PURPOSES : The objective of this study is to evaluate the mechanical properties of ternary blended cement concrete incorporated with pulverized reject ash (PRA) or pulverized fuel ash (PFA) based on a comparison with those of ordinary Portland cement (OPC) concrete. METHODS : To produce the concretes, the level of OPC replacement is set at 60%, which comprises 30%~45% ground granulate blast furnace slag and 15%~25% of fly ash (FA). The FA can be categorized into PFA, 4PRA (fineness 3,930 cm2/g3), and 8PRA (fineness 7,840 cm2/g3). The compressive strength, surface electric resistivity, initial absorption coefficient, and chloride ion penetrability of OPC and the ternary blended cement concrete are measured at predetermined periods after water curing. RESULTS : It is discovered that the mechanical properties of concrete with 8PRA are better than those of OPC concrete. The performance of 4PRA concrete is worse than that of 8PRA concrete, indicating that the fineness of the PRA can affect the mechanical properties of the ternary blended cement concrete. CONCLUSIONS : The use of PRA is feasible for the production of ternary blended cement concrete, provided that the appropriate mix design and grinding technology are used.

본 연구에서는 고로슬래그 미분말 및 플라이애시와 같은 광물질 혼화재를 사용한 친환경 고성능 3성분계 시멘트 콘크리트 교면 포장의 성능을 평가하기 위하여 실험을 하였다. 광물질 혼화재의 혼입률 변화에 따른 3성분계 시멘트 콘크리트의 최적배합을 찾기 위하여 압축강도 및 휨강도 시험을 하였으며 최적배합을 사용하여 내구성 시험인 염소이온 침투저항성, 동결융해, 박리 저항성, 균열 저항성 및 알칼리골재반응 시험으로 친환경 고성능 3성분계 시멘트 콘크리트 교면 표장의 내구성 평가 및 신 구 콘크리트의 부착력을 평가하기 위하여 부착강도 시험을 하였다. 시험결과, 시멘트 70%, 고로슬래그 미분말15% 및 플라이애시 15%의 배합 바인더에서 압축강도 및 휨강도가 우수하게 나타났으며 이를 최적배합으로 도출하였다. 실내 및 시험시공에서 최적 배합을 사용한 실험결과는 염소이온 침투 저항성, 동결융해 저항성, 표면박리 저항성, 알칼리골재 반응 억제 및 내마모성이 우수하게 나타났다. 또한, 특수 제작된 Polymer Cement Mortar(Brooming)를 사용한 신 구 콘크리트의 부착력에서도 우수한 성능을 나타냈다.

The purpose of this study was to evaluate the sulfate attack of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature on the matching mixtures. Test results revealed that compressive strength ratio at each age was superior to the developed mixtures than control mixtures. Whereas, the mass change ratio was superior to the control mixture at all ages.

The purpose of this study was to evaluate the shrinkage of ternary blended concrete based on low-heat cement for reducing the heat of hydration. The main parameters were water-to-binder ratio and curing temperature(5, 20, 40℃). Test results showed that the shrinkage significantly was influenced by water-to-binder ratio than binder type. The shrinkage strain of all of the mixtures was increased with increasing the curing temperature.

본 연구는 초고강도콘크리트의 배합에 사용되는 3성분계 혼합시멘트의 최적조합을 도출하기 위한 실험연구이다. 3성분계 혼합시멘트는 포틀랜드시멘트, 고로슬래브 미분말 0%, 30%, 40%, 50% 및 플라이애시 0%, 10%, 20%, 30%로 구성하였다. 물결합재비 0.18의 초고강도콘크리트를 대상으로 각 실험체의 압축강도와 공극구조를 조사한 결과, 플라이애시 10%, 고로슬래그 미분말 30%를 혼합한 3성분계 혼합시멘트를 사용한 콘크리트의 압축강도는, 50nm 이상의 공극량 감소에 의해, Plain 콘크리트에 비해 현저히 증가하였다.