In this study, the deformation of friction stir welding on the aluminum battery housing material(AL6063-T5) applied to the electric vehicle was effectively predicted through experiments and numerical simulations. The temperature data were measured during the friction stir welding experiment, and the numerical simulation was carried out using the experimental temperature data. In the heat transfer analysis, the temperature distribution of the structure over time was calculated using the Reynolds equation. The final friction stir welding deformation was calculated by performing the structural analysis using the calculated temperature distribution data over time. The thermal elasto-plastic analysis was performed according to the friction stir welding process conditions and the welding sequences. Finally, the optimum welding condition was derived that the welding speed is 1000 mm/min and the rotation speed of the tool is 2000 RPM.

정치망 어선에 사용하는 더블 캡스턴 드럼의 용접공정은, 순간적으로 집중투입되는 고온열원에 의해 상당 열응력과 열변형 거동이 시간의 경과에 따라 비정상적으로 발생한다. 유한요소법으로 이것들의 거동을 해석한 후 다음과 같은 결론을 얻었다. 1) 용접 초기에는 용접열원 위치에서 54∼48MPa의 상당 열응력을 나타내고, 캡스턴 드럼의 내부로 진행될수록 42∼18Mpa 정도의 열응력 분포를 보이며, 열응력 구배는 1mm당 3.6MPa의 기울기를 형성하고 있었다. 용접열원에서 0.004∼0.015mm정도의 미세한 변형량이 계산되었고 좌측 자유단으로 진행하면서 0.03∼0.033mm의 변형량은 용접초기에 열충격 현상으로 발생한 것으로 사료되므로 이에 대한 대비책이 있어야 한다. 2) 용접 중반부에서는 상당 열응력 크기는 용접 초기보다 다소 작아져서 최대 51MPa, 최소 11.3MPa을 보여주며 열응력 기울기도 다소 완화된다. 이것은 용접 열원이 이동하면서 발생하는 예열효과로 상당 열응력이 감소한 것으로 사료된다. 상당 열변형의 크기는 최대 0.04mm, 최소 0.0045mm 정도를 형성하고 있고, 용접열원의 진행으로 전체적인 변형 양상이 용접진행 방향과 동일하게 이동하고 있다. 3) 용접공정의 후반부는 상당 열변형량이 최소 0.005mm, 최대 0.045mm 정도이므로, 정밀한 용접가공을 위해 반대방향에 지그나 고정구를 설치해야 한다. 상당 열응력의 구배는 모재 내부로 진행된 양상을 보이고 있으나 열응력의 절대 크기는 최소 3MPa에서 최대 27MPa로 작아졌다. 이 것은 용접의 이동열원이 제거됨으로서 모재 내부의 열응력이 현저히 저하되었음을 의미하지만, 잔류 열응력이 존재하므로 뜨임처리와 같은 후처리가 요망된다.