High-temperature friction performances of graphite blocks (GBs) and zinc phosphate impregnated graphite blocks (IGBs) were evaluated under various friction temperatures. The surface of IGB exhibited extremely lower average friction coefficient values, that was 0.007 at 400 °C and 0.008 at 450 °C, in comparison to that of GB (0.13 at 400 °C and 0.16 at 450 °C, respectively). The worn surface of IGB in the high-temperature friction test was smoother and more complete than that of GB. The wear under high temperature and load caused the transformation of zinc pyrophosphate to zinc metaphosphate and the formation of a continuous large-area boundary lubrication layer combined with graphite and metallic element on the wear surface. The superior tribology property of IGB could be attributed to the digestion of iron oxides by tribo-chemical reactions and passivation of the exposed dangling covalent bonds. Specifically, the layered structure generated on the IGB wear interface effectively decreased the adhesive forces and prevented the surface from serious damage.

Si-Cr계 내열강 SUH3와 Cr-Ni계 stainless강 SUS 303 및 이들이 마찰용접재 SUH3-SUS303을 1,060℃에서 용체화처리하고 다시 700℃에서 10, 100시간 시효열처리한 각 시험편의 고온 피로강도에 대한 시효열처리의 효과를 알기 위하여 700℃에서 고온 회전굽힘 피로시험을 하고 파약거동을 미시적으로 관찰하여 다음과 같은 결과를 얻었다. 1) SUH3재와 SUS303재의 최적마찰용접조건은 회전수 2420rpm, 마찰가압력 8kg/mm2, 전 upset량 7mm(마찰가압시간 3sec, upset시간 2sec)이었다. 2) 700℃ 고온에서 장시간 이루어지는 고온피로시험에 있어, 용체화처리재의 S-N 곡선 경사부의 기울기가 가장 급하게 나타났다. 3) SUH3-SUS303 마찰용접재는 1,060℃에서 1시간용체화 처리하고, 700℃에서 시효처리하는 경우 최적시효시간은 10시간이었다. 4) 10시간 시료재의 고온피로한도는 모재보다 SUH3은 75.4%, SUS303은 28.5% 높았으며, 용접재 SUH3-SUS303은 44.2% 정도 높았다. 100시간 시효재는 모재보다 SUH3은 64.91% SUS303은 30.4% 높았으며, SUH3-SUS303은 30.4% 높았으며, SUH3-SUS303은 36.6% 높았다. 5) 마찰용접재의 상온 및 고온의 피로파단은 모두 SUS303의 모재측에 발생하였으며, 용접면에서의 파단은 전혀 없었다. 6) SUS303재와 마찰용접재 SUH3-SUS303재의 크랙은 입내파양형이었으나 SUH3은 입계크랙의 전파로 파양한다.