In this research, the magnetic abrasive finishing process using (Nd-Fe-B) permanent magnet was applied to confirm the performance and to find the optimum conditions. The STS304 bar was used as the specimen in this experiment. In order to confirm the performance of magnetic abrasive finishing process, the surface roughness (Ra) and diameter reduction were measured when the specimens were processed under the conditions of rotational speeds, frequencies, and magnetic pole shapes. The rotational speeds were varied at 8000rpm, 15000rpm, 20000rpm, and 25000rpm. And the frequencies were changed to 0Hz, 4Hz and 10Hz. Also the shapes of the magnetic pole were changed to flat edge, sharp edge and round edge. It can be concluded that the surface roughness (Ra) and diameter reduction were found to be the best at 25000rpm, 4Hz, flat edge.

환원.확산법에 의해 Sm2Fe17Nx 계 희토류 영구자석을 제조하기 위한 기초연구로서, 우선 Sm2Fe17 금속간화합물의 제조를 위하여, 금속 Ca에 의한 Sm2O3의 환원반응과 Fe분말중에 Sm의 확산반응을 검토하였다. 그 결과 전자는 1000˚C이상의 고온의 경우에 매우 빠르게 완료되지만, 후자의 Fe분말의 중심까지 Sm의 확산반응의 완료(완전한 균질화조건)는 1100˚C에서 3h 정도의 R-D 반응이 필요하며, 이 확산반응이 전체반응에 있어서 율속단계임을 알았다. Sm-Fe 계의 금속간화합물들의 성장은 1000˚C이하에서는 SmFe2, SmFe3,Sm2Fe17금속간화합물의 3개의 상이 관찰되었으나, 1100˚C에서는 Sm2Fe17 금속간화합물의 상만이 관찰되었다. 본 연구에서 얻어진 최종시료의 산소 및 Ca량은 각각 0.72wt% 및 0.11wt%이었다.