General D-glass(Dielectric glass) fibers are adaptable to PCBs(Printed circuit boards) because they have a low dielectric constant of about 3.5~4.5. However, very few papers have appeared on the physical characteristics of D-glass fibers. D-glass fibers were fabricated via continuous spinning process using bulk D-glass. In order to fabricate the D-glass, raw materials were put into a Pt crucible, melted at 1650℃ for 2 hrs, and then annealed at 521 ± 10℃ for 2 hrs. We obtained transparent clear glass. The transmittance and adaptable temperature for spinning of the bulk marble glass were characterized using a UV-visible spectrometer and a viscometer. Continuous spinning was carried out using direct melting spinning equipment as a function of the fiberizing temperature in the range of 1368℃ to 1460℃, while the winder speed was between 100 rpm and 200 rpm. We investigated the physical properties of the D-glass fibers. The average diameters of the glass fibers were measured by optical microscope and FE-SEM. The average diameters of the D-glass fibers were 21.36 um at 100 rpm and 34.06 um at 200 rpm. The mechanical properties of the fibers were confirmed using a UTM(Universal materials testing machine). The average tensile strengths of the D-glass fibers were 467.03 MPa at 100 rpm and 522.60 MPa at 200 rpm.

플라즈마 화학기상증착법에 의해 증착된 저유전율 SiOF박막의 물성 안정화를 위하여 증착후 N2O플라즈마로 열처리함으로써 그 특성을 평가하였다. SiOF박막은 대기방치 및 열처리에 불안정한 성질을 가진다. SiOF 박막은 박막내의 F-Si-F 결합의 존재 때문에 흡습현상이 발생하며, 박막내의 F함량이 증가함에 따라 수분 흡수가 증가한다. 또한 열처리를 거치면서 F이 탈착되어 박막내의 F함량이 감소한다. N2O플라즈마 열처리는 표면에 얇은 SiON층을 형성시킴으로써 박막을 안정화시키는데 효과적이었다. 그러나 장시간의 N/sun 2/O플라즈마 열처리는 유전율을 크게 증가시킨다. 따라서 N2O플라즈마 열처리에 의한 유전율의 증가없이 물성을 안정화 시키기 위해서는, 대기방치나 열처리에 의한 안정화 효과를 유지하면서 N2O플라즈마 열처리에 의한 유전율의 증가를 최소화시킬 수 있는 공정의 확립이 필요하다.