This paper is concerned with a test method that can be used to investigate the parameters of the Johnson-Cook constitutive model. These parameters are essential for accurately analyzing material behavior under impact loading conditions in numerical simulation. Ti-6Al-4V alloy (HCP crytal structure) was used as a specimen for the experiments. In the 10−3-103/ s strain rate range, three types of experimental methods (convention, compression and tension) were employed to compare the differences using MTS-810, SHPB and SHTB. Finite element analysis results when applying these parameters were displayed along with the experiment results.

Yttria stabilized zirconia (Y-CSZ) single crystals show plastic deformation at high temperatures byactivating dislocations. The effect of strain rate on the plastic behavior of this crystal was studied. As increasingstrain rate from ε=1.04×10-5sec-1 to 2.08×10-5sec-1 the yield drop was suppressed and resulted in higherYoung's modulus and yield stress. Dislocation structures of the strained crystals were analyzed using atransmission electron microscope to elucidate the plastic behavior of these crystals. In the early stage of plasticdeformation, dislocation dipoles and prismatic dislocation loops were formed in both samples. However,dislocation density was increased by increasing strain rate. Strong sessile dislocations were observed in thesample with higher strain rate, which may cause the higher work hardening.

The purpose of this study was to evaluate the tensile fracture energy absorption capacity of hybrid fiber reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

The purpose of this study was to evaluate the direct tensile fracture behavior of steel fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that SSF suppressed the microcrack around the HSF at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the HSF.

The purpose of this study was to evaluate the direct tensile fracture behavior of fiber hybrid reinforced cement composite by strain rate. Experiment result, it was confirmed that PVA suppressed the microcrack around the steel fiber at the strain rate 101/s, which resulted in the improvement of the pullout resistance of the steel fiber.

The purpose of this study was to evaluate the tensile fracture behavior of fiber hybrid reinforced cement composite according to the strain rate. Experiment result, it was confirmed that the number of cracks and the strain capacity tended to decrease with increasing PVA fiber volume fraction at the strain rate of 101/s.

본 연구에서는 유압식 급속재하 시험 장치를 제작하여 변형 속도에 따른 후크형 강섬유 및 폴리아미드 섬유보강 시멘트 복합체의 압축강도 및 인장강도 특성을 평가하였다. 그 결과, 변형 속도가 증가함에 따라 압축강도, 최대 응력 점에서의 변형 및 탄성계수는 증가하였으 며, 섬유 종류 및 혼입률은 변형 속도에 의한 압축강도의 영향은 크지 않았다. 본 연구에서 평가된 압축강도의 DIF는 CEB-FIP model code 2010 에 비해 상회하였으며, ACI-349의 예측값과 유사한 경향이 나타났다. 인장특성의 경우에도 변형 속도가 증가함에 따라 인장강도와 변형능력 이 크게 향상되었다. 후크형 강섬유보강 시멘트 복합체는 변형 속도가 증가함에 따라 섬유와 매트릭스의 부착력이 증가하는 것에 의해 인장강 도와 변형능력이 크게 향상되었으며, 섬유가 매트릭스로부터 인발되는 파괴 특성이 나타났다. 한편, 폴리아미드 섬유보강 시멘트 복합체의 경 우 섬유와 매트릭스의 부착력이 크기 때문에 섬유가 매트릭스로부터 인발되지 않고 끊어지는 파괴 특성이 나타났으며, 폴리아미드 섬유보강 시멘트 복합체의 인장특성에 대한 변형 속도 효과는 섬유의 인장강도에 큰 영향을 받는 것으로 판단되었다. 이러한 결과로부터 폴리아미드 섬 유보강 시멘트 복합체의 인장강도에 대한 변형 속도의 효과는 후크형 강섬유의 부착력에 대한 민감도 보다 큰 것으로 사료된다.