FeS2 has been widely used for cathode materials in thermal battery because of its high stability and currentcapability at high operation temperature. Salts such as a LiCl-KCl were added as a binder for improving electrical per-formance and formability of FeS2 cathode powder. In this study, the effects of the addition of Li2O in LiCl-KCl binderon the formability of FeS2 powder compact were investigated. With the increasing amount of Li2O addition to LiCl-KClbinder salts, the strength of the pressed compacts increased considerably when the powder mixture were pre-heat-treatedabove 350oC. The heat-treatment resulted in promoting the coating coverage of FeS2 particles by the salts as Li2O wasadded. The observed coating as Li2O addition might be attributed to the enhanced wettability of the salt rather than itsreduced melting temperature. The high strength of compacts by the Li2O addition and pre-heat-treatment could improvethe formability of FeS2 raw materials.

황철석에 대한 압축성 연구를 다이아몬드 앤빌 기기 및 방사광을 이용하고 에너지분산 X-선회절법을 적용하여 상온에서 시행하였다. 황철석의 체적탄성률은 실험조건과 실험기기에 따라 매우 큰 변이를 보이고 있는데 이는 압력전달매체의 특성에 따른 것으로 알려져 있다. FeS2#1(황철석+NaCl)과 FeS2#2(황철석+MgO)에 대해 압력전달 매체로 각각 NaCl과 유체를 이용하여 체적탄성률 138.9 GPa와 198.2 GPa를 각각 얻었다. 이러한 값은 시료방의 압력상태에 따른 예측 결과치에 대치되는 것으로 그 원인은 압력전달액체의 상변이에 따른 것으로 추정되며 이외에 고상검출기의 차이, E*d값의 차이 등도 영향을 미친 것으로 판단된다. 모든 실험은 포항가속기연구소 1B2 빔라인에서 시행되었다.