Spherical monosized pure aluminum (Al) particles are successfully fabricated by the pulsated orifice ejection method (POEM). The surface reaction between Al and the graphite crucible is investigated by analysing the microstructure and chemical composition of the materials. No significant chemical reaction occurs between Al and the graphite owing to the crystalline Al oxide (γ-Al2O3) layer generated in the initial state. The γ-Al2O3 layer is clearly observed in all regions between the Al particles and graphite via transmission electron microscopy and confirmed by the selected area diffraction pattern. The morphology of the γ-Al2O3 layer perfectly follows the surface morphology of the graphite crucible, which showed nanoscale roughness. This implies that molten Al could not directly contact graphite even though the surface of the crucible became rough to some extent. However, this passivation phenomenon allowed the successful fabrication of monosized pure Al particles. Therefore, POEM is a useful process at least to manufacture monosized pure Al particles.

본 연구의 목적은 혼산 화물의 폭발사고에 대한 화학반응 경로를 분석하는데 있다. 분석에는 사건-가지분석기법을 적용한 구조 적인 시나리오를 이용하였다. 구조적인 시나리오는 재결서에 기록된 혼산 화물 사고의 내용에서 다양한 화학반응 경로를 추정하여 구축하 였다. 분석에는 화학 이론에 의거한 정성적 분석과 화학 반응식을 이용한 정량적 분석 및 설문조사를 통한 확률적 분석 등 세 가지 방법을 혼합 적용하였다. 분석결과, 사고 발생의 주요 경로는 진한 황산과 물이 반응하여 폭발하는 경로, 혼산과 금속이 반응하여 폭발하는 경로, 특수한 물질과 합성하여 폭발하는 경로 등 세 가지로 나타났다. 이 결과는 재결서에 기록된 경로와 유사함을 알았고, 이를 통해서 본 연구 에서 제안한 화학물질의 경로분석 기법이 타당함을 알았다. 본 연구에서 제안한 방법은 다양한 화학물질 사고의 화학반응 경로 추정에 적 용 가능할 것으로 기대된다.

고온 용융염 전해환원 공정은 후행핵연료 주기의 대안 공정인 파이로공정의 산화물 사용후핵연료의 확대 를 위해 필수적인 공정이다. 사용후핵연료는 다성분 산화물로 이루어져 있으며 각 산화물은 전해환원 공정 에서 화학적 특성에 따라 산소를 잃게 된다. 본 연구에서는 건식분말화 공정 이후 전해환원 반응기에 도입되 는 사용후핵연료 조성을 기준으로 각 금속-산소 시스템을 독립적인 이상고용체로 가정하여 전해환원 반응거동을 계산하였다. 전해환원을 Li의 환원과 이어지는 Li과의 화학반응의 결합으로 산정하여 U을 비롯한 금 속 환원 거동을 계산하였다. 계산결과 대부분의 산화물들은 전해환원 공정에 의해 금속으로 전환되는 것으 로 예상되었다. 란타나이드 원소들의 경우 Li2O의 농도가 낮아지면 금속 전환율이 높아지나 대부분 산화물로 존재하는 것으로 나타났다. 추가적으로 U3O8의 전해환원 거동에 대해 Li의 확산과 Li과의 화학반응을 고려하 여 반실험적 모델이 제시되었다. 실험데이터를 활용하여 매개변수를 결정하였으며 시간에 대한 환원율 및 전류에 대한 99.9% 환원 시간을 계산하였다.

The magnetron sputtering was used to deposit Ni buffer layers on the polyimide surfaces to increase the adhesion strength between Cu thin films and polyimide as well as to prevent Cu diffusion into the polyimide. The Ni layer thickness was varied from 100 to 400Å. The adhesion strength increased rather significantly up to 200Å of Ni thickness, however, there was no significant increase in strength over 200Å. The XPS analysis revealed that Ni thin films could increase the adhesion strength by reacting with the polar C=O bonds on the polyimide surface and also it could prevent Cu diffusion into the polyimide. The Cu/Ni/ polyimide multilayer thin films showed a high stability even at the high heating temperature of 200˚C, however, at the temperature of 300˚C, Cu diffused through the Ni buffer layer into polyimide, resulting in the drastic decrease in adhesion strength.

The application of Carbon and graphite based materials in unprotected environment is limited to a temperature of 450℃ or so because of their susceptibility to oxidation at this temperature and higher. To over come these obstacles a low cost chemical vapour reaction process (CVR) was developed to give crystalline and high purity SiC coating on graphite and isotropic C/C composite. CVR is most effective carbothermal reduction method for conversation of a few micron of carbon layer to SiC. In the CVR method, a sic conversation layer is formed by reaction between carbon and gaseous reagent silicon monoxide at high temperature. Characterization of SiC coating was carried out using SEM. The other properties studied were hardness density and conversion efficiency.

Ag powder was prepared from by wet chemical reduction method using various reduction agent system involving , (AgCl) and Ag complex ion aqueous solution. The pure Ag powder could be prepared regardless of reaction system but the particle shape and distribution were affected very much according to the kind of reduction agents and reaction systems. The optimum reaction system for the preparation of the silver powder having the uniform particle shape and size distribution was Ag complex ion aqueous solution-reduction agent system and in particular, and as a reduction agent leaded the more uniform particle shape and size distribution

본 연구에서는 준 회분식 교반조를 사용하여 polybutene (PB)와 polyisobutylene (PIB)고분자를 용해한 벤젠 용액을 연속상, 물을 불연속상으로 구성한 w/o 에멀션액막에 CO2을 흡수시켜 흡수속도를 측정하였다. 점탄성을 나타내는 Deborah 수를 사용하여 점탄성 비뉴튼액체에서 구한 부피물질전달계수 (kLa)를 고찰하고, 수용액에 첨가한 2-amino-2-methyl-1-propanol(AMP)와 CO2의 반응 메카니즘을 해석하였다.

수도품종명 도열병 저항성 차이와 도체내 성분과의 관계를 구명코저 저항성 품종, 중간정도 품종, 감수성인 품종의 실소 및 당 함량을 비교한 결과를 요약하면 다음과 같다. 1) 전질소, 전당 함량은 저항성인 품종이 감수성인 품종에 비해 전질소는 적고 전당은 많았다. 따라서 C/N 률은 저항성 품종이 감수성인 품종에 비해 높았다. 2) Free amino acid에 있어서는 저항성인 품종이 감수성인 품종에 비해 Glutamine, Valine 그리고 Leucine 과 Iso-leucine함량이 많았다. 3) 각종당액에서 전분합성은 저항성인 품종이 감수성인 품종에 비해 Fructose, Glucose에서는 높았고 Sucrose에서는 낮았으나 Indica type로 저항성인 Zenith에서는 오히려 전분합성이 감수성인 다다조 보다 떨어졌다. 4) 질소비료를 증시하면 전질소함량은 보비보다 증가하는데 그 증가율은 저항성인 품종에서 낮은 경향이었다. 전당은 분벽초기에 감소되며 그 감소율은 저항성인 품종이 더 떨어졌고 분벽최성기에는 오히려 증가하였는데 그 증가율은 저항성인 품종이 높은 경향이었다.