12%수준까지 TDFA로 치환해도 공학적인 성능을 확보할 수 있을 것으로 판단된다.

콘크리트의 강도를 평가하기 위하여 반발경도법과 초음파속도법이 폭넓게 사용되고 있다. 그러나 재료의 상태뿐만 아니라 콘크리 트의 재령, 성숙도 및 손상도 등에 따라 예측강도와 현장의 실제강도가 차이가 발생하게 된다. 표준공시체와 현장에서 드릴링에 의하여 채취하 는 코어공시체의 압축강도는 드릴링하는 동안 기계에 의한 교란이 발생하여 압축강도에 영향을 미치게 된다. 또한 반발경도 및 초음파속도의 경우에도 콘크리트의 재령 및 성숙도가 변화함에 따라 표면의 경도와 내부 미세조직의 변화에 의해서도 변화하게 된다. 저자들은 재령와 코어 의 영향을 비파과시험결과에 반영하기 위하여 실험을 실시하였으며, 코어 및 콘크리트 재령에 의한 영향을 압축강도 실험 및 예측결과와 비교 분석하였다.

This paper describes the findings of the study conducted to evaluate early-age strength characteristics of rapid-setting concrete containing waste pottery powder. The experimental variables selected were 5, 10, and 15 percent replacements of cement with waste pottery powder. The findings are summarized as follows: (1) slump of the concrete decreased as the replacement rate of cement with waste pottery powder increased, and (2) compared with the strength of the control specimens with no replacement rate, compressive strength of concrete increased at 5% replacement rate, and was comparable to the control at 10% replacement rate; however, at 15% replacement rate, compressive strength actually decreased.

In this paper, evaluation of compressive strength development of concrete cured by microwave heating system is introduced. For this evaluation, core strength tests were conducted. Test results show that the development was accelerated by microwave heating system. And two parameters in a equation for predicting initial strength development were presented when using this system.

Industrial by-products in combination with FA, BS was excellent compressive strength, chloride penetration resistance by OPC 60(W/C 60%) based on the comparative analysis. The most effective periods were BS 28 days and FA 56 days.

Time dependent finite element formulation for age-dependent torsional analysis of prestressed concrete flexural member was derived based on the time-independent finite element formulation. In the formulation, torsional creep was considered to predict torsion behavior of beam structure. Two-span prestressed double T-beam was analyzed to observe the effect of torsion creep.

Reaction degree of ground granulated blast furnace slag(GGBFS) in cement paste was measured by water-binder ratio and GGBFS replacement ratio, curing temperature with ages using selective dissolution. In result of experimental, when water-binder ratio and curing temperature were high and replace ratio of GGBFS was low, reaction degree was estimated high.

To evaluate the quality of the concrete cover a research project using non destructive air permeability measurements is carried out. Measurements were conducted in the laboratory as well as on concrete structures.

This study investigated the compressive strength of concrete by using ultrasonic pulse velocity method, and proposed the equation able to predict the compressive strength of concrete.