Al-Cu alloy nano powders were produced by the electrical explosion of Cu-plated Al wires. The composition and phase of the alloy could be controlled by varying the thickness of Cu deposit on Al wire. When the Cu layer was thin, Al solid solution and were the major phases. As the Cu layer becomes thicker, Al diminished while phase prevailed instead. The average particle size of Al-Cu nano powders became slightly smaller from 63 nm to 44 nm as Cu layer becomes thicker. The oxygen content of Al-Cu powder decreased linearly with Cu content. It is well demonstrated that the electrodeposition combined with wire explosion could be simple and economical means to prepare variety of alloy and intermetallic nano powders.

10-50wt% 범위의 W을 함유하는 Ni-W 합금을 전기도금에 의해 제조하였다. 합금 중의 W 량은 전류밀도가 증가함에 따라 증가하였다. 전류밀도가 50mA/cm2이하인 경우 Ni-W합금은 미세한 결정립을 갖는 Ni의 고용체이었으며, 전류밀도가 50mA/cm2이상인 경우 비정질상으로 변화하였다. 이들의 결정질→비정질 천이는 W량이 40-46wt%인 구간에서 일어났으며 반각폭이 3배이상으로 증가하였다. 결정질 합금의 격자상수는 평형상태도 상의 W의 고용한계(약 30wt%)를 초과하는 40wt%까지 연속적으로 증가하는 것으로 나타나 Ni이 W을 과고용하고 있는 상태인 것으로 밝혀졌다. 비정질 Ni-W 합금은 400˚C이상의 온도에서 열처리하면 강한 [111]방향성을 가지며 재결정하였으며, 800˚C이상의 온도에서는 과고용된 W이 석출하였다. 합금조성 및 결정구조의 전류밀도 의존성을 이용하여 Ni-30%W과 Ni-50%W 합금층이 반복되는 결정질/비정질의 다층도금을 제조하였다.