In this paper, Results of mock-up test for mitigating carbonation of high volume mineral admixture concrete by spreading waste cooking oil. Concrete incorporating 60% of BS and 30% of FA with the size of 900×600×200 are discussed. Denatured Silicate paint is also applied to compare the performance. Test results indicate that the application of ERCO and DSP enhance carbonation resistance.

In previous research team had reported that the durability of carbonation is improved by filling voids due to the saponification reaction of oil and concrete. The purpose of this study was to have experimental investigation the effect of mock-up experiment on the carbonation resistance of the waste concrete admixture.

In previous research team had reported that the durability of carbonation is improved by filling voids due to the saponification reaction of oil and concrete. The purpose of this study was to have experimental investigation the effect of mock-up experiment on the carbonation resistance of the waste concrete admixture.

In this study, mock-up test of ternary blended concrete using structure was conducted in order to evaluate the temperature rise. The results of the mock-up test, it was found that it was convenient to obtain the minimum temperature rise of 3:5:2 mixing.

Girder type and slab type modular bridges require using UHSC(Ultra High Strength Concrete) and high performance mortar to connect each girder and slab modules at joint parts. This study presents the results of mock-up tests on the properties of UHSC and high performance mortar for modular bridge

본 연구는 개발된 저수축 고성능 콘크리트를 대상으로 모의부재 시험체에 있어서 콘크리트의 기초적 물성과 수축특성에 대하여 검토한 것이다. 실험연구 결과, 콘크리트의 배합특성으로 제안 배합은 목표 슬럼프플로우 및 목표 공기량을 만족하기 위해 SP제량 증가, AE제량 감소의 배합보정이 필요하였다. 응결시간은 제안 배합이 8시간 정도 빠르게 나타났으며, 굳은 콘크리트의 압축강도는 60MPa 이상의 고강도로 나타냈다. 수축특성으로 제안 배합 자기수축의 경우 플레인 배합 자기수축에 비해 50% 정도 저감되었고, 제안 배합의 중심부 건조수축은 수분발산이 없는 것에 기인하여 자기수축과 유사한 경향이었으나, 표면부는 크게 수축하였다. 단, 철근배근 시험체인 경우는 철근구속에 의해 내부 및 표면의 수축량이 작게 나타났다.