The evolvement in the microstructure and electrical properties of PAN-based carbon fibers during high-temperature carbonization were investigated. The study showed that as the heat treatment temperature increases, the change of carbon fiber resistivity around 1100 °C can be divided into two stages. In the first stage, the carbon content of the fiber increased rapidly, and small molecules such as nitrogen were gradually released to form a turbostratic of carbon crystal structure. The resistivity dropped rapidly from 3.19 × 10− 5 Ω·m to 2.12 × 10− 5 Ω·m. In the second stage, the carbon microcrystalline structure gradually became regular, and the electron movement area gradually became larger. At this time, the resistivity further decreases, from 2.12 × 10− 5 Ω·m to 1.59 × 10− 5 Ω·m. During carbonization, the tensile strength of carbon fiber first increased and then decreased. This is because the irregular and disordered graphite structure is formed first. As the temperature rose, the graphite layer spacing decreased and the grain thickness gradually increases. The modulus also gradually increased.

Polyacrylonitrile (PAN)-based carbon fibers (CFs) and their composites, CF-reinforced plastics, have garnered significant interest as promising structural materials owing to their excellent properties and lightweight. Therefore, various processing technologies for fabricating these advanced materials using thermal energy have been intensively investigated and developed. In most cases, these thermal energy-based processes (heat treatment) are energy and time consuming due to the inefficient energy transfer from the source to materials. Meanwhile, advanced processing technologies that directly transfer energy to materials, such as radiation processing, have been developed and applied in several industrial sectors since the 1960s. Herein, general aspects of radiation processing and several key parameters for electron-beam (e-beam) processing are introduced, followed by a review of our previous studies pertaining to the preparation of low-cost CFs using specific and textile-grade PAN fibers and improvements in the mechanical and thermal properties of CF-reinforced thermoplastics afforded by e-beam irradiation. Radiation processing using e-beam irradiation is anticipated to be a promising method for fabricating advanced carbon materials and their composites.

This study demonstrates that low processing rate for producing polyacrylonitrile (PAN)-based carbon fiber is a critical to obtain a homogeneous radial microstructure with high resistance to oxidation, thereby resulting in their improved mechanical strength. The dry-jet wet spun PAN organic fibers were processed (e.g., stabilized and then carbonized) utilizing two different rates; one is 1.6 times longer than the other. The effect of processing rate on the microstructural evolutions of carbon fibers was analyzed by scanning electron microscopy after slow etching in air, as well as Raman mapping after graphitization. The rapidly processed fiber exhibited the multilayered radial structure, which is caused by the radial direction stretching of the extrusion in the spinning. In case of the slowly processed fiber, the layered radial structure formed in the spinning process was changed into a more homogeneous radial microstructure. The slowly processed fibers showed higher oxidation resistance, higher mechanical properties, and higher crystallinity than the rapidly processed one. Raman mapping confirmed that the microstructure developed during spinning was sustained even though fiber was thermally treated up to 2800 °C.

Polyacrylonitrile (PAN)-based carbon fibers have high specific strength, elastic modulus, thermal resistance, and thermal conductivity. Due to these properties, they have been increasingly widely used in various spheres including leisure, aviation, aerospace, military, and energy applications. However, if exposed to air at high temperatures, they are oxidized, thus weakening the properties of carbon fibers and carbon composite materials. As such, it is important to understand the oxidation reactions of carbon fibers, which are often used as a reinforcement for composite materials. PAN-based carbon fibers T300 and T700 were isothermally oxidized in air, and microstructural changes caused by oxidation reactions were examined. The results showed a decrease in the rate of oxidation with increasing burn-off for both T300 and T700 fibers. The rate of oxidation of T300 fibers was two times faster than that of T700 fibers. The diameter of T700 fibers decreased linearly with increasing burn-off. The diameter of T300 also decreased with increasing burn-off but at slower rates over time. Cross-sectional observations after oxidation reactions revealed hollow cores in the longitudinal direction for both T300 and T700 fibers. The formation of hollow cores after oxidation can be traced to differences in the fabrication process such as the starting material and final heat treatment temperature.

The process of oxidizing polyacrylonitrile (PAN)-based carbon fibers converts them into an infusible and non-flammable state prior to carbonization. This represents one of the most important stages in determining the mechanical properties of the final carbon fibers, but the most commonly used methods, such as thermal treatment (200°C to 300°C), tend to waste a great deal of process time, money, and energy. There is therefore a need to develop more advanced oxidation methods for PAN precursor fibers. In this review, we assess the viability of electron beam, gamma-ray, ultra-violet, and plasma treatments with a view to advancing these areas of research and their industrial application.

In this study, the oxyfluorination of PAN-based carbon fibers was undertaken at room temperature using fluorine-oxygen mixtures, and the influence of oxyfluorination on properties was investigated. The surface characteristics of the modified fiber were determined by using X-ray photoelectron spectroscopy (XPS) and dynamic contact angle analyzer. The oxyfluorination of carbon fibers was one of the more effective methods to increase surface wettability by the formation of semicovalent C-F bond and C-O bond depending on reaction conditions. When oxygen mole fraction is increased from 0.5 to 0.9, it is probable that attached fluorine atoms at the surface of the fibers reacted with other components. As increased oxyfluorination time and decreased its pressures, semi-covalent peak is increased at 0.5 of oxygen mole fraction. The total surface free energy of oxyfluorinated carbon fibers decreased with increasing oxygen mole fraction over 0.5. These results indicate that the surface of carbon fibers became much more hydrophilic after the short oxyfluorination. The surface free energy of oxyfluorinated carbon fibers progressively decreased after 10 min treatment. The polar components of surface free energies were however, significantly higher for all oxyfluorinated samples than that for the untreated carbon fiber.