본 연구에서는 PEN 수지 안전관리를 위하여 HPLC-UV검출기를 이용한 2,6-NDC 및 2,6-NDA 분석법을 확립하였다. 분석법 검증 결과, 2,6-NDC 및 2,6-NDA 모두 0.002μg/mL 검출한계, 0.005 μg/mL 정량한계 및 0.05~1 μg/mL의 농도 범위에서 r2= 0.999 이상의 직선성을 확인할 수있었다. 또한 회수율도 90~110%임을 확인할 수 있었다.

The surface of poly(ethylene naphthalate) film applicable to high temerature insulator for convection microwave oven was modified with silicone coating solutions in the presence of silane crosslinking agent. The structure and properties of the PEN films were investigated by using Fourier transform IR spectroscopy, viscometry, microscopy, and tensile tests. The experimental results showed that the coating with silicone enhanced thermal stability up to 200℃, and slightly lowered the tensile strength and elongation of the PEN films. Judging from dimensional stability results the silicone coated PEN films can not be used for higher temperature insulator above 230℃. Serious dimensional contraction of films was obtained during heat treatment at 250℃ even for 1h. However, the surface of those films still have same chemical structure of silicones. Therefore, If we use PEN film prestretched at 230℃ as base one it will be possible to prepare a high temperature insulator up to 230℃. Conclusively, a silicone coated PEN film can be suitable for the application to convection microwave oven door insulator at high temperature up to 230℃.