Boron nitride nanotubes (BNNTs) are receiving great attention because of their unusual material properties, such as high thermal conductivity, mechanical strength, and electrical resistance. However, high-throughput and highefficiency synthesis of BNNTs has been hindered due to the high boiling point of boron (~ 4000℃) and weak interaction between boron and nitrogen. Although, hydrogen-catalyzed plasma synthesis has shown potential for scalable synthesis of BNNTs, the direct use of H2 gas as a precursor material is not strongly recommended, as it is extremely flammable. In the present study, BNNTs have been synthesized using radio-frequency inductively coupled thermal plasma (RF-ITP) catalyzed by solid-state ammonium chloride (NH4Cl), a safe catalyst materials for BNNT synthesis. Similar to BNNTs synthesized from h-BN (hexagonal boron nitride) + H2, successful fabrication of BNNTs synthesized from h-BN+NH4Cl is confirmed by their sheet-like properties, FE-SEM images, and XRD analysis. In addition, improved dispersion properties in aqueous solution are found in BNNTs synthesized from h-BN +NH4Cl.

꼬막, 참굴, 바윗굴 및 가리비 등 폐기되는 몇 종의 패각류를 이용하여 칼슘 보강용 식품 첨가제의 원료로써 사용 할 수 있는 고순도의 탄산칼슘을 제조하고자 하였다. 꼬막 패각을 900℃에서 5시간 회화한 회화분의 칼슘 함량이 64.9%로 가장 높게 나타났으며, 가리비 62.5%, 참굴 62.4%, 바윗굴 61.5% 순이었다. 백색도는 가리비 패각 회화분의 경우 81.6-85.8로서 패각류 중 가장 높았다. 꼬막 패각 회화분(Ca 39.92%)에 ammonium chloride process(ACP)와 ammonium nitrate process(ANP)법을 적용하여 제조한 CaCO₃의 Ca 함량은 40.03-40.04%로 높아졌고, ANP법에 의해 제조한 pH조정 시료의 경우가 40.04%로서 가장 높았으며, 이 방법들에 의해 불순물이 거의 대부분 제거되는 것으로 나타났다. ACP법과 ANP법에 의해 제조한 CaCO₃의 백색도는 101.0-101.5로 매우 우수하였으며, 칼슘보강용 식품첨가제로서 사용될 가능성이 충분하다고 판단된다.