The microstructure of the 1020 mild steel target in the region ahead of craters, made by colliding against Cu and W-Cu shaped-charge jets. has been investigated in the present work. The region ahead of the crater impacted by the Cu shaped-charge jet reveals grain refinement implying the formation of sub-grains, while that of W-Cu one leads to martensitic transformation indicating that the region was heated up to an austenitic region which was followed by rapid cooling. The pressure of W-Cu shaped-charge jet impacting against the target when calculated is higher than that of Cu one. The microhardness of the region ahead of the crater impacted by the W-Cu shaped-charge jet is also higher than that of the Cu one. The microstructure of W-Cu slug that remains inside of the crater depicts the occurrence of the remarkable elongation of W particles during the liner collapse. The microstructural evolution of the region ahead of the crater is discussed on the basis of the pressure dependency of the ferrite/austenite transformation in the steel.

The microstructure of the reagion of carters, created by Cu and W-Cu shaped charge jets, in a 1020 mild steel target has been intestiaged. The region ahead of the crater created by the Cu shaped charge jet, reveals dramatic grain refinement implying the occurrence of a dynamic recrystallization, while that of W-Cu one dose a martensitic transformation indicative of heating up to an austenitic region followed by rapid cooling.The impacting pressure calculated when the W-Cu shaped charge jet encounters the target is higher than that of the Cu one. The micro-hardness of the region ahead of the crater created by the W-Cu shaped charge jet is also higher than that of the Cu one. The microstructure of W-Cu slug remained in the inside of the craters depicts the occurrence of the remarkable elongation of W particles during the liner collaphse. From these results, the microstructural variation of the region ahead of the crater with Cu and W-Cu shaped charge jets is discussed in trems of the pressure dependency of the transformation region of ferrite and austenite phases.