Geopolymer, also known as alkali aluminum silicate, is used as a substitute for Portland cement, and it is also used as a binder because of its good adhesive properties and heat resistance. Since Davidovits developed Geopolymer matrix composites (GMCs) based on the binder properties of geopolymer, they have been utilized as flame exhaust ducts and aircraft fire protection materials. Geopolymer structures are formed through hydrolysis and dehydration reactions, and their physical properties can be influenced by reaction conditions such as concentration, reaction time, and temperature. The aim of this study is to examine the effects of silica size and aging time on the mechanical properties of composites. Commercial water glass and kaolin were used to synthesize geopolymers, and two types of silica powder were added to increase the silicon content. Using carbon fiber mats, a fiber-reinforced composite material was fabricated using the hand lay-up method. Spectroscopy was used to confirm polymerization, aging effects, and heat treatment, and composite materials were used to measure flexural strength. As a result, it was confirmed that the longer time aging and use of nano-sized silica particles were helpful in improving the mechanical properties of the geopolymer matrix composite.

수처리 및 의약바이오 분야에서 유효물질 분리에 활용되고 있는 알루미나 중공사 분리막은 얇은 두께로 인해 취 급 및 적용시 쉽게 파괴되는 단점이 있기 때문에 분리막의 강도를 100 MPa 이상으로 향상시키기 위한 연구가 필요하다. 본 연구에서는 나노입자의 함량을 0, 1, 3, 5 wt%로 증가시켰을 때 제조된 중공사 분리막의 특성을 평가하였다. 그 결과, 나노입 자의 함량이 증가함에 따라 중공사 분리막의 강도는 79 MPa에서 115 MPa로 증가하였으며, 밀도는 1.76 g/m3에서 1.88 g/m3 으로 증가하였고 기공률과 평균기공크기는 각각 51%에서 48%로, 416 nm에서 352 nm로 감소한 것을 확인하였다. 스폰지구 조가 발달하고 스폰지구조의 기공크기가 향상된 알루미나 중공사 분리막은 100 MPa 이상으로 기계적 강도가 향상되었으며, 약 100000 GPU의 높은 질소 투과도 및 약 3000 L/m2h의 높은 물 투과도를 나타내었다. 따라서, γ-알루미나 나노입자를 소 결조제로 첨가하는 것은 α-알루미나 중공사 분리막의 기계적 강도를 효과적으로 증진시키고 높은 투과성능을 유지할 수 있 는 매우 유효한 방법임을 확인하였다.

This study aims to analyze the effects of 4 directions of wind, wind speed, year of construction of slate roofs, installation area and other factors on the concentration and size distribution of airborne fiber particles in farmhouses with a slate roof containing asbestos. Airborne fiber particle samples were collected from the air in six houses with a slate roof containing asbestos using a high flow rate pump (10 L/min) for 2 hours, three times a day with a different condition, 72 times in total. The airborne fiber particle concentrations were measured using a phase contrast microscope, and the size of fiber particles of 72 samples in total was estimated using the mean value of those in each sample measured at 100 with a field of view. The total average concentration of fiber particles collected from in the air in four directions of the targeted farmhouses was 2.83 fiber/L, and its maximum concentration was 5.75 fiber/L, which means that among all samples there was no place that exceeded 10 fiber/L, a recommended indoor air quality standard. The average size of the fiber particles was 11.55 μm, and the maximum size was 40 μm. A multiple regression analysis of factors affecting the concentration and size of fiber particles in the air collected from the farmhouses with a slate roof containing asbestos found that the closer to the main wind direction (p<0.001) and the faster the average wind speed (p<0.05), the fiber particles concentration became significantly higher. In this case, the coefficient of determination was 52.8%. It was also found that the wider the total area of the slate roof (p<0.001) and the slower the average wind speed (p<0.05), the longer the fiber particles; the coefficient of determination for this finding was 19.6%. The concentration of fiber particles in the air of farmhouses with a slate roof appeared to be the highest under the main wind direction, and became significantly higher as the wind speed became faster. This proved that fiber particles were leaked from the slate roof. The size of the fiber particles became significantly longer as the area of the slate roof became wider and the wind speed became slower.

침지식분리막 오염을 최소화하기 위한 두 가지 공기세정방식을 비교하였다. 연속적인 공기세정과 단계별 공기량을 증가시키는 방식을 연구하였다. 15분의 여과 중에 세정공기의 증가는 5분마다 단계별로 공기량을 증가시켜주었다. 모의 여과 원수에 분말활성탄을 10 g/L 이하 그리고 카올린은 20 g/L 이하로 준비하였으며, 플러스는 80 LMH로 하였다. 단계별 공기세정방식은 연속적인 공기세정 방식보다 분리막 오염억제에 효과적이었다. 추가적으로 주입된 응집제는 분리막 오염저감을 보다 향상시켰다. 연속적인 공기세정의 오염현상은 공경막힘과 분리막 표면에 지속적인 입자의 축적에 기인하였다.

The electrospinning process was established as a promising method to fabricate nano and micro-textured scaffolds for tissue engineering applications. A BCP-loaded PCL micro-textured scaffold thus can be a viable option. The biocompatibility as well as the mechanical properties of such scaffold materials should be optimized for this purpose. In this study, a composite scaffold of poly (ε-caprolactone) (PCL)-biphase calcium phosphate (BCP) was successfully fabricated by electrospinning. EDS and XRD data show successful loading of BCP nano particles in the PCL fibers. Morphological characterization of fibers shows that with a higher loaded BCP content the fiber surface was rougher and the diameter was approximately 1 to 7 μm. Tensile modulus and ultimate tensile stress reached their highest values in the PCL- 10 wt% BCP composite. When content of nano ceramic particles was low, they were dispersed in the fibers as reinforcements for the polymer matrix. However, at a high content of ceramic particles, the particles tend to agglomerate and lead to decreasing tensile modulus and ultimate stress of the PCL-BCP composite mats. Therefore, the use of nano BCP content for distribution in fiber polymer using BCP for reinforcement is limited. Tensile strain decreased with increasing content of BCP loading. From in vitro study using MG-63 osteoblast cells and L-929 fibroblast like cells, it was confirmed that electrospun PCL-BCP composite mats were biocompatible and that spreading behavior was good. As BCP content increased, the area of cell spreading on the surface of the mats also increased. Cells showed the best adherence on the surface of composite mats at 50 wt% BCP for both L-929 fibroblast-like cells and MG-63 osteoblast cell. PCL- BCP composites are a promising material for application in bone scaffolds.

his study was investigated the characteristics of indoor air concentration of fiber particles in 30 public facilities and 245 schools by PCM (phase contrast microscopy). Also SEM/EDX (scanning electron microscope / energy dispersive using X-ray analysis) was used to obtain physicochemical information of asbestos fiber and to classify asbestos and non-asbestos of fiber particles. The airborne concentrations of fiber particles were 0.0009±0.0009 counts/mL in public facilities and 0.0012±0.0006 counts/mL in schools by PCM. All the samples were satisfied with the IAQ (indoor air quality) level of 0.01counts/mL. In classification of 4 type shapes, over 80% of the fiber particles were identified as single fiber type. And this study analysed airborne fiber particles in 4 sites for identifying asbestos of by SEM/EDX. The asbestos fibers in most samples could not be found.