Various inorganic fillers improve the thermal conductivity and physical properties of organic products. Alumina has been used a representative filler in the heat radiation sheet for the heat radiation of electric device. The high filling rate of alumina increases the thermal conductivity and properties of products. We successfully developed the spherical alumina by flame fusion process using the oxygen burner with LPG fuel. In the high temperature flame (25003000) of oxygen burner, sprayed powders were melting and then rotated by carrier gas. This surface melting and rotation process made spherical alumina. Especially effects of chemical composition and particle size of stating materials on the melting behavior of starting materials in the flame and spheroidization ratio were investigated. As a result, spheroidization ratio of boehmite and aluminum hydroxide with endothermic reaction of dehydration process was lower than that of the sintered alumina without dehydration reaction.

To increase pot life in the formulation mixed with bisphenol F epoxy resin, anhydride-based curing agent, and imidazole-based curing accelerator powders as a paste material for high-speed RFID chip bonding, size variation of the imidazole-based powders and a coating method of the powders were adopted in this study. In experiment with regard to the size variation, the pot life was not outstandingly increased. Through the idea using the coating method, however, the pot life was increased up to 4.25 times in comparison with the addition of initial imidazole-based powders. Consequently, successive bonding of RFID chip could be performed with very short time of 5sec using the suggested formulation having improved pot life.

To investigate the distribution characteristics of grain size and organic matter of surface sediments from the Nakdong-Goryeong Mid-watershed, surface sediments were collected and analyzed. The samples were collected from six sited at four different times between May 2013 and May 2014. The were analyzed for grain size, water content, ignition loss, chemical oxygen demand, total organic carbon and total nitrogen. The surface sediments were mainly composed of medium sand (mean 44.7%) and coarse sand (mean 32.8%) and became coarser in May 2014. Fine sediments at the site NG-2 were poorly sorted and positively skewed, and occur in a tributary environment that is relatively low-energy compared with the other sites. The water content at the studied sites (15.3 ~ 34.9%) averaged 20.25%, and ignition loss (0.4 ~ 5.8%) and total nitrogen (274 ~ 2493 mg/kg) averaged 1.33% and, 696 mg/kg, respectively. These values indicated that the sediments were not seriously contaminated when compared with the sediment pollution evaluation standard of the National Institute of Environmental Research. The chemical oxygen demand (mean 0.17%) was at the non-polluted level compared with United States Environmental Protection Agency sediment quality standards. The total organic carbon (mean 0.18%) at all sites except site NG-2 (lowest effect level) was the no effect level of the Ontario sediment quality guidelines. The COD/IL (0.02 ~ 0.20) and C/N (0.73 ~ 6.76) were less than 1 and 10, respectively. Organic matter in the study area produced naturally from aquatic organisms. Results of principal component analysis showed that fine sediments (very fine sand and silt) were significantly affected by organic matters (ignition loss, chemical oxygen demand, total organic carbon and total nitrogen). In addition, the highest organic matters content in the study area occurred at the site with the finest sediments (NG-2).

최근 고유가 시대를 맞아 신재생 에너지확보가 필요한 시점에 가연성 폐기물로부터 고형연료제품을 생산하여 대체연료로 활용하는 방안이 부상되고 있다. 폐기물을 에너지화하여 온실가스의 배출을 감소시키고, 온실가스 배출 감축량(CERs) 확보를 통한 국가 경쟁력을 높일 수 있다. 현 시점을 토대로 본 연구의 목적은 D군에서 발생되는 사업장 생활계폐기물의 질적 특성, 배출량 및 처리방법 등을 파악함으로써, 합리적인 폐기물 처리시설을 계획하기 위한 기초자료를 확보하는데 목적이 있다. 본 조사의 대상지역은 주거형태, 생활수준 그리고 당진군 사업장 생활폐기물 발생특성을 고려하여 도심 주거지역(공동주택1,2, 단독주택), 상업지역, 업무지역 등 대표성을 띠는 총 5개의 지역으로 나누었다. 본 조사에서 삼성분 분석결과, 함수율의 경우 공동주택지역 20.78%, 단독주택 19.58%, 상가지역 21.57%, 업무지역 12.66%으로 조사되었으며, 상가지역이 조금 높게, 업무지역에서 낮게 나타났다. 가연분 결과는 공동주택 53.58%, 단독주택 53.22%, 상가지역 50.55%, 업무지역 58.32%로 조사되었다. 회분조사 결과에는 공동주택 25.64%, 단독주택 27.20%, 상가지역 27.88%, 업무지역 29.02%로 나타났다. 4개 조사지점 평균 삼성분 함량은 함수율 18.65%, 가연분 53.92%, 회분 27.43%로 조사되었다. 발열량 분석결과, 고위발열량의 경우 공동주택 폐기물에서 4312.66kcal/kg, 단독주택 폐기물에서 2907.37 kcal/kg, 상가지역 폐기물에서 3554.10kcal/kg, 업무지역 폐기물에서 4477.81kcal/kg로 조사되었다. 저위발열량의 경우 공동주택폐기물에서 3675.31kcal/kg, 단독주택 폐기물에서 2643.32kcal/kg, 상가지역 폐기물에서 3554.10kcal/kg, 업무지역 폐기물에서 4108.32kcal/kg로 조사되었다. 4개 조사지점에서의 평균 고위발열량은 4015.27kcal/kg, 저위발열량은 4108.32kcal/kg으로 조사되었다. 입도분석 결과, 30mm이하인 폐기물은 전체의 평균 7.18%, 30~50mm은 16.06%, 50~80mm은 37.62%, 80~100mm은 16.92%, 100~200mm은 20.86%, 200mm 이상은 1.36%로 조사되었다. 5지역 모두 가장 많은 입도분포를 나타내는 부분은 50~80mm이고, 가장 적은 분포는 200mm이상에서 조사되었다. 평균 발열량은 환경부에서 지정한 고형연료제품의 등급기준 3,500~4,500kcal/kg인 4등급에 포함이 될 수 있는 수치를 보였다. 연료로의 기준치(6,000kcal/kg)의 및 석탄과 유사한 발열량을 보이기에는 부족한 점이 있어 발열량을 높일 수 있는 부분은 혼재하여 사용해야 할 것으로 사료되며, 입도분석의 결과 개괄적인 특성을 토대로 고형연료로서의 기준에 맞게 파쇄하여 성형을 해야 할 것으로 사료된다. 본 연구를 통해 폐기물 고형연료(RDF)의 제작에 있어 기초자료로 사용될 수 있을 것이라 사료된다.

습식체질법, 퇴적법 및 원심분리법을 이용하여 얻어진 산청고령토의 9개 입도분리시료에 대하여 체계적인 X-선 회절 및 주사전자현미분석을 시행한 결과, 각 입도분의 점토광물 조성은 고령토의 원조직과 관련이 있음을 알 수 있었다. 침전작용에 의하여 생성된 10-a 형 할로이사이트, 일라이트 및 침철석은 미세입도분에 농집되고 모광물의 가상으로 생성된 버미큘라이트는 굵은 입도분에 농집된다. 침전작용 및 가상으로 생성된 다양한 유형의 캐올리나이트는 넓은 입도 분포를 보이지만 일반적으로 굵은 입도분에 농집된다. 굵은 입도분의 할로이사이트는 고령토 원래의 방상구조의 파편들인 할로이사이트 또는 하로이사이트와 캐올리나이트의 덩어리들로 존재하며 분쇄, 초음파처리 및 화학처리에 의해 분산되지 않은 것들이다. 체계적인 습식입도분리 실험에 의하여 10-a형 할로이사이트와 캐올리나이트의 구분도 가능하였다. 버미큘라이트와 캐올리나이트 등의 굵은 광물은 2μm 이하의 점토입도분에서는 검출되지 않는 반면 일라이트 및 침철석은 그 양이 적은 경우 원시료만의 X-선 회절분석에서는 검출되지 않는다. 따라서 고령토의 광물조성을 이해하기 위해서는 체계적인 습식입도분리 실험이 필수적이다.