This study investigated the effect of surface water on concrete substrate on adhesive strength in tension of very high flowable SBR-modified cement mortar. Polymer cement ratio(P/C) were 10, 20, 30, 50 and 75% and the weight ratio of fine aggregate to cement were 1:1 and 1:3. The specimens obtained with different P/C and C:F were characterized by unit weight, flow test, crack resistance and adhesion test. Three selected specimens among these tested specimens were studied about the effect of surface water evenly sprayed on concrete substrate on adhesive strength.

자류철석 표면에 부착한 고온성박테리아들과 이차 생성물을 전자현미경분석을 통하여 조사하였다. 일본 산성 온천수에서 채취된 고온성박테리아를 자류철석에 42℃, 52℃, 62℃에 각각 접종하였다. 반응된 자류철석 표변에는 2차 생성물과 막대 모양의 박테리아들이 각각 부착하여 나타났다. 자류철석 표면에 부착한 박테리아들의 크기는 0.4×1.5μm에서 0.3×11.9μm 범위였다. 박테리아들은 세포외중합체물질을 생성하는 것으로 관찰되었으며 이들 세포외중합체물질의 기능은 극한 환경으로부터 박테리아 자신을 보호하는 보호막 역할을 하는 것으로 추정되었다. 원소 황, 철수산화물, S와 Fe로 구성된 결정들, 그리고 O, P, Fe 결정들이 2차 생성물로 관찰되었다.

This paper discussed effect of the surface roughness and the hydrophobicity of support material on the microbial attachment in a rotating biological contactor. The hydrophobicity of each support material was determined by the measurement of contact angle of water and the surface roughness was measured by the surface roughness instrument. Microorganisms have well attached on the surface of more hydrophilic support material like Nylon6 than that of the hydrophobic support material like PE. When the relatively hydrophilic surface was roughen, the microbial attachment was increased but when the relatively hydrophobic surface was roughen, the attachment was slightly increased because the hydrophobicity of support material was increased by roughening the hydrophobic surface. Although both variables, the surface hydrophobicity and the surface roughness, have influenced the microbial attachment, the influence of the surface roughness overruled that of the surface hydrophobicity. Support material whose surfaces were roughened about l㎛, 6㎛ and 11㎛ were allowed for attached 3, 7 and 24hr, but the differences of maximum and minimum attachment of each material gave nearly constant values and similar trend with time.