Porous carbons have been widely used as electrode material for supercapacitors. However, commercial porous carbons, such as activated carbons, have low electrochemical performance. Nitrogen-doping is one of the most promising strategies to improve electrochemical performance of porous carbons. In this study, nitrogen self-doped porous carbon (NPC) is prepared from melamine foam by carbonization to improve the supercapacitive performance. The prepared NPC is characterized in terms of the chemical structures and elements, morphology, pore structures, and electrochemical performance. The results of the N2 physisorption measurement, X-ray diffraction, and Raman analyses reveal that the prepared NPC has bimodal pore structures and pseudo-graphite structures with nitrogen functionality. The NPC-based electrode exhibits a gravimetric capacitance of 153 F g−1 at 1 A g−1, a rate capability of 73.2 % at 10 A g−1, and an outstanding cycling ability of 97.85% after 10,000 cycles at 10 A g−1. Thus, the NPC prepared in this study can be applied as electrode material for high-performance supercapacitors.

본 연구에서는 다공성 활성탄소와 금속유기골격체 복합재료 기반의 전극 재료와 “이온젤” 이라고 불리는 고분자 고체 전해질을 이용하여 슈퍼커패시터를 제작 하였으며, 금속유기골격체의 함량에 따른 전기화학적 거동을 관찰하여 보았다. 슈퍼커패시터의 전기화학적 특성은 순환전압전류법(CV), 전기화학적 임피던스 분광법(EIS) 및 전정류 충·방전법(GCD)으로 분석하였으며, 그 결과로, 다공성 활성탄소 대비 금속유기골격체를 0.5 wt% 첨가 하였을 때 가장 높은 전기용량값을 확인 할 수 있었으며, 0.5 wt% 이상의 금속유기골격체의 함유량은 전기화학적 특성 감소에 영향을 주는 것으로 사료되며, 이러한 결과를 바탕으로 제조된 다공성 활성탄소/금속유기골격체 복합재료 기반의 슈퍼커패시터는 다양한 분야에 활용이 가능 할 것으로 판단된다.

본 연구에서는 “이온젤” 이라고 불리는 고분자 기반의 PVA(polyvinyl alcohol) 기반의 고체 전 해질에 이온성 액체 BMIMBF4 (1-buthyl-3-methylimidazolium tetrafluoroborate)를 첨가하여 제조한 전 고체 전해질과 활성탄소와 금속유기골격체 복합재료 기반의 전극 재료를 이용하여 슈퍼커패시터를 제작 하였으며, 유기골격체의 유 무에 따른 전기화학적 특성을 분석하여 보았다. 슈퍼커패시터의 전기화학적 특 성은 순환전압전류법(CV), 전기화학적 임피던스 분광법(EIS) 및 전정류 충·방전법(GCD)을 통하여 비교 및 분석하여 보았다. 그 결과로, 금속유기골격체가 함유되지 않은 슈퍼커패시터의 전기용량값은 380 F/g 으로 확인 할 수 있었고, 이 값은 금속유기골격체를 첨가하였을 때 340 F/g로 감소하는 현상을 확인할 수 있었 다. 이러한 결과로 1 wt%의 금속유기골격체의 함유량은 전기화학적 특성 감소에 영향을 주는 것으로 사료 되며 이러한 결과를 바탕으로 금속유기골격체의 첨가량을 최적화 할 필요가 있다고 판단된다

Porous materials such as polymeric foam are widely adopted in engineering and biomedical fields. Porous materials often exhibit complex nonlinear behaviors and are sensitive to material and environmental factors including cell size and shape, amount of porosity, and temperature, which are influenced by the type of base materials, reinforcements, method of fabrication, etc. Hence, the material characteristics of porous materials such as compressive stress-strain behavior and void volume fraction according to aforementioned factors should be precisely identified. In this study, unconfined uniaxial compressive test for two types of closed-cell structure polyurethane foam, namely, 0.16 and 0.32 g/cm3 of densities were carried out. In addition, the void volume fraction of three different domains, namely, center, surface and buckling regions under various compressive strains (10%, 30 %, 50 % and 70 %) were quantitatively observed using Micro 3D Computed Tomography(micro-CT) scanning system. Based on the experimental results, the relationship between compressive strain and void volume fraction with respect to cell size, density and boundary condition were investigated.

Porous TiNi bodies were produced by Self-propagating High-temperature Synthesis (SHS) method from a powder mixture of Ti and Ni. Porosity, pore size and structure, mechanical property, and transformation temperature of TiNi product were investigated. The average porosity and pore size of produced porous TiNi body are 63% and , respectively. XRD analysis showed that the major phase of produced TiNi body is B2 phase. Its average fracture strength and elastic modulus measured under dry condition were MPa and GPa, respectively. It could be strained up to 7.3 %. The transformation temperatures determined by DSC showed the temperature of and temperature of .

삼차원적 골격구조를 가지며 세공의 크기와 산성도가 유사한 SAPO-44, SAPO-34(CHA type), SAPO-17(ERI type), 그리고 1차원적 고격구조를 가진 ZSM-23(MTT type) 촉매재료를 합성하고, 메탄올 전환방응에 있어서의 촉매적 성능을 비교 검토하였다. 이들의 산성도 세기는 SAPO-44>SAPO-34>SAPO-17>ZSM-23 순으로 나타났다. 메탄올 전환반응을 비교한 결과, 삼차원적 골격구조를 가지고 있는 SAPO-34와 SAPO-44에서 높은 에티렌 선택성이 얻어졌으며, 특히 Ni을 골격내에 도입시켰을 때 그 선택율은 더욱 증가하였다. 반면에 1차원적 골격구조를 가지고 있는 ZSM-23에서는 입체적 형상선택성의 감소로 올레핀보다는 파라핀의 선택율이 우세하였다.

본 연구에서는 최근 환경재료로서 관심이 모아지고 있는 다공성 콘크리트를 하천구조물(보 및 하상재료)에 적용함으로써 수질을 개선하고자 수행하였다. 먼저, 물리ㆍ화학적 특징을 평가해 본 결과, 공극률 10% 및 30%의 다공성 콘크리트의 압축강도는 일반 콘크리트의 최저 압축강도(180 kgf/)를 상회하여 하천구조물에 적용 가능하였고, 알칼리 용출에 의한 부착 미생물에의 영향도 거의 없을 것으로 판단되었다. 또한, 일반 콘크리트와 다공성 콘크리트로 하천구조