The physical and antibacterial properties of ophthalmic lenses fabricated by copolymerization with hydrogel monomers using two types of graphene were measured, and their usability as contact lens materials was analyzed. For polymerization, silicone monomers, including SID-OH, 3-(methacryloxy)propyl tris(trimethylsiloxy)silane, and decamethylcyclopentasiloxane, were used, and N,N-dimethylacetamide, ethylene glycol dimethacrylate as a crosslinking agent, and azobisisobutyronitrile as an initiator were added. Also, graphene oxide nanoparticle (GON) and graphene nanoplate (GNP) were used as an additive, and the physical properties of the lenses fabricated after copolymerization were evaluated. The fabricated lenses satisfied the basic physical properties of general hydrogel contact lenses and showed the characteristics of lenses with high water content, and the disadvantage of very weak durability, due to low tensile strength. However, it was confirmed that the tensile strength and antibacterial properties were greatly improved by adding GON and GNP. With GON, the oxygen permeability and refractive index of the fabricated lenses were slightly improved. Therefore, it was determined that the graphene materials used in this study can be used in various ways as a contact lens material.

Purpose: This study was to assess the influence of silicone hydrogel contact lenses wearing time on corneal higher-order aberrations (HOAs), visual performance, and subjective ocular symptoms. Methods: Thirty subjects took part in this study. Subjects were fitted with silicone hydrogel contact lenses (Biofinity). Best-corrected visual acuity (VA) at two contrast levels (100% and 10%) and best-corrected contrast sensitivity (CS) for four spatial frequencies (3, 6, 12, and 18 cycles per degree) were measured under photopic and mesopic conditions. Corneal HOAs were measured with 4-mm and 6-mm pupils using Wavefront Analyzer. All measurements were performed respectively after 2 hours and 9 hours wear with the silicone hydrogel lenses during a day. Subjects were asked by a study examiner to complete the questionnaire for contact lens-related subjective ocular symptoms. Results: Data for this study were employed for fifty-four eyes (27 subjects; 14 females, 13 males) and the subjects were 24.30 ± 2.96 years. For the subjects, current or previous experience with contact lenses was 23 subjects and non-experience with contact lenses was 4 subjects. Regarding visual quality under photopic and mesopic conditions, there was no statistically significant difference in high contrast and low contrast visual acuity as well as contrast sensitivity between 2 hours and 9 hours wear. For corneal HOAs, we also did not find any significant changes in total HOAs, third-order, fourth-order, coma, and spherical aberration for both 4-mm and 6-mm pupils between the two wearing time. In the relative frequency of contact lens-related subjective ocular symptoms, there were statistically differences in discomfort, dryness, and closing eyes between 2 hours and 9 hours wear within the brand (p=0.031, p=0.001, and p=0.031, respectively) (after 9 hours of the lens wear, discomfort (52%), dryness (74%), and closing eyes (56%)); however, there were no significant differences in changeable vision and removing lenses between the two wearing time. Conclusions: Silicone hydrogel contact lenses used this study do not reduce optical quality of the eye and visual quality after nine hours of the contact lens wear during a day. However, the majority of soft contact lens wearers still encounter clinically significant ocular symptoms including discomfort and dryness with the silicone hydrogel lenses.

목 적: 비구면과 구면 실리콘하이드로겔 콘택트렌즈를 착용시킨 후 고위수차와 시력의 질을 비교 평가 하였다. 방 법: 근시안 25명(나이: 24.32±2.87세)을 대상으로 Biofinity 비구면 실리콘하이드로겔 렌즈와 Acuvue Oasys 구면 실리콘하이드로겔 렌즈를 각각 착용시킨 후, 밝은 조명 (photopic)과 어두운(mesopic) 조명 상태에서, 고대비 및 저대비 시력검사와 3, 6, 12, 18의 공간주파수를 포함하는 대비감도검사를 시행하 였다. 파면수차 분석기를 이용하여 4 mm와 6 mm의 동공 크기에 따른 눈의 고위수차를 렌즈 착용 전과 렌즈 착용 상태에서 각각 측정하였고, 이틀 동안 하루에 한 종류의 렌즈를 착용하였으며 모든 검사는 단안으로 이루어졌다. 결 과: 밝은 조명과 어두운 조명 상태에서 검사한 고대비시력과 저대비시력은 비구면렌즈와 구면렌즈 사이에서 통계적으로 유의한 차이가 없었다. 대비감도는 어두운 조명 상태의 공간 주파수 12cpd에서 두 렌즈 디자인 사이에 유의한 차이가 보였지만(p=0.012), 다른 공간주파수 에서는 조명 상태에 상관없이 유의한 차이가 없었다. 두 종류의 렌즈를 착용한 후 각각의 고위수차 양은 4 mm와 6 mm 동공크기 모두에서 렌즈 착용 전의 고위수차 양를 감소시킨 것으로 나타났으며, 두 렌즈 디자인 사이에서 구면수차만 통계적으로 유의 한 차이가 있었고(4 mm 동공에서 p=0.002; 6 mm 동공에서 p=0.001), 다른 고위수차들은 동공크기에 관계없이 유의한 차이가 없었다. 결 론: 비구면 디자인의 실리콘하이드로겔 콘택트렌즈는 구면 실리콘하이드로겔 렌즈와 비교하여 임상적으로 시력의 질은 차이가 없는 것으로 나타났다.

목 적: 전기분해 자동분석법(polarographic method)을 이용한 산소침투성 측정장비의 신뢰도를 평가하 고, 하이드로겔 및 실리콘 하이드로겔 콘택트렌즈 재질들의 산소침투성(Oxygen permeability; Dk)을 측정 하여 제조사에서 제시된 값과 비교하고자 하였다. 방 법: Dk 값이 제시되어 있는 -3.00D의 하이드로겔 및 실리콘 하이드로겔 재질의 콘택트렌즈 8종을 선 정하고, 전기분해 자동분석기를 이용하여 산소침투성을 측정하였다. 각 측정 표본은 국제표준화기구(ISO) 규정에 따라 측정하고 Fatt와 Chasten의 계산식을 이용하여 보정하였다. 결 과: 8종의 시료 가운데 5종은 제조사에서 제시한 Dk 값보다 약간 높게 측정되었으며, 3종은 제조사에 서 제시한 값보다 다소 낮게 측정되었다. 한 가지 두께의 측정값을 이용하여 계산한 Dk 값과 여러 가지 두 께의 측정값들을 이용하여 계산한 Dk 값은 큰 차이가 있었으며, 여러 가지 두께의 측정값들을 이용하여 계 산한 Dk 값의 신뢰성이 더 높았다. 결 론: 3종의 콘택트렌즈는 제조사에서 제시한 Dk 값보다 다소 낮게 측정되었으나, 편차를 감안한 값들 의 일부는 제시된 Dk 값을 기준으로 ISO에서 정한 오차 범위 안에 포함되어 있었다. 본 연구에 사용된 전기 분해 자동분석기의 성능은 ISO 규격에 적합하며, Dk 값을 측정할 때 여러 가지 두께의 콘택트렌즈를 측정하 여 계산하는 것이 타당하다고 사료된다.

목적: In vitro 조건 하에서 재질이 다른 실리콘 하이드로겔 렌즈에 결합되는 눈물의 지방성분인 올레산(oleic acid), 올레산에스테르(oleic acid methyl ester) 및 콜레스테롤(cholesterol)을 각각 정량하여 실리콘 하이드로겔렌즈에 부착되는 지방침전물을 비교하였다. 방법: Lotrafilcon A, lotrafilcon B, galyficon A 및 balafilcon A 재질의 실리콘 하이드로겔 렌즈와polymacon 렌즈 및 RGP 렌즈를 올레산, 올레산에스테르 및 콜레스테롤을 동일한 양 포함하는 식염수 용액에 담가 37℃에서 흔들어주면서 24시간 동안 오염시킨 후, methanol과 chloroform을 1:1(v/v) 비율로 포함하는 유기용매를 이용하여 4시간 동안 렌즈에 부착된 지방을 추출하였다. 추출된 지방은 C-18 column을 사용하여 HPLC(high performance liquid chromatography)를 수행하여 분리하고 정량하였다. 결과: 실리콘 하이드로겔렌즈에 부착된 지방의 총량은 재질의 종류에 따라 48~67 ㎍/lens, polymacon 렌즈와 RGP 렌즈에서는 각각 18 ㎍/lens, 177 ㎍/lens로 측정되어, 실리콘 하이드로겔렌즈의 지방 부착량은 polymacon 소프트렌즈의 300~372%, RGP 렌즈의 30.5~37.8%로 나타났다. 지방침전물은 galyfilcon A 재질에 가장 많이 부착되었으며(p