In this work, we report a direct preparation of a few-walled carbon nanotube (FWCNTs) and NiMgAl composites namely FWCNT-NiMgAl by pyrolysis of waste high-density polyethylene (HDPE) plastic at 800 °C with NiMgAl-layered double hydroxide (LDH) as catalysts. The composite formation is carried out in a single step using our lab-developed pyrolysis reactor. The NiMgAl-LDH catalyst was prepared by co-precipitation method and the FWCNTs were grown on the NiMgAl-LDH catalyst with FWCNT yield of 10% and FWCNT-NiMgAl composite yield of 55% whose quality is determined by Raman ID/IG ratio of 2.57. The average outer and inner diameter of the FWCNT are found to be 5.5 nm and 2.9 nm, respectively, from TEM and 2.92 nm from the outer RBM (radial breathing mode) band, which indicates the formation of a few-walled CNTs. FWCNT-NiMgAl is used for the fabrication of flexible supercapacitor electrodes on a polyethylene terephthalate (PET) sheet which achieved a specific capacitance of 432 Fg− 1 in a wide potential range (ΔV = 2) at a scan rate of 5 mV s− 1 in 2 M KOH electrolyte with a high energy density of 240 Wh kg− 1, whereas NiMgAl displayed a capacitance of 200 Fg− 1 with an energy density of 111 Wh kg− 1. The diffusion-type charge storage mechanism (pseudocapacitance) is found to be dominant with contributions of 73.2% and 69.75% for NiMgAl and FWCNT-NiMgAl, respectively. The highest specific capacitance and energy density are obtained for NiMgAl in 2 M KCl and for FWCNT-NiMgAl in 2 M NaOH electrolytes. However, the largest potential window is observed in KOH electrolyte for both NiMgAl and FWCNT-NiMgAl with value of ΔV = 2 V. The electrode material shows good stability in acidic electrolytes and also shows good capacitive stability at high frequencies maintaining a phase angle of 70°. The present work is a novel approach to fabricate low-cost multifunctional carbon composite nanomaterials and will contribute to the research on low-cost waste-derived CNT composite preparation and its application in flexible energy storage devices.

To solve the problem of water pollution, researchers have proposed a photocatalytic degradation technology, in which the key factor is the development of efficient photocatalytic materials. Graphitic carbon nitride (g-C3N4), an n-type semiconductor, has been widely studied due to its suitable band gap (2.7 eV), low cost, easy preparation, non-toxicity, and high photostability. However, the pure-phase g-C3N4 still has defects such as low specific surface area, insufficient visible light absorption, low charge mobility, few active sites for interfacial reaction, and easy recombination of photogenerated electron–hole pairs, which leads to the lower photocatalytic activity of g-C3N4. Aiming at the problems mentioned above, this paper focus on the synthesis of g-C3N4-based composites with high photocatalytic activity via lemon juice induction method. Thiourea and lemon juice were selected as precursors, and carbon quantum dots (CQDs) as electron mediators were introduced anchoring on the surface of g-C3N4 to build g-C3N4/CQDs with compact interface. The results showed that small-sized CQDs are uniformly distributed on the surface of g-C3N4, and the g-C3N4/CQDs composite has a 2D0D structure, which reduces the recombination of photogenerated electron–hole pairs. The photocatalytic degradation efficiency of 4% g-C3N4/CQDs for RhB reaches the highest data of 90.9%, and the photocatalytic degradation rate is 0.016 min− 1, which is about 2.3 times that of g-C3N4. After four cycles of photocatalytic reaction, the photocatalytic degradation efficiency of the material remained at 81.7%. Therefore, the g-C3N4/CQDs synthesized via lemon juice induction has a more stable microstructure, and the charge separation efficiency is greatly improved, which is suitable for practical photocatalytic environmental protection.

Here, we have demonstrated the successful exfoliation of graphite into a layered material with scotch tape-like exfoliation. Sulfur acts as an exfoliating agent and exfoliates the loosely bounded graphite stacks. The shear force by ball milling provides the force required to overcome the van der Waals force between the layers. The MnO2 nanorods were synthesized using a KMnO4 precursor in a hydrothermal arrangement, and due to their intrinsic chemisorption capability, they were doped for polysulfide trapping. With an initial capacity of 1150 mAh/g achieved by the MnO2 nanorod-doped exfoliate-graphite/sulfur composite material, the material has displayed its application in lithium–sulfur batteries, but its use is not limited; it can be a low-cost eco-friendly solution to various energy storage systems with extensive structural qualities.

For graphene oxide (GO) composite hydrogels, a two-dimensional GO material is introduced into them, whose special structure is used to improve their properties. GO contains abundant oxygen-containing functional groups, which can improve the mechanical properties of hydrogels and support the application needs. Especially, the unique-conjugated structure of GO can endow or enhance the stimulation response of hydrogels. Therefore, GO composite hydrogels have a great potential in the field of wearable devices. We referred to the works published in recent years, and reviewed from these aspects: (a) structure of GO; (b) factors affecting the mechanical properties of the composite hydrogel, including hydrogen bond, ionic bond, coordination bond and physical crosslinking; (c) stimuli and signals; (d) challenges. Finally, we summarized the research progress of GO composite hydrogels in the field of wearable devices, and put forward some prospects.

Most of the wastes generated when dismantling nuclear power plant were contaminated with lowlevel radioactive materials, therefore, applying a plasma melting system is a good option to dispose of the complex wastes safely. Melting system with plasma technology was developed to dispose single metal or composite objects. Its purpose is to secure final emissions satisfying final treatment conditions by controlling oxidization/ reduction reaction condition in detail during the melting process. A hollow plasma torch applied at plasma melting system could be operated with various plasmaforming gasses such as N2, Air, Ar, O2, and etc. The melting furnace was designed based on a double sealing structure to prevent risk factors; such as leaks, etc. in the reaction condition. The effect of the external air inflow on the melting conditions was minimized by carefully designing the object input device, torch mounting part, final object discharge part, etc.

The ZnO–Na2Ti6O13 composites were synthesized by facile solution combustion method with different molar concentrations of sodium titanate which is prepared by hydrothermal route. The formation of the composites was confirmed by the X-ray diffraction (XRD) analysis. Field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM) results revealed that the synthesized composites exhibit porous morphology, whereas the pristine Na2Ti6O13 nanoparticles have whisker like morphology. Diffuse reflectance spectroscopy (DRS) and photoluminescence (PL) studies were utilized to compute the bandgap and the presence of defects in the composites respectively. The photocatalytic activity of ZnO–Na2Ti6O13 catalyst was investigated through the degradation of 4-nitrophenol under solar light over a period of 180 min and the composite with 0.05 M of Na2Ti6O13 showed higher degradation efficiency (96%) than the other concentrations of Na2Ti6O13 and pristine ZnO. The reduced bandgap, high charge transfer, more oxygen vacancies and the production of high superoxide anion radicals have profound effect on the higher photocatalytic efficiency of the composite with 0.05 of M Na2Ti6O13.

CNTs/Al-Li composite was first prepared by hot-pressed sintering from Al-Li alloy powder and CNTs solution, and then the hot compression tests were performed on MMS-100 thermal simulator at strain rate range of 0.01– 10 s− 1, deformation temperature range of 350–500 °C, and total deformation amount of 60%. True stress–strain curves were plotted, and constitutive equation as well as hot processing maps were successfully confirmed based on Arrhenius constitutive model and Prasad instability criterion. Results show that CNTs/Al-Li composite have a very poor hot deformation ability and narrow processing region, which is strain rate range of 0.1–1 s− 1 and deformation temperature range of 360–400 °C. Hot extrusion experiment was carried out and the processing parameters were selected according to the established hot processing map, and an improvement on strength and a good balance between strength and plasticity can be obtained, which is about 650 MPa for tensile strength and 9% for elongation.

A composite photocatalyst of zinc oxide (ZnO) nanoparticles decorated with different content of reduced graphene oxide (rGO) was prepared via a simple and facile one-step method in this paper. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectra, and UV–Vis diffuse reflection spectroscopy (UV–Vis DRS) were used to characterize the crystal structure, morphology and optical properties of the rGO–ZnO composite photocatalyst. The photocatalytic properties of the composites were investigated using methyl orange (MO), a typical orange compound, as a test pollutant. The results showed that rGO–ZnO composites displayed significantly enhanced photocatalytic activity in MO degradation than pure ZnO, and the pseudo-first-order kinetic constant on the optimal rGO–ZnO composite was 14 times as great as that on pure ZnO. The enhanced photocatalytic ability of the rGO-ZnO composites was mainly benefited from the high specific surface area and high conductivity of rGO, which facilitated efficient charge separation in the rGO-ZnO nanocomposite.

본 연구는 다중벽 탄소나노튜브(MWCNT)로 보강된 복합재 구조의 동적 해석을 다루었다. Mori-Tanaka 모델을 기반으 로 MWCNT 중량 비율, 패널의 곡률, 그리고 CNT의 임의 배열이 복합재의 동적거동에 미치는 상호작용을 연구하였다. 본 연구 결과는 CNT의 부피함유비율의 변화에 따른 복합재의 유효탄성계수를 예측하는 기존 문헌결과와 비교하여 검증하였다. 수치해 석 예제는 복합재의 동적 특성을 평가함에 있어서 MWCNT 보강의 불규칙한 배열 또는 기울어진 방향으로 배치된 효과에 대한 중요성을 제시하였다.

최근 경주, 포항에 연이은 지진 발생으로 인하여 내진설계에 관심이 높아지고 있다. 다가구주택 필로티기둥은 수직 비정형 시스템으로 상,하부층의 강성 차이로 인하여 지진 발생 시 막대한 피해가 예상되기 때문에 다가구주택 필로티기둥의 내 진보강이 필요하다. 그러나 민간 소유인 다가구주택의 경우 막대한 비용과 시간으로 인하여 보강이 어려운 실정이다. 이에 따 라, 복합섬유패널로 에폭시 접착제 미사용으로 건식시공이 가능한 전단보강공법을 제안하고자 한다. 본 연구에서는 복합섬유패 널 보강 유무에 따른 내진보강공법의 전단내력을 실험을 통하여 검증하였고, 에폭시를 사용하지 않아 일체화 거동을 하지는 않 지만 복합섬유패널의 영향으로 전단내력은 1.46∼1.49배 증가하는 것으로 평가되었다. 따라서 다가구주택 필로티기둥의 내진보 강효과가 있을 것으로 판단된다.