PURPOSES : The numeric-based Highway Pavement Management System (HPMS), along with an advanced three-dimensional pavement condition monitoring profiler vehicle (3DPM), in South Korea has presented remarkable advancements in pavement management since the early 2000. Based on these results, visual distress on pavement surfaces can be easily detected and analyzed. Additionally, the entire expressway pavement surface conditions in South Korea can be easily monitored using the current graphical user interface-based advanced information graphic (AIG) approach. Therefore, a critically negative pavement section can be detected and managed more easily and efficiently. However, the actual mechanical performance of the selected pavement layer still needs to be investigated in a more thorough manner not only to provide more accurate pavement performance results but also to verify the feasibility of the current 3DPM and AIG approaches. In this study, the low-temperature performance of the selected asphalt pavement layer section was evaluated to further verify and strengthen the feasibility of the current 3DPM and AIG approaches developed by the Korea Expressway Corporation. METHODS : Based on 3DPM and AIG approach, the positive and negative-riding-quality road sections were selected, respectively. The asphalt material cores were extracted from each section then bending beam rheometer mixture creep test was performed to measure their low-temperature properties. Based on the experimental results, thermal stress results were computed and visually compared. RESULTS : As expected, the asphalt material from the negative driving performance section presented a poorer low-temperature cracking resistance than that from the positive driving performance section. CONCLUSIONS : Current 3DPM equipment can successfully evaluate expressway surface conditions and the corresponding material performance quality. However, more extensive experimental studies are recommended to verify and strengthen the findings of this study

PURPOSES : This purpose of this study is to analyze the effect to autogenous shrinkage of the top-layer material of a two-lift concrete pavement mixing both silica fume and polymer powder. METHODS: The bottom-layer of a two-lift concrete pavement was paved with original portland cement (OPC) with a 20~23 cm thickness. Additionally, the top-layer which is directly exposed to the environment and vehicles was paved with a high-performance concrete (HPC) with a 7~10 cm thickness. These types of pavements can achieve a long service life by reducing joint damage and increasing the abrasion and scaling resistance. In order to integrate the different bottom and top layer materials, autogenous shrinkage tests were performed in this study according to the mixing ratio of silica fume and polymer powder, which are the admixture of the top-layer material. RESULTS: Autogenous shrinkage decreased when polymer powder was used in the mix. Contrary to this, autogenous shrinkage tended to rise with increasing silica fume content. However, the effects were not significant when small amounts of polymer powder were used (3% and 11%). CONCLUSIONS : The durability and compressive strength increase when silica fume is used in the mix. The flexural strength considerably increases and autogenous shrinkage of concrete decreases when polymer powder is used in the mix. As seen from above, the proper use of these materials improves not only durability, but also autogenous shrinkage, leading to better shrinkage crack control in the concrete.

PURPOSES: Reflection cracking has been one of the major causes of distress when asphalt pavement is laid on top of concrete pavement. This study evaluated the reflection cracking resistance of asphalt mixtures reinforced with asphalt embedded glass fiber and carbon fiber using a Texas Transportation Institute (TTI) overlay tester. METHODS : Different asphalt mixtures such as polymer-modified mastic asphalt (PSMA) and a dense graded asphalt mixture were reinforced with asphalt-embedded carbon fiber and glass fiber. For comparison purposes, two PSMA asphalt mixtures and one dense graded asphalt mixture were evaluated without fiber reinforcement. Two different overlay test modes, the repeated overlay test (R-OT) and monotonic overlay test (M-OT), were used to evaluate the reflection cracking resistance of asphalt mixtures at 0 ℃. In the R-OT test, the number of repeated load when the specimen failed was obtained. In the M-OT test, the tensile strength at the peak load and tensile strain were obtained. RESULTS : As expected, the fiber-reinforced asphalt mixture showed a higher reflection cracking resistance than the conventional nonreinforced asphalt mixtures based on the R-OT test and M-OT test. The dense graded asphalt mixture showed the least reflection cracking resistance and less resistance than the PSMA. CONCLUSIONS: The TTI overlay tester could be used to differentiate the reflection cracking resistance values of asphalt mixtures. Based on the R-OT and M-OT results, the carbon-fiber-reinforced asphalt mixture showed the highest reflection cracking resistance among the nonreinforced asphalt mixtures and glass-fiber-reinforced asphalt mixture.

아스팔트 혼합물의 균열 저항성은 일반적으로 인장 강도, 스티프니스와 같은 단일 물성치를 측정함으로써 평가된다. 그러나, 아스팔트 혼합물의 균열 성능을 평가함에 있어서 단일 물성치의 이용은 의문시되어 왔다. 따라서 본 연구에서는 아스팔트 혼합물의 균열 저항성과 관련이 있는 주요 특성치를 좀 더 심도 있게 규명하고자 하였다. 이를 위해 다양한 하중 조건 하에서 파괴 시험 크리프 시험, 강도 시험이 일반 아스팔트 혼합물과 개질 아스팔트 혼합물에 대해서 수행되었다. 시험 결과, 혼합물의 균열 저항성은 주로 미세 손상 축적 속도에 영향을 받음을 알 수 있었으며, 이 값은 파괴 에너지 한계에 영향을 주지 않으면서 m값에 반영됨을 알 수 있었다. 또한, 짧은 하중 재하 시간 (탄성거동) 동안 얻어지는 스티프니스는 혼합물의 균열 저항성의 차이를 규명하는데 한계가 있음을 알 수 있었다. 따라서 아스팔트 혼합물의 균열 저항성을 보다 명확히 평가하기 위해서는 혼합물의 크리프 거동과 파괴 한계점을 동시에 고려하는 것이 필수적임을 알 수 있었다. 또한 수퍼페이브 간접 인장 강도 시험으로부터 구한 잔여 소멸 에너지는 비교적 손쉬운 실험을 통해 아스팔트 혼합물의 균열 저항성의 상대적인 차이를 보여줄 수 있는 유용한 물성치임을 알 수 있었으며, 장기 크리프 시험에서 얻어지는 파괴 변형률은 아스팔트 혼합물의 크리프 거동과 파괴 한계점을 동시에 고려함으로써 균열 저항성을 평가할 수 있는 유용한 물성치 임을 알 수 있었다.

7050 Al합금의 응력부식저항성에 미치는 2단 시효처리의 영향을 미세조직관찰, 전기전도도시험 및 SCF값을 평가함으로써 조사하였다. 최대 경도 이상 과시효에 의해 주 강화상인 η'상이 η상으로 변태되었고, 입내 및 입계에 존재하는 η상의 크기와 간격이 커졌으며 그 결과 응력부식저항성이 증대되었다. 2차 시효시간의 증가에 따라 전기전도도값은 증가되었으나 항복강도의 감소로 인하여 SCF값은 감소되었는데, 이러한 결과는 응력부식저항성의 증가를 의미한다. AMS 4107규격을 기준으로 하였을 때 7050 Al합금 단조재의 적정시효조건은 1차시효가 120˚C에서 6시간, 2차시효는 175˚C에서 12시간이었다.

초강인 AISI 4340강을 850˚C에서 2시간 동안 오스테나이징 처리 후 수냉하고, 250, 400, 600˚C에서 각각 2시간 동안 템퍼링 처리를 하였다. AISI 4340강의 인장 특성은 상온에서 측정되었다. AISI 4340강 위에 니켈 전해도금된 것과 도금되지 않은 시편의 분극 특성이 3.5wt%NaCI 수용액과 인공해수에서 측정되었다. AISI 4340강위에 니켈 전해도금된 시편은 500mV(vs. Ag/AgCI)이하의 전위에서 부식 저항이 크게 향상되었다. 그러나 1A/cm2의 전류밀도에서 30분 이상 니켈 전해도금된 시편은 도금층에 불순물과 기공이 형성되었기 때문에 AISI 4340강의 부식 저항은 감소되었다. AISI 4340강의 수소취화형 응력부식균열을 여러 작용 응력과 음극인가전력에서 U-bend 시편을 이용하여 IN 3.5 wt% NaCI 수용액에서 조사되었고, 수소취화형 응력부식균열 거동은 주사전자현미경으로 조사되었다.

Concept of primary solidification mode control was adopted to obtain optimal solidification crack resistance, hot ductility, corrosion resistance and toughness for austenitic stainless steel. By controlling primary solidification phase as primary δ and containing no ferrite at room temperature, optimal solidification crack resistance, hot ductility, corrosion resistance and cryogenic toughness could be obtained. The optimum chemical composition of austenitic stainless steel ranges 1.46~1.55(Creq/Nieq ratio) calculated by Schaeffler's equation.