Sulfonated poly(arylene ether sulfone) (SPAES) random copolymers have been perceived as alternatives to perfluorinated sulfonic acid ionomers used as polymer electrolyte membranes for fuel cells. SPAES copolymers are suffering from degradation under harsh fuel cell operation conditions. One solution to overcome the decomposition issue is to fill SPAES copolymers into polymeric support films (e.g., poly(tetrafluoro ethylene), PTFE) with interconnected porous structures. It is difficult to fill the SPAES copolymers dissolved in polar aprotic solvents into PTFE support films owing to their different surface energies. In this study, a SPAES nanodispersion in a water-alcohol mixture is used to make defect-free pore-filling membranes where poly(ethylene glycol) oligomers are added to induce advanced morphologies for fast proton conduction.

최근 전자 디스플레이에서 각광받고 있는 터치스크린은 급속한 정보화 사회 속에서 비약적인 발전을 거듭하고 있다. 터치패널은 키보드나 마우스와 같은 입력장치를 사용하지 않고, 화면에 나타난 문자나 특정 위치에 사람의 손 또는 물체가 닿으면 그 위치를 파악하여 특정한 기능을 처리하도록 한 패널이다. 이러한 터치스크린에서의 터치패널용 Ag 페이스트는 대부분 열 경화형 페이스트를 사용하고 있다. 이러한 열 경화형 페이스트는 건조공정에 따른 열에너지 소비와 유기용제에 따른 작업환경 개선의 문제점을 가지고 있다. 본 연구에서는 기존에 사용되는 열 경화형 Ag 페이스트가 아닌 친환경적이고 경제적인 UV 경화형 페이스트를 제조하였다. 현재 시판중인 열 경화형 바인더 대신 UV 경화형 올리고머를 사용하였고 유동특성을 부여하기 위해 단관능 모노머를 첨가하여 전도성 Ag paste 패턴형성을 할 수 있었다. 그 결과 열 경화형 Ag 페이스트만큼 접착력, 경도, 내성 등이 우수하였으며 미세패턴의 재현이 가능했으며 스크린 인쇄를 이용한 친환경적인 패터닝 기술로서의 가능성을 확인할 수 있었다.

Oligomer type anionic surfactants(RmM-Na or RmD-Na were synthesized from C8~C16 long chain alkylvinylether and maleic anhydride (or maleic diethylether). And also their fluorescent anionic surfactants (RmF- Na) were obtained from alkali neutralization which opens the lactone ring of the condensing materials produced by maleic anhydride alkylvinylether copolymer and 3-aminophenol. The measurement results for the surface active properties of water soluble oligomer type anionic surfactants with fluorescent structure (RmF-Na) exhibited a remarkable surface tension lowing property, foam breaking property, and a ernulsing power.

Allylaliphatic carboxylate oligomers were prepared from polymerization giving allyl aliphatic carboxylates in the presence of potassium persulfate in methanol and the α-sulfonation of these allyl aliphatic carboxylates oligomers were carried by direct addition of dry sulfur trioxide. The dispersing performance of oligomer type anionic surfactants and SDS in the aqueous suspension of Fe2O3 and Tio2 particles were evaluated by particle size distribution and ξ-potential measurement. As results, the particles of Fe2O3 and Tio2 were flocculated by addition of small amount of oligomer type anionic surfactants and SDS, then the flocks redispersed by more addition oligomer type anionic surfactants and SDS. The dispersion and flocculation were observed in lower concentration range of oligomer type anionic surfactants than SDS.