        1.
        2022.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Magnetically separable and reusable zinc ferrite/reduced graphene oxide ( ZnFe2O4/rGO) nanocomposite has been prepared by hydrothermal method. The results illustrate that the construction of ZnFe2O4 and rGO occur concurrently in a hydrothermal reaction that initiates the formation of rGO-wrapped ZnFe2O4 nanospheres. The morphological and structural features of the ZnFe2O4/ rGO nanocomposites reveal that the rGO nanosheets anchored to the ZnFe2O4 sphere act as a self-protective clamping layer to avoid the photo corrosion effect under photo irradiations. The nanocomposites express the soft magnetic behavior with high saturation magnetization under annealing temperature at 300 °C, which may attribute to the well-defined crystalline structure and surface defects. In addition, the GZF 300 nanocomposites exhibit the enhanced photocatalytic degradation over Rhodamine B dye which is 3.4, 1.15, and 1.32 times higher than that of ZF, GZF, and GZF 600 over under visible irradiation in 120 min. The GZF 300 nanocomposites demonstrate their ability to degrade RhB efficiently, even after several photocatalysis cycles with high catalyst recovery by its magnetically separable behavior. The high densities of oxygen defects improvise electron transfer from ZnFe2O4 to rGO and delay the recombination process of the nanocomposite, resulting in enhanced visible photocatalytic activity. The strong magnetic properties of rGO wrapped ZnFe2O4 nanocomposite catalysts the easy separation from the suspension system for multiple usages in water treatment.
        4,300원
        2.
        2006.09 구독 인증기관·개인회원 무료
        Mechanochemical synthesis of zinc ferrite, ZnFe2O4, was attempted from a powder mixture of iron (III) oxide, alpha-Fe2O3 and zinc (II) oxide, ZnO. Nanocrystalline zinc ferrite, ZnFe2O4 powders were successfully synthesized only bymilling for 30 hours. Evidence of the ZnFe2O4 formation was absent for the powders milled for 10 and 20 hours; the milling lowered the crystallinity of the starting materials. Heating after milling enhanced the formation of ZnFe2O4, crystal growth of ZnFe2O4 and the unreacted starting materials. The unreacted starting materials decreased their amounts by heating at higher temperatures.