We investigate the effect of phosphorous content on the microstructure and magnetic properties of Fe83.2Si5.33-0.33xB10.67-0.67xPxCu0.8 (x = 1–4 at.%) nanocrystalline soft magnetic alloys. The simultaneous addition of Cu and P to nanocrystalline alloys reportedly decreases the nanocrystalline size significantly, to 10–20 nm. In the P-containing nanocrystalline alloy, P atoms are distributed in an amorphous residual matrix, which suppresses grain growth, increases permeability, and decreases coercivity. In this study, nanocrystalline ribbons with a composition of Fe83.2Si5.33-0.33xB10.67- 0.67xPxCu0.8 (x = 1–4 at.%) are fabricated by rapid quenching melt-spinning and thermal annealing. It is demonstrated that the addition of a small amount of P to the alloy improves the glass-forming ability and increases the resistance to undesirable Fex(B,P) crystallization. Among the alloys investigated in this work, an Fe83.2Si5B10P1Cu0.8 nanocrystalline ribbon annealed at 460oC exhibits excellent soft-magnetic properties including low coercivity, low core loss, and high saturation magnetization. The uniform nanocrystallization of the Fe83.2Si5B10P1Cu0.8 alloy is confirmed by high-resolution transmission electron microscopy analysis.

본 연구는 국내외 여건으로 침체되고 국내 인삼산업 활성화에 필요한 인삼가공식품의 경쟁력 제고를 위하여 대표 인삼제품인 홍삼토닉의 소비자 선호속성을 선택실험법을 통해 분석하였다. 실험에 사용된 선호속성으로는 재배연근, 우수농산물(GAP) 인증 여부, 당류함량, 가격이 포함되었으며 총 1,796개의 실험에 대한 답변을 취득하여 각 속성에 대한 가치를 다항로짓모형을 이용하여 추정하였다. 그 결과, 6 년근 원료를 사용하여 우수농산물(GAP) 인증을 받은 저당도 제품에 대한 선호도를 화폐가치로 환산하였다. 이를 정리하면, 5년근 대비 6년근 원료를 사용한 제품에 약 94,000원, GAP 인증을 받지 않은 경우에 비해서 약 89,000원, 당을 1g 줄인 경우 약 5,000의 추가지불의사금액을 확인할 수 있었다. 따 라서 단기적으로 GAP 인증된 6년근 원료를 사용한 저당의 제품 개발이 필요하며, 인삼 GAP 인증에 대한 지원과 홍보가 필요할 것으로 보인다. 한편 인삼 농가 생산성 개선을 위해 저년근 인삼 효능에 대한 과도한 저평가를 개선하기 위한 장기적인 노력이 병행되어야 할 것으로 보인다.

Boron nitride nanotubes (BNNTs) are receiving great attention because of their unusual material properties, such as high thermal conductivity, mechanical strength, and electrical resistance. However, high-throughput and highefficiency synthesis of BNNTs has been hindered due to the high boiling point of boron (~ 4000℃) and weak interaction between boron and nitrogen. Although, hydrogen-catalyzed plasma synthesis has shown potential for scalable synthesis of BNNTs, the direct use of H2 gas as a precursor material is not strongly recommended, as it is extremely flammable. In the present study, BNNTs have been synthesized using radio-frequency inductively coupled thermal plasma (RF-ITP) catalyzed by solid-state ammonium chloride (NH4Cl), a safe catalyst materials for BNNT synthesis. Similar to BNNTs synthesized from h-BN (hexagonal boron nitride) + H2, successful fabrication of BNNTs synthesized from h-BN+NH4Cl is confirmed by their sheet-like properties, FE-SEM images, and XRD analysis. In addition, improved dispersion properties in aqueous solution are found in BNNTs synthesized from h-BN +NH4Cl.

In this study, ultra-fine soft-magnetic micro-powders are prepared by high-pressure gas atomization of an Fe-based alloy, Fe-Hf-B-Nb-P-C. Spherical powders are successfully obtained by disintegration of the alloy melts under high-pressure He or N2 gas. The mean particle diameter of the obtained powders is 25.7 μm and 42.1 μm for He and N2 gas, respectively. Their crystallographic structure is confirmed to be amorphous throughout the interior when the particle diameter is less than 45 μm. The prepared powders show excellent soft magnetic properties with a saturation magnetization of 164.5 emu/g and a coercivity of 9.0 Oe. Finally, a toroidal core is fabricated for measuring the magnetic permeability, and a μr of up to 78.5 is obtained. It is strongly believed that soft magnetic powders prepared by gas atomization will be beneficial in the fabrication of high-performance devices, including inductors and motors.

In order to improve the water environment at urban streams in Korea, several river restoration projects have been initiated for past few years. This study evaluates the impact of diverting water application at the riverhead of Onchun stream through the monitoring program for several water quality and ecological parameters. Various water quality parameters and ecological item such as benthic macroinverterates has been investigated between 09/05 and 12/06. Analysis indicates that the application of diverting water from Nakdong river to Onchun stream distinctly improved several water quality parameters such as, PH, BOD, TN, TP and concentrations of heavy metals. Low flow augmentation also improve ecological indicies such as the diversity index of benthic macroinvertebrates. Generally speaking, releasing addition water from head water of Onchun stream improves various water environmental characteristics.

The toxicity values of various heavy metals were evaluated by acute immobilization and chronic reproduction impairment tests, using Daphnia magna. Acute tests were evaluated by the inhibition of their mobilization after 24hrs without food addition. The tests of reproductive impairment were investigated for 21 days by food addition and exchange of water. The effect of each concentration was assessed by Probit analysis and t-test. The results obtained from this study were as follows : 1) The change of pH and DO was not significant in the acute tests, while, in the reproductive tests, pH was increased by 0.3∼1.4 and DO also increased. 2) The EiG50 values of immobilization to Daphnia magna in artificial fresh water were 0.030㎎/ℓ(Cu), 0.054㎎/ℓ(Cd), 0.12㎎/ℓ(Cr), 0.74㎎/ℓ(Pb), 3.4㎎/ℓ(As) and the NOEiC values were 0.010㎎/ℓ(Cu), 0.018㎎/ℓ(Cd), 0.010㎎/ℓ(Cr), 0.10㎎/ℓ(Pb), and 1.8㎎/ℓ(As). 3) The EiC50 values of reproductive impairment to Daphnia magna were 13.8㎍/ℓ(Cu), 2.9㎍/ℓ(Cd), 15.5㎍/ℓ(Cr), 61.7㎍/ℓ(Pb), 759㎍/ℓ(As), and NOErC values were 0.95㎍/ℓ(Cu), 0.54㎍/ℓ(Cd), 1.2㎍/ℓ(Cd), 7.4㎍/ℓ(Pb), 110㎍/ℓ(As). The results of tests using OECD artificial culture water were more sensitive than natural water for culturing. The presented data show that an artificial culture water is suitable in the experiment of bioassay for assessing the toxicity of materials.