Flexible self-supported laser-induced graphene (LIG) electrode devices were facilely fabricated through laser ablation technique by employing commercial polyimide film as the precursor material. Compared with the widely used traditional glassy carbon electrodes, the resulted LIG electrodes displayed abundant porous structure and surface defects. Notably, the onestep yielded LIG electrode devices were endowed with large electrochemically active surface area and accelerated electron transfer ability. Benefiting from its superior electrochemical property, these unmodified LIG electrodes exhibited remarkable enhanced electrochemical oxidation reactivity toward the food additive molecule Allura Red. Based on the augmented oxidation signal of Allura Red molecules on the LIG electrodes, a novel electrochemical sensor with high sensitivity for the detection of Allura Red was successfully developed. The sensor demonstrated a linear detection range spanning from 5 nM to 1 μM and exhibited a detection limit as low as 2.5 nM. Besides, the sensitivity was calculated to be 240.62 μA μM−1 cm− 2. More importantly, the sensor manifested outstanding stability, reproducibility, and practicality, further emphasizing its potential for real-world application.

Graphene is a suitable transducer for wearable sensors because of its high conductivity, large specific surface area, flexibility, and other unique considerable features. Using a simple, fast galvanic pulse electrodeposition approach, a unique nonenzymatic glucose amperometric electrode was successfully developed based on well-distributed fine Cu nanoparticles anchored on the surface of 3D structure laser-induced graphene. The fabricated electrode allows glucose detection with a sensitivity of 2665 μA/mM/cm2, a response time of less than 5 s, a linear range of 0.03–4.5 mM, and a LOD of 0.023 μM. It also detects glucose selectively in the presence of interfering species such as ascorbic acid and urea. These provide the designed electrode the advantages for glucose sensing in saliva with 97% accuracy and present it among the best saliva-range non-enzymatic glucose sensors reported to date for real-life diagnostic applications.

Vertically Aligned Carbon Nanotubes (VACNTs)-coated flexible aluminium (Al) foil is studied as an electrode for supercapacitor applications. VACNTs are grown on Al foil inside thermal Chemical Vapor Deposition (CVD) reactor. 20 nm thick layer of Fe is used as a catalyst while Ar, H2 and C2H2 are used as precursor gases. The effect of growth temperature on the structure of CNTs is studied by varying the temperature of CVD reactor from 550 °C to 625 °C. Better alignment of VACNTs arrays on Al foil is recorded at 600 °C growth temperature in comparison to other processing temperatures. Cyclic voltammetry results shows that VACNTs-coated Al foil has a specific capacitance of ~ 3.01 F/g at a scan rate of 50 mV/s. The direct growth of VACNT array results in better contact with Al foil and thus low ESR values observed in impedance spectroscopy analysis. This leads to a fast charge–discharge cycle as well as a very high value of power density (187.79 kW/ kg) suitable for high power applications. Moreover, wettability study shows that the fabricated VACNT electrode has a contact angle of more than 152° which signifies that it is a superhydrophobic surface and hence shows lower specific capacitance in comparison to reported values for VACNT array. Therefore, it is necessary to develop suitable post-processing strategies to make VACNTs hydrophilic to realize their full potential in supercapacitor applications.

Free-standing hybridized electrode consisting of double-walled carbon nanotubes (DWNTs) and activated carbon have been fabricated for flexible supercapacitor applications. The xanthan-gum, used in our methodology, showed high ability in dispersing the strongly bundled DWNTs, and was then effectively converted to activated carbon with large surface area via chemical activation. The homogeneously dispersed DWNTs within xanthan-gum derived activated carbon acted as both electrical path and mechanical support of electrode material. The hybridized film from highly dispersed DWNTs and activated carbon was mechanically strong, has high electrical conductivity, and exhibited high specific capacitance of 141.5 F/g at the current density of 100 mV/s. Our hybridized film is highly promising as electrode material for flexible supercapacitors in wearable device.

본 연구에서는 각기 다른 두 제조사의 AgNW를 활용하여 스핀코팅 속도, 열처리 온도 및 방법 그리고 PDMS코팅 속도에 따른 AgNW/PDMS composite공정 연구를 실시하였다. 실험결과 peel off 특성에 영향을 미치는 인자로 건조방식이 주요하게 작용하며 공정온도 또한 전극 특성에 영향을 주었다. 핫플레이트를 사용한 건조방식은 한방향 열전달로 인해 PDMS를 충분히 건조시키지 못하였지만 오븐 건조를 통해 그 결점을 보완할 수 있었다. 또한, PDMS 코팅속도가 증가함에 따라 스트레처블 특성이 향상되었고 GF는 0.03에서 0.07로 약 100정도 향상되었다.

본 연구에서는 유연성을 갖는 전극 제조를 위해 산 처리된 단일벽 탄소나노튜브 (Acid treated-SWCNTs)를 금이 코팅된 PET 기판 위에 스프레이 코팅하였다. 단일벽 탄소나노튜브가 가지는 단점을 보완하기 위하여 산 처리 공정을 이용하여 나노튜브에 작용기를 도입하여 분산성을 극대화 시켰 으며 전기화학적 특성을 향상 시켰다. 스프레이 기술을 이용하여 제조된 유연성을 갖는 단일벽 탄소나노 튜브 기반의 전극을 1 M의 황산 전해질에서 순환 전압 전류법, 임피던스 분광법 그리고 충·방전 시험을 통하여 전기화학적 특성을 분석 하였다. 그 결과, 응력을 가하지 않은 전극의 전기 용량값은 67 F․g-1로 측정 되었으며, 1000번의 충·방전 시험 후에는 전기 용량값이 63 F․g-1 (94 % 유지)로 감소하는 결과를 보였다. 이에 반하여, 탄소나노튜브 기반의 플렉시블 전극은 500번의 굽힘 시험 (bending test)과 6000 번의 충·방전 시험 후에는 초기의 전기 용량값 (67 F․g-1)이 유지되는 결과를 얻었다.