In this study, an AISI 316 L alloy was manufactured using a selective laser melting (SLM) process. The tensile and impact toughness properties of the SLM AISI 316 L alloy were examined. In addition, stress relieving heat treatment (650oC / 2 h) was performed on the as-built SLM alloy to investigate the effects of heat treatment on the mechanical properties. In the as-built SLM AISI 316 L alloy, cellular dendrite and molten pool structures were observed. Although the molten pool did not disappear following heat treatment, EBSD KAM analytical results confirmed that the fractions of the low- and high-angle boundaries decreased and increased, respectively. As the heat treatment was performed, the yield strength decreased, but the tensile strength and elongation increased only slightly. Impact toughness results revealed that the impact energy increased by 33.5% when heat treatment was applied. The deformation behavior of the SLM AISI 316 L alloy was also examined in relation to the microstructure through analyses of the tensile and impact fracture surfaces.

In this study, three kinds of bainitic steels are fabricated by controlling the contents of vanadium and boron. High vanadium steel has a lot of carbides and nitrides, and so, during the cooling process, acicular ferrite is well formed. Carbides and nitrides develop fine grains by inhibiting grain growth. As a result, the low temperature Charpy absorbed energy of high vanadium steel is higher than that of low vanadium steel. In boron added steel, boron segregates at the prior austenite grain boundary, so that acicular ferrite formation occurs well during the cooling process. However, the granular bainite packet size of the boron added steel is larger than that of high vanadium steel because boron cannot effectively suppress grain growth. Therefore, the low temperature Charpy absorbed energy of the boron added steel is lower than that of the low vanadium steel. HAZ (heat affected zone) microstructure formation affects not only vanadium and boron but also the prior austenite grain size. In the HAZ specimen having large prior austenite grain size, acicular ferrite is formed inside the austenite, and granular bainite, bainitic ferrite, and martensite are also formed in a complex, resulting in a mixed acicular ferrite region with a high volume fraction. On the other hand, in the HAZ specimen having small prior austenite grain size, the volume fraction of the mixed acicular ferrite region is low because granular bainite and bainitic ferrite are coarse due to the large number of prior austenite grain boundaries.

This paper presents a study on the room- and low-temperature impact toughness of hypoeutectoid steels with ferritepearlite structures. Six kinds of hypoeutectoid steel specimens were fabricated by varying the carbon content and austenitizing temperature to investigate the effect of microstructural factors such as pearlite volume fraction, interlamellar spacing, and cementite thickness on the impact toughness. The pearlite volume fraction usually increased with increasing carbon content and austenitizing temperature, while the pearlite interlamellar spacing and cementite thickness mostly decreased with increasing carbon content and austenitizing temperature. The 30C steel with medium pearlite volume fraction and higher manganese content, on the other hand, even though it had a higher volume fraction of pearlite than did the 20C steel, showed a better low-temperature toughness due to its having the lowest ductile-brittle transition temperature. This is because various microstructural factors in addition to the pearlite volume fraction largely affect the ductile-brittle transition temperature and lowtemperature toughness of hypoeutectoid steels with ferrite-pearlite structure. In order to improve the room- and low-temperature impact toughness of hypoeutectoid steels with different ferrite-pearlite structures, therefore, more systematic studies are required to understand the effects of various microstructural factors on impact toughness, with a viewpoint of ductile-brittle transition temperature.

In this study, low-carbon hypoeutectoid steels with different ferrite-pearlite microstructures were fabricated byvarying transformation temperature. The microstructural factors such as pearlite fraction and interlamellar spacing, and cementitethickness were quantitatively measured and then Charpy impact tests conducted on the specimens in order to investigate thecorrelation of the microstructural factors with impact toughness and ductile-brittle transition temperature. The microstructuralanalysis results showed that the pearlite interlamellar spacing and cementite thickness decreases while the pearlite fractionincreases as the transformation temperature decreases. Although the specimens with higher pearlite fractions have low absorbedenergy, on the other hand, the absorbed energy is higher in room temperature than in low temperature. The upper-shelf energyslightly increases with decreasing the pearlite interlamellar spacing. However, the ductile-brittle transition temperature is hardlyaffected by the pearlite interlamellar spacing because there is an optimum interlamellar spacing dependent on lamellar ferriteand cementite thickness and because the increase in pearlite fraction and the decrease in interlamellar spacing with decreasingtransformation temperature have a contradictory role on absorbed energy.

샤피 V-노치 충격 하중-변위 곡선으로부터 얻은 균열정지하중을 이용하여 원자로압력용기강의 균열정지파괴인성(KIa)을 예측할 수 있는 방법을 모색하고 그 타당성을 고찰하였다. 샤피충격 하중-변위 곡선으로부터 얻은 균열정지하중값의 변화는 특성온도로 보정된 지수함수의 형태로 잘 표현될 수 있었다. 특성온도 TPa=2kN은 실험적인 무연성천이온도(TNDT) 및 T41 J과 높은 상관성을 나타냈으며, 원자로압력용기강의 균열정지파괴인성을 표현하는 새로운 특성온도로 사용할 수 있을 것으로 판단되었다. 또한 균열정지하중값의 변화는 파면으로부터 측정된 안정균열길이의 변화와 매우 높은 상관성을 나타내었다. 따라서 무딘 노치를 갖는 시편에 대한 계장화샤피충격시험을 통하여 균열정지하중 및 안정균열길이를 측정하믈써 비교적 정확하게 원자로압력용기강에 대한 하한값의 파괴인성치(KIa)를 평가하는 것이 가능한 것으로 판단되었다.