Cavitation can occur in pipes when liquid is moving at high velocity, especially at pittings where the smooth bore of the pipe is interrupted. The effect is usually to produce pitting on the downstream side of the turbulence. However, stress corrosion cracking behavior under cavitation erosion-corrosion was neatly unknown. In this study, therefore, some were investigated of stress corrosion cracking behavior, others were stress corrosion cracking behavior under cavitation erosion-corrosion of water injection. And datas obtained as the results of experiment were compared between the two. Mainresult obtained are as follows: 1) Stress corrosion cracking growth rate of heat affected zone under cavitation erosion-corrosion becomes most rapid, and stress intensity factor K1becomes most high. 2) Stress corrosion cracking growth mechanism by cavitation erosion-corrosion is judgement on the strength of the film rupture model and the tunnel model. 3) The range of potential as passivation of heat affected zone is less noble than that of base metal, and that value is smaller. 4) Corrosion potential under cavitation erosion-corrosion in loaded stress is less noble than that of stress corrosion, and corrosion current density is higher.

The effect of fluid flow on corrosion and erosion-corrosion of metal is a well-recognized phenomenon in pipelines and machinery equipment, and so on. Not only are fluid hydrodynamics important, but also the corrosiveness of the process or production stream affects the corrosion system. Recent research demonstrates that it is possible to erosion-corrosion(E/C) phenomena in terms of hydrodynamics, electrochemical corrosion kinetics and film growth/removal phenomena. Stress corrosion cracking behavior under cavitation erosion-corrosion of mild steel(SS41) was investigated of base metal and weldment under loaded stress. Main result obtained are as follows : 1) The cavitation erosion sensitivity of base metal affected weight loss is more susceptive than heat affected zone, 2) The corrosion sensitivity affected weight loss of welding heat cycle is less susceptive on stress corrosion under cavitation erosion-corrosion than stress corrosion.

The component materials threatened by cavitation include ship propellers as well as turbine runners, pump impellers, pipe lines and radiators. Today it is known that cavitation damage takes place on many other components including on the coding water side of the cylinder liners of diesel engines. Cavitation erosion - corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. To suppress cavitation erosion as well as cavitation erosion - corrosion to hydraulic equipment, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. In this study, we investigated that the cavitation erosion - corrosion damage under vibratory cavitation can be reduced by adding of side now velocity to the cavitation bubble group in order to eliminate bubbles formed in sea water environment.

Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquids corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. To suppress cavitation erosion as well as cavitation erosion-corrosion to hydraulic equipments, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. This study was tested by using the piezoelectric vibrator with 20kHz, 24μm for cavitation generation. And also, the vibratory cavitation erosion-corrosion tests on commercial mild steel SS41were carried out. We carefully observed the erosion pattern and surface photography. The geometrical mechanism of pit growth, which is to be likely these processing; shallow typelongrightarrowundercut typelongrightarrowwide shallow type.

각종 환경 조건에서 진동 캐비테이션 침식-부식 시험 장치에 의해 연강(SS41)의 캐비테이션 침식-부식 손상 거동에 관한 연구를 한 결과 다음과 같은 결론을 얻었다. 1) 해수 중에서 캐비테이션 침식-부식 손상 거동은 중앙부와 테두리 부에서 거의 비슷한 정도로 발생하여 성장되지만, 증류수 중에서는 테두리부에서 손상이 먼저 발생한 다음 중앙부에도 손상이 점차 일어난다. 2) 비저항이 낮은 수도수 중의 캐비테이션 침식-부식 손상은 초기에는 비저항이 높은 증류수중에서의 것보다 증가하지만 시간이 경과하면서 CaCO 하(3)의 피막 형성에 의해 둔화된다. 3) 케비테이션 침식-부식 손상 특성은 잠복기, 증가기, 감소기 및 안정기의 4단계로 구분된다.

Recently, with the rapid development in the industries such as an iron mill and chemical plants, there is enlarged by the use of the piping. Sepecially, the piping connected with a fluid, if it is increase the speed of running fluid, ought to generate cavitation phenomenon with unbalanced pressure. So, the cavitation phenomenon cause serious damage of the piping, because it generate erosion and corrosion in the piping. In this study, the steel pipe piping water (SPPW) and SPPW on weldment were tested by using of cavitation-erosion test apparatus with nozzle and were investigated under the marine environment of liquid. (specific resistance : 25 Omega. cm) The main results obtained are as follows : 1) The total weight loss and weight loss rate of affected zone of weldment by corrosion-erosion in the sea water are more increased than that of base metal. 2) The electrode potential by corrosion-erosion in the sea water becomes less noble than that of base metal, and current density is more increased. 3) As time goes by, the total weight loss and weight loss rate by cavitation erosion-corrosion in air-liquid 2 phase flow become more increased then those in only liquid solution. but these values turn to be decreased.

Recently. with the rapid development in large sea water systems. there occurs much interest in the study of erosion-corrosion. In this study. the mild steel(SB41) was tested by using of a erosion-corrosion test apparatus with fountain-jet and was investigated under the environments of liquid, air-liquid 2 phase flow and solid particle-liquid 2 phase flow. Main results obtained are as follows : 1. The weight loss by corrosion-erosion in air-liquid 2 phase flow are more increased than that in only liquid solution. 2. Effect of air-liquid 2 phase flow on corrosion-erosion sensitivity becomes more sensitive in natural seawater than that in distilled water. 3. The corrosion potential by corrosion-erosion in air-liquid and solid particle-liquid 2 phase flow becomes noble than that of only liquid solution.

In this paper, the behaviour of cavitation erosion, influence of corrosion and corrosion control on slide bearing metals for internal combustion engine were investigated, and this experiment was done by the vibratory cavitation erosion tester. The main results obtained are as follows: 1. With decreasing the space between horn and specimen, the weight loss and its rate increased step by step. But the weight loss and its rate of 0.2mm space decreased conversely more than that of 0.4mm space at early stage. 2. The weight loss and its rate with change of pH were appeared to the order of pH2>pH12>pH7>pH4. And the weight loss and its rate at pH 4 decreased at best. 3. The weight loss and its rate by cavitation erosion for bearing metals were shown to the order of W.M7>W.M1>K.M4. 4. There appeared mainly small pit hole at pH2, and appeared the pit of netting thread type at pH12 by the results of the damaged surfaces at pH2 and pH12 environments that were sensitive to cavitation erosion. 5. With increasing the viscosity of lubricating oil, the weight loss rate by cavitation erosion became dull at the space below 0.5mm. 6. The protective efficiency of cavitation erosion-corrosion is superior inhibitor of chormate(25 ppm) to cathodic protection.

이상으로부터 부분 캐비테이션이 발생하는 익형에 대하여 지금까지 사용된 경계층 제어법과는 달리 전자력 가속에 의하여 익형의 전연 부근에서 흐름을 가속시킨 결과 경계층의 억제에 의해 부분 캐비테이션의 두께 및 길이가 다소 감소하였음을 알 수 있었다. 앞으로의 연구는 캐비테이션의 종류 및 조건들에 맞는 최적의 유동속도 가속장치 설계가 이루어 져야 할 것으로 생각된다.

유압관로에서의 캐비테이션 발생 기구를 조사할 목적으로, 과도흐름에 수반하여 발생하는 캐비테이션 초생에 관한 실험 및 압력이 급강하 할 때의 기포 성장에 대한 계산을 행하였다. 실험에서 얻은 결과를 기초로 한 계산에서, 작동유가 절대압 영이하의 부압에 노출되어도 캐비테이션이 발생하지 않을 정도의 장력을 갖기 위해서는 소위 말하는 기포(기포 주위의 액체가 연속체로 간주될 수 있을 정도의 크기를 갖는 기포)가 유중에 존재할 가능성은 거의 없음이 입증되었다.

초음파 캐비테이션 현상이란 강한 초음파 조사 조건에서 매질(주로 유체) 내에서 미세기포를 발생시키고, 천이시키는 물리적 현상을 의미한다. 본 연구에서는 초음파 캐비테이션 발생량의 정량적 평가를 위하여 초음파 조사조건에 따른 기포군의 초음파 음향 특성변화를 관찰하였다. 중심 주파수가 500 kHz. 1.1 MHz인 곡면형 단일 초음파 변환기를 이용하여 캐비테이션 현상을 발생시켰으며, 형성되는 기포군을 가로지르는 2.25 MHz 간섭 초음파를 송/수신하여 분석하였다. 본 연구에서는 캐비테이션 발생량 평가를 위한 파라미터로 투과하는 파의 중심주파수 변화 및 감쇠 특성, 전파시간을 제시하였으며, 캐비테이션 발생 조건(조사 강도 및 여기 신호, 중심주파수)에 따른 변화를 관찰하였다. 획득된간섭 초음파 수신신호를 분석한 결과, 중심 주파수의 변화의 경우 상관계수는 낮지만 조사 강도에 따른 상관관계를 확인할 수 있었으며, 특정 조사 조건에서 주목할 만한 급격한 중심 주파수 변화가 관찰되었다. 조사조건에 따른 간섭 초음파의 감쇠 추세는 모든 조건에서 높은 상관관계를 보였으며, 캐비테이션 발생형태에 영향을 받지 않는 것으로 확인되었다. 조사조건에 따른 전파 시간의 변화는 관찰되지 않았다. 차후 다양한 조사조건에 대한 평가를 통하여 보다 정량적인 캐비테이션 발생량 평가가 가능할 것으로 판단되며, 이러한 정량적 평가는 고강도 초음파 치료에서 발생할 수 있는 현상에 대한 기초 연구로서 활용 가능할 것으로 사료된다.

콘크리트 도로 상판 또는 터널 라이닝의 배면 공동은 구조물의 함몰 또는 붕괴로까지 이어질 가능성이 있다. 이 공동을 비파괴로 검출하기 위한 방법 중의 하나가 저주파수대 레이더(GPR)의 사용이다. 그러나 이와 같은 토목구조물에는 분해능이 좋지 않은 저주파수대의 레이더를 사용할 수밖에 없기 때문에 작은 공동의 크기나 두께까지 탐사하는 일은 현재 기술로는 거의 불가능하다. 본 연구는 이와 같은 문제와 한계를 극복하기 위해 다양한 공동의 크기와 두께, 깊이를 대상으로 많은 량의 실측 실험을 통해, 저주파 레이더 측정치와 공동 간의 상관관계를 분석함으로 해서 공동의 깊이, 크기와 두께까지를 추정하기 위한 새로운 해석방법을 제안하고 그 적용성을 검토하였다. 또한 본 검토에서는 공동만을 그 크기(횡폭)에 맞게 화상처리에 의해 나타낼 수 있는 역치를 산정하였다. 그 결과, 본 연구에서 제안된 방법에 의해 실험실 수준에서는 정도 좋게 공동의 깊이와 크기, 두께를 추정하는 것이 가능하였다.