This study evaluated the enhancement of microstructural and mechanical properties of a cross rolled Ni-10Cr alloy, comparing with conventionally rolled material. Cold rolling was carried out to 90% thickness reduction and the specimens were subsequently annealed at 700˚C for 30 min to obtain a fully recrystallized microstructure. Cross roll rolling was carried out at a tilted roll mill condition of 5˚ from the transverse direction in the RD-TD plane. In order to observe the deformed microstructures of the cold rolled materials, transmission electron microscopy was employed. For annealed materials after rolling, in order to investigate the grain boundary characteristic distributions, an electron back-scattering diffraction technique was applied. Application of cold rolling to the Ni-10Cr alloy contributed to notable grain refinement, and consequently the average grain size was refined from 135 μm in the initial material to 9.4 and 4.2 μm in conventionally rolled and cross rolled materials, respectively, thus showing more significantly refined grains in the cross rolled material. This refined grain size led to enhanced mechanical properties such as yield and tensile strengths, with slightly higher values in the cross rolled material. Furthermore, the<111>//ND texture in the CRR material was better developed compared to that of the CR material, which contributed to enhanced mechanical properties and formability.
Titanium alloys have been attractive due to a high ratio of strength to weight as well as good corrosion resistance. However, strengthening causes a decrease in ductility in Ti alloys, as is usual in other alloys. For enhanced strength without ductility reduction, grain refinement and tensile properties were investigated as functions of thickness reduction of cold rolling and annealing condition in Ti-15V-3Cr-3Sn-3Al alloy with a β single phase. The average grain size of the specimen, which was cold-rolled by 90% and annealed at 700˚C for 5 min, was decreased to approximately 19 μm. The grain refinement of 63 μm to 19 μm increased yield stress by 90 MPa without a significant decrease in total elongation. The Ti-15-3 alloy exhibited very low work hardening during tensile test at a crosshead speed of 2 mm/min. This result was discussed based on dynamic recovery associated with dislocation annihilation in grain boundaries.
본 연구는 냉간가공과 열처리를 통해 Cu-26.65Zn-4.05Al-0.31Ti(wt%) 형상기억합금의 결정립을 미세화하기 위한 목적으로 수행하였다. 냉간가공을 위하여는 α-상이 가능한 많이 존재하는 (α+β)-조직을 가져야 하는데, 이는 550℃에서 열처리함으로써 얻었고, 최종두께 1mm로 냉간압연하였다. 총 압연율은 70%와 90%이었다. 냉간압연한 판재를 800℃에서 가열 후 급랭함으로써 형상기억특성을 갖는 상으로 변태시켰으며, 이 대 결정립크기를 측정한 결과, 열간압연한 경우보다 냉간압연과 열처리를 한 경우의 결정립이 월등히 작아졌음을 보여주었다. 냉간압연과 열처리를 한 경우에는 냉간압연 변형율이 큰 경우가 결정립이 더 작아지는 경향을 보였다. 또한 결정립크기가 작아짐에 따라 변태온도가 저하되었으며 오스테나이트상이 더 안정하게 되었음을 확인할 수 있었다. In this study, cold-rolling and appropriate annealing was adopted for the grain refining of Cu-26.65Zn-4. 05Al-0.31Ti(wt%) shape memory alloy. For the cold deformation of this alloy the ducti1e α-phase must be contained. After heat treatment at 550℃ the (α+β)-dual phase with 40vol.% α-phase was obtained which could be rolled at room temperature. This alloy was cold rolled into a final thickness of 1.0mm with total reduction degrees of 70% and 90%. The rolled sheets were betanized at 800℃ for various times, then quenched into ice water. The grain size of co]d rolled samples were 60∼80 ㎛ which is much smaller comparing with the hot-rolled samples. And the 90% rolled sample showed smaller grain size than the case of the 70% rolled one. The small grain size had influence on the phase transformation temperatures and stabilization of the austenitic phases.