Tin bis(monohydrogen orthophosphate) monohydrate 물질의 흡착 성질에 관하여 KCl 수용액을 통하여 조사하였다. 금속이온 농도와 pH를 변화시키면서 어떻게 달라지는지 화학평형에 바탕을 두고 data를 분석하였다. 금속이온들의 흡착 data는 Langmuir 흡착식에 넣어 Langmuir 수치들을 얻는데 사용되었다. Tin phosphate는 산성에서 이온교환 화합물로 작용하였으며, 2가의 전이금속이온에 대해 Cu+2 > Co+2 > Ni+2의 순서로 선택적 흡착성질을 나타내었다. 약한 산성 이온 교환체에서와 같이 금속이온의 교환은 tin phosphate의 선택성을 결정하는데 결정적 역할을 하였다. 모든 경우에서 흡착의 정도는 온도와 농도의 증가와 함께 증가하였다. Lnngmuir 수치들은 흡착과정 동안의 엔트로피, 엔탈피, 자유에너지 변화량같은 열역학적 함수들을 계산하는데 이용되었다.

In this study, composite PAN-based ACNFs embedded with MgO and MnO2 were prepared by the electrospinning method. The resultant pristine ACNFs, ACNF/MgO and ACNF/MnO2 were characterized in terms of their morphological changes, SSA, crystallinity and functional group with FESEM-EDX, the BET method, XRD and FTIR analysis, respectively. Results from this study showed that the SSA of the ACNF/MgO composite (1893 m2 g–1) is significantly higher than that of the pristine ACNFs and ACNF/MnO2 which is 478 and 430 m2 g–1, respectively. FTIR analysis showed peaks of 476 and 547 cm–1, indicating the presence of MgO and MnO2, respectively. The FESEM micrographs analysis showed a smooth but coarser structure in all the ACNFs. Meanwhile, the ACNF/MgO has the smallest fiber diameter (314.38±62.42 nm) compared to other ACNFs. The presence of MgO and MnO2 inside the ACNFs was also confirmed with EDX analysis as well as XRD. The adsorption capacities of each ACNF toward CH4 were tested with the volumetric adsorption method in which the ACNF/MgO exhibited the highest CH4 adsorption up to 2.39 mmol g–1. Meanwhile, all the ACNF samples followed the pseudo-second order kinetic model with a R2 up to 0.9996.

Rhodiola sachalinensis fermentates by lactic acid bacteria were prepared using the adsorption process, and were investigated for changes of the main compounds and anti-oxidative activities during the adsorption and fermentation process. While the R. sachalinensis extract (RSE), which did not go through the adsorption process, showed little change in pH during fermentation and a significant reduction in the number of lactic acid bacteria, the pre-preparatory adsorption process was found to be helpful for promoting fermentation and for maintenance of bacterial numbers. The contents of total phenolic compounds mostly decreased during the adsorption process, but showed an increasing tendency to rebound during the fermentation process. The contents of salidroside and p-tyrosol in the RSE were 1153.3 ㎎% and 185.0 ㎎% respectively, and they did not significantly change after treatment with acid clay or bentonite as adsorbents, which were 1093.0 and 190.5 ㎎% by acid clay, and 882.2 and 157.3 ㎎% by bentonite. When the extract was fermented after treatment with acid clay or bentonite, the salidroside contents were decreased by 282.7 and 505.0 ㎎% respectively, but the p-tyrosol contents were increased by 714.0 and 522.4 ㎎% respectively. Compared to the DPPH radical scavenging activity of the RSE (66.8%) at the conc. of 0.1%, that of the fermented RSE, which went through adsorption process with acid clay or bentonite, was significantly increased to 79.4 and 72.7% respectively at the same concentration (p<0.05). Though fermentation by lactic acid bacteria was suppressed in the RSE, the results suggested that the adsorption process may promote fermentation without any change in the content of major active compounds. It is expected that fermentation by lactic acid bacteria could improve the antioxidant activity and various associated functionalities of R. sachalinensis.

국내 포항 소재 R사의 구룡포산 천연 제올라이트의 물리·화학적 특성을 규명하기 위해 X-선 회절 분석, X-선 형광 분석, 열 시차·열 중량 분석, 양이온 교환능 분석 및 세슘(Cs), 스트론튬(Sr) 흡착 실험을 수행하였다. X- 선 회절 분석 결과 모데나이트, 휼란다이트, 클라이놉티로라이트 및 일라이트와 같은 광물이 함유되어 있으며, X- 선 형광 분석 결과 SiO2, Al2O3, CaO, K2O, MgO, Fe2O3 및 Na2O 원소가 함유되어 있었다. 양이온 교환능은 148.6 meq/100 g이었으며 열시차 및 열중량 분석 결과 600℃까지 열적으로 안정성이 우수한 것을 확인하였다. 시 간에 따른 흡착 평형 실험 결과 세슘(Cs)의 경우 30분이내 스트론튬(Sr)의 경우 8시간이내에 평형에 도달하였으며 세슘(Cs) 및 스트론튬(Sr)의 흡착률은 각각 80% 및 18%를 보이고 있었다. 단일 성분 등온 흡착 실험 결과 Langmuir model에 부합하였으며 세슘(Cs) 최대 흡착량은 131.5 mg/g으로 높게 나타났으며 반면 스트론튬(Sr) 최 대 흡착량은 29.5 mg/g로 낮은 흡착량을 나타내었다. 본 연구에 사용된 천연 제올라이트의 경우 클라이놉티로라 이트, 휼란다이트 및 모데나이트와 같은 8-ring을 포함하는 광물의 함량이 높아 세슘(Cs)에 대한 높은 선택성을 보 여주고 있다.

Ca-형과 Na-형 벤토나이트는 물성의 차이로 인하여 그 용도를 달리하며, 국내에서는 Ca-형 벤토나이트만 산출되기 때문에 산업체에서는 Na-형으로 변환시켜 토목용이나 주물용으로 활용되고 있다. 이 연구는 Ca-형과 Na-형 벤토나이트의 몇 가지 물성을 비교하여 그 차별성을 명확히 밝히고자 한다. 또한 HDTMA(Hexadecyltrimethylammonium)나 CP(Cetylprydinium)와 같은 유기양이온을 Ca-형과 Na-형 벤토나이트에 치환시켜 유기 양이온과 벤토나이트와의 흡착 특성을 비교 하고자 시도되었다. Na-형 벤토나이트는 Ca-형 벤토나이트에 비해 강한 알카리성, 매우 높은 팽윤성과 점도를 나타내나, 양이온 교환능과 MB(Methylene Blue) 흡착양은 변화를 보이지 않는다. 탁도는 Na-형 벤토나이트가 높으며 시간의 변화에 따라서도 거의 변화가 초래되지 않았으나, Ca-형 벤토나이트는 단시간 내 급격하게 응집이 초래되었다. 열 분석 결과 큰 차이는 보이지 않으나 흡착수와 층간수의 분해는 Na-형 벤토나이트가 보다 저온에서 빨리 일어나며, 완전한 구조의 분해는 Ca-형 벤토나이트가 Na-형 벤토나이트보다 저온에서 용이하게 일어났다. HDTMA와 CP를 벤토나이트에 치환케 되면 대체적으로 강한 층간팽창이 초래되어 저면 간격이 40 a 이상 늘어남으로써 공간을 제공하여 연속적인 흡착이 초래되었다. HDTMA의 흡착은 양이온 교환능의 200% 이상을 치환하였을 때 거의 포화상태에 달하여 저면 간격이 37～38a으로 팽창이 초래되었으나, CP의 흡착은 양이온 교환능의 140% 이상을 치환케 되면 저면 간격이 40a에 달하여 거의 포화되었다. 이는 CP가 HDTMA보다 용이하게 층간팽창을 초래시키고 흡착이 일어남을 의미한다. CP와 Ca-형 및 Na-형 벤토나이트와의 흡착거동은 L형의 흡착등온선을 나타내었으며, 매우 규칙적이고 일관성 있게 흡착이 일어남으로써 안정한 상태를 유지하였다. 또한 층간 교환성 양이온 종에 관계없이 유기양이온 흡착거동은 거의 동일하게 일어났다.