PURPOSES: In order to apply high-speed weigh-in-motion (HS WIM) systems to asphalt pavement, three high-durability asphalt concrete mixtures installed with a WIM epoxy are evaluated. METHODS: In this study, dynamic stability, number of loading repetitions to reach the rut depth of 1 mm, and rut depth measurements of three asphalt mixtures at 60℃ were compared using an Asphalt Pavement Analyzer (APA). Laboratory-fabricated material and field core samples were prepared and tested according to KS F2374. RESULTS : Through the laboratory tests, it was found that all three modified asphalt mixtures (stone-mastic, porous, and semi-rigid) with WIM epoxy showed favorable permanent deformation results and passed the dynamic stability criterion of 3000 loading repetitions per 1 mm. In addition, it was confirmed that the modified SMA mixtures cored from the field construction yields satisfactory rutting testing results using the APA. Finally, the epoxy used for the HS WIM installation shows good adhesion with the three asphalt mixtures and permanent deformation resistance.

PURPOSES: The aim of this study is to analyze overloading control effectiveness of enforcing overweighted vehicles using HS-WIM (High-Speed Weigh-in-Motion) at main lane of expressway. METHODS: To analyze the weight distribution statistically, HS-WIM system should has an appropriate weighing accuracy. Thus, the weighing accuracy of the two HS-WIM systems was estimated by applying European specifications and ASTM (American Standards for Testing and Materials) for WIM in this study. Based on the results of accuracy test, overweight enforcement system has been operated at main lanes of two expressway routes in order to provide weight informations of overweighted vehicle in real time for enforcement squad. To evaluate the overloading control effectiveness with enforcement, traffic volume and axle loads of trucks for two months at the right after beginning of the enforcement were compared with data set for same periods before the enforcement. RESULTS: As the results of weighing accuracy test, both WIM systems were accepted to the most precise type that can be useful to applicate not only statistical purpose but enforcing on overweight vehicles directly. After the enforcement, the rate of overweighted trucks that weighed over enforcement limits had been decreased by 27% compared with the rate before the enforcement. Especially, the rate of overweighted trucks that weighed over 48 tons had been decreased by 91%. On the other hand, in counterpoint to decrease of the overweighted vehicle, the rate of trucks that weighed under enforcement limits had been increased by 7%. CONCLUSIONS: From the results, it is quite clear that overloading has been controlled since the beginning of the enforcement.

본 논문의 목적은 인접차로에서 동시에 주행하는 차량재하의 확률과 실제 차량의 중량을 고려하여 합리적인 다차로 재하계수를 제시하는 것이다. 차량동시재하의 확률은 국내 여러 곳에서 촬영한 비디오영상으로부터 분석되었으며 중차량의 중량은 국내 두 곳에서 Weigh-In-Motion시스템으로부터 계측한 자료를 이용하였다. 이 두 자료를 대표적인 2차로교량과 5차로교량에 각각 적용하여 다차로재하계수를 계산하였다. 또한 본 논문에서 제시한 동시재하확률 및 WIM자료의 중량이 국내의 지역별 특성을 대표하는 값으로 가정하여 다차로재하계수의 통계적인 특성을 산출하였다. 본 논문의 결과는 국내외의 교량 설계기준과 비교하였으며 그 결과 현행 국내의 도로교설계기준의 값보다는 작고, 유로코드 및 AASHTO LRFD기준보다는 큰 값을 나타냈으며 전체적으로 캐나다의 설계기준과 유사한 값을 보이는 것으로 나타났다.

본 연구는 포스트텐션 콘크리트 포장(PTCP: Post-Tensioned Concrete Pavement)에 고속축중계(WIM: Weigh-in-Motion)를 설치한 포장 시스템의 거동을 분석하기 위하여 수행되었다. PTCP는 일차로 폭으로 기존의 아스팔트 포장을 절삭하여 제거한 후에 시공되었다. PTCP는 슬래브의 연장이 길기 때문에 긴장을 통해 프리스트레스를 적절히 작용시키기 위해서는 슬래브와 하부층과의 마찰이 적어야 하며 이러한 영향을 시험시공을 통해 우선적으로 분석하였으며, 환경하중에 따른 슬래브의 종방향 거동도 분석하였다. 시험시공을 통해 얻은 결과를 바탕으로 공용중인 도로에 WIM 센서를 설치한 PTCP를 시공하였으며 이러한 포장체가 환경하중을 받을 때의 컬링 거동을 측정하여 특성을 분석하였다. 연구결과 PTCP 슬래브 상부의 일부를 절삭하여 WIM 센서를 설치하더라도 PTCP의 거동은 이에 영향을 받지 않는 것을 알 수 있었으며, WIM 센서의 정밀 측정에 부합되는 PTCP 시스템을 시공할 수 있는 기반을 마련하였다.