This research is conducted to analyze the compatibility of used monomers and produce the high functional hydrogel ophthalmic polymer containing silane and nanoparticles. VTMS (vinyltrimethoxysilane), TAVS [Triacetoxy(vinyl)silane] and cobalt oxide nanoparticles are used as additives for the basic combination of SilM (silicone monomer), MMA (methyl methacrylate) and MA (methyl acrylate). Also, the materials are copolymerized with EGDMA (ethylene glycol dimethacrylate) as cross-linking agent, AIBN (thermal polymerization initiator) as the initiator. It is judged that the lenses of all combinations are optically excellent and thus have good compatibility. Measurement of the optical and physical characteristics of the manufactured hydrophilic ophthalmic polymer are different in each case. Especially for TAVS, the addition of cobalt oxide nanoparticles increases the oxygen permeability. These materials are considered to create synergy, so they can be used in functional hydrogel ophthalmic lenses.

This study is carried out to evaluate the commercial feasibility of the room temperature and thermal polymerization method as a lens manufacturing method. All samples are found to be transparent after polymerization, thereby indicating that their physical and surface properties are suitable for hydrogel ophthalmic lenses. The optical and physical properties of the lenses are compared. The water content of the samples that are prepared via a room temperature polymerization process decreases with the addition of MMA as compared to the water content of the samples that are prepared via thermal polymerization. When MMA and DMA are used as an additive for improving functionality, the wettability of the lenses increases. By measuring the AFM, the surface roughness is shown to improve more than MMA and DMA. Therefore, it is judged to be an appropriate process for manufacturing hydrogel lenses with high functionality.

친수성 단량체를 polyvinylidene fluoride (PVDF) 분리막 표면에 열중합으로 lamination하여 분리막을 친수화하였 다. 친수화 처리 후 접촉각은 95°에서 55°까지 감소하였고 수투과량은 10배 이상 증가하였으며 bovine serum albumin (BSA) 흡착량은 1/4 수준으로 감소하였다. 열중합 공정에서 각 공정변수별 영향을 조사하였고 이를 최적화하였다. 단량체 중 dimethyl oxobuthyl acrylamide (DOAA)가 친수성이 높아 다른 단량체에 비하여 친수화 효과가 우수하였다. 단량체의 농도가 증가함에 따라 성능이 향상되었으나 30 wt% 이상의 경우 homopolymerization을 유발하여 성능을 저하시켰다. 개시제로 사용 되었던 azobis (isobutyronitrile)(AIBN)의 활성 온도 범위가 benzoyl peroxide (BPO)의 활성온도 범위보다 넓기 때문에 높은 친수화 효율을 나타내었다. 개시제를 먼저 도포시켜주고 단량체를 나중에 첨가하는 2단계 lamination 방식이 일괄 공급하는 1단계 방식보다 친수화도는 크게 향상됐지만 pore blocking현상이 나타나면서 순수투과도는 매우 감소하였다.

This study experimentally investigated dicyclohexylammonium 2-cyanoacrylate (CA) as a potential comonomer for polyacrylonitrile (PAN) based carbon fiber precursors. The P(AN-CA) copolymers with different CA contents (0.19-0.78 mol% in the feed) were polymerized using solution polymerization with 2,2-azobis(isobutyronitrile) as an initiator. The chemical structure and composition of P(AN-CA) copolymers were determined by proton nuclear magnetic resonance and elemental analysis, and the copolymer composition was similar to the feeding ratio of the monomers. The effects of CA comonomer on the thermal properties of its copolymers were characterized differential scanning calorimetry (DSC) in nitrogen and air atmospheres. The DSC curves of P(AN-CA) under nitrogen atmosphere indicated that the initiation temperature for cyclization of nitrile groups was reduced to around 235℃. The heat release and the activation energy for cyclization reactions were decreased in comparison with those of PAN homopolymers. On the other hand, under air atmosphere, the P(AN-CA) with 0.78 mol% CA content showed that the initiation temperature of cyclization was significantly lowered to 160.1℃. The activation energy value showed 116 kJ/mol, that was smaller than that of the copolymers with 0.82 mol% of itaconic acids. The thermal stability of P(AN-CA), evidenced by thermogravimetric analyses in air atmosphere, was found higher than PAN homopolymer and similar to P(AN-IA) copolymers. Therefore, this study successfully demonstrated the great potential of P(AN-CA) copolymers as carbon fiber precursors, taking advantages of the temperature-lowering effects of CA comonomers and higher thermal stability of the CA copolymers for the stabilizing processes.

Emulsion polymerization was carried out using RMA like MMA, EMA, BMA and Styrene(St.) as monomer for core-shell latex preparation. It was synthesized at 80℃ in the presence of anionic surfactant SLS. FT-IR, TGA and DSC analysis are used to confirm synthesized core-shell emulsion latexes and to investigate the thermal characteristics of them. From analysis of TGA and DSC, the differences of the decomposition rate and the activation energy are not so large. It considers that the pendent group is not affect of the thermal characteristics and stability on core-shell latexes, which is synthesized with RMA and Styrene.

다공성 Poly(propylene) 분리막의 지지 하에 전해질 용액 (EC/DEC 1 : 1 혼합물 내의 LiPF6 1 M 용액) 내에서 DEGDMA [Di(ethylene glycol) dimethacrylate]의 70℃ 열중합을 통하여 겔 고분자 전해질(GPE)막이 합성 되었다. 합성된 겔 고분자 전해질막의 이온전도도 및 전기화학적 안정성은 AC 임피던스법 및 CV (cyclic voltametry)법에 의하여 측정 평가하였다. 겔 고분자를 전해질로, 그리고 양극 및 음극으로는 각각 LiMi0.8Co0.2O2 및 graphite로 이용하여 리튬이온전지(LIB)도 제작하였다. 열중합을 통하여 리튬 이온전지에 적합한 이온전도도(10 -3 S/cm 이상) 및 전기화학적 안정성을 보이면서 자체적인 성상을 유지하는 겔 고분자 전해질막을 얻을 수 있었다. 단량체 함량 5%의 전구체로 제작한 겔 고분자 전지는 단량체 함량이 7.0% 및 10.0%인 경우에 비하여 우수한 고율 및 충-방전 효율을 보였다.