Nanosized Gd2O3:Eu3+ red phosphor is prepared using a template method from metal salt impregnated into a crystalline cellulose and is dispersed using a bead mill wet process. The driving force of the surface coating between Gd2O3:Eu3+ and mica is induced by the Coulomb force. The red phosphor nanosol is effectively coated on mica flakes by the electrostatic interaction between positively charged Gd2O3:Eu3+ and negatively charged mica above pH 6. To prepare Gd2O3:Eu3+-coated mica (Gd2O3:Eu/mica), the coating conditions are optimized, including the stirring temperature, pH, calcination temperature, and coating amount (wt%) of Gd2O3:Eu3+. In spite of the low luminescence of the Gd2O3:Eu/mica, the luminescent property is recovered after calcination above 600℃ and is enhanced by increasing the Gd2O3:Eu3+ coating amount. The Gd2O3:Eu/mica is characterized using X-ray diffraction, field emission scanning electron microscopy, zeta potential measurements, and fluorescence spectrometer analysis.

Gd2O3:Eu3+ red phosphors were prepared by template method from crystalline cellulose impregnated by metal salt. The crystallite size and photoluminescence(PL) property of Gd2O3:Eu3+ red phosphors were controlled by varying the calcination temperature and Eu3+ mol ratio. The nano dispersion of Gd2O3:Eu3+ was also conducted with a bead mill wet process. Dependent on the time of bead milling, Gd2O3:Eu3+ nanosol of around 100 nm (median particle size : D50) was produced. As the bead milling process proceeded, the luminescent efficiency decreased due to the low crystallinity of the Gd2O3:Eu3+ nanoparticles. In spite of the low PL property of Gd2O3:Eu3+ nanosol, it was observed that the photoluminescent property was recovered after re-calcination. In addition, in the dispersed nanosol treated at 85 oC, a self assembly phenomenon between particles appeared, and the particles changed from spherical to rod-shaped. These results indicate that particle growth occurs due to mutual assembly of Gd(OH)3 particles, which is the hydration of Gd2O3 particles, in aqueous solvent at 85 oC.