Recently, as the demand for a non-contact liquid crystal alignment method capable of improving viewing angle characteristics has spread throughout the industry, various non-contact liquid crystal alignment methods, including conventional UV light alignment, are being actively studied. In the case of UV light alignment, it is currently applied to mass production in many fields and shows relatively excellent initial characteristics, but there is a problem of display quality deterioration over time. In this study, among these non-contact liquid crystal alignment methods, the liquid crystal is oriented by quantitatively irradiating an ion beam onto the SiOF inorganic film, which has excellent initial characteristics and does not cause deterioration in quality over time., the electro-optical properties were evaluated by manufacturing a commercial-level IPS (In-Plane Switching) liquid crystal cell. In particular, in the case of such inorganic film orientation, it is common to have many problems with orientation stability, but the evaluation cell manufactured by the method proposed in this study is capable of maintaining a uniform orientation without losing orientation even after heat treatment at a high temperature of 200°C. could be observed.

Sand casting 3D printing uses a binder jetting method to produce a mold having complicated shape by spraying a binder on sand coated with activator. Appropriate heat treatment process in sand mold fabrication can increase the degree of polymerization to improve flexural strength. However, long heat treatment of over 24 hours decreases flexural strength and reliability due to chemical bond decomposition through thermal degradation. The main role of the activator is to control the reaction rate between the polymer chains. As a result, when the activator composition is increased from 0.15 wt% to 0.25 wt%, the flexural strength is increased by 218 N/cm2. However, excess activator (0.40 wt%) has been shown to decrease reliability without increasing flexural strength. The main role of the binder is to control the flexural strength of the specimen. As the binder composition is increased from 2.00 wt% to 4.00 wt%, the flexural strength increases to about 255 N/cm2, indicating the maximum flexural strength increase. Finally, the reliability of the flexural strength of the fabricated specimens is evaluated by a Weibull plot. Weibull modulus calculations are used to evaluate the flexural strength reliability of the specimens, and maximum reliability value of 11.7 is obtained at 0.20 wt% activator composition. Therefore, it is confirmed that this composition has maximum flexural strength reliability.

본 연구에서는 서로 다른 터치스크린용 Ag pastes를 스크린 인쇄 방식으로 ITO film 위에 전도성 패턴을 형성하고 10장씩 인쇄하여 130℃ 10분 동안 건조 하였다. 여기서 130℃ 10분의 건조 조건은 ITO film의 열화가 발생하지 않는 조건이다. 신뢰성 테스트는 염수테스트와 고온고습테스트를 진행한다. 각 테스트는 2장씩의 전도성 패턴 상태를 확인한다. 전도성 패턴을 침적 시킨 염수(NaCl 5% 녹인 증류수)를박스형 열풍 건조기(35℃)에서각 24, 48, 72시간 마다 상태를 확인하고 고온고습기(60℃ 90%)에서는 각120, 240시간 마다 상태를 확인하였다. 이런 신뢰성 테스트를 통해 서로 다른 Ag pastes의 접착력, 전도성의 변화 등을 알 수 있어 품질 저하를 막을 수 있고, 신뢰성 테스트에서 표면의 산소함량이 많은 Ag paste는 변색이 빨리 올 수 있음을 알 수 있었다.

무딘 모양 물체의 대표적 형상인 정사각주의 후류에서의 와류 형성 분석을 위한 스트롤수 측정 실험에서 실험 방법 및 결과의 신뢰성 확보를 위하여 실험계획법과 불확실성 해석을 수행하였다. 스트롤수는 정사각주와 지면과의 간극을 변화시키면서 열선유속계를 사용하여 측정하였다. 정사각주가 지면과 충분히 떨어져 있다면, 후류의 어느 곳에서 스트롤수를 측정하더라도 신뢰할 수 있다. 그러나 정사각주가 지면과 가까워지면 와류가 부분적으로 약하게 형성되기 때문에 스트롤수는 후류의 일정한 영역에서만 측정할 수 있으며, 신뢰할 수 있는 값을 얻기가 쉽지 않다. 이에 요인배치법과 분산분석을 이용하여 5% 유의수준에서 신뢰할 수 있는 스트롤수 측정 구역을 확보하였다. 마지막으로 불확실성 해석을 실시하여 실험 환경 및 계측 장비로부터의 오차 요인을 분석하였으며 스트롤수에 대한 95% 신뢰구간을 구하였다.

연약지반에 시공된 지반구조물의 거동은 구조물 하부의 연약지반이나 인접 지반의 특성에 크게 영향을 받는다. 지반 구조물 설계시 사용되는 지반 특성치는 결정론적인 모델이나 확률론적인 모델을 이용하여 나타낼 수 있다. 일반적인 지반구조물 설계시 사용되는 결정론적인 모델은 설계 파라메타로 단 하나의 대표값을 사용하는 반면, 확률론적인 모델은 이산통계나 확률 밀도함수를 이용한다. 연약지반의 압밀도나 침하량등의 산정 결과는 간극비, 압밀계수, 연직 및 수평방향 투수계수등의 불확실성 요소에 영향을 받는다. 본 연구에서는 연직 드레인을 이용한 개량지반에 대한 침하해석시 사용되는 불확실성 인자들에 대한 영향을 분석하여 보았다. 또한, 변동계수가 침하량에 미치는 영향을 분석하였으며 이들 파라메타들이 압밀도나 침하계산시 미치는 영향에 대한 민감도 분석을 실시하였다.