H2S adsorption characteristics of adsorbent made by coffee waste were investigated. For analyses of the manufactured adsorbent, various methods such as scanning electron microscope(SEM), measurements of BET(Brunauer Emmett Teller) surface area, pH, and Iodide adsorption were adopted. As major adsorption characteristics, adsorption equilibrium capacity was measured by using a batch type experimental apparatus for operating variables such as adsorption temperature(25～45℃), adsorbent types. The experimental result showed that the H2S adsorption equilibrium capacity of adsorbent made by coffee waste much more increases with steam activation for the coffee waste.

The effect of Cu content on hydrogen reduction behavior of ball-milled -CuO nanocomposite powders was investigated. Hydrogen reduction behavior and reduction percent() of nanopowders were characterized by thermogravimetry (TG) and hygrometry measurements. Activation energy for hydrogen reduction of nanopowders with different Cu content was calculated at each heating rate and reduction percent(). The activation energy for reduction of obtained in this study existed in the ranging from 129 to 139 kJ/mol, which was in accordance with the activation energy for powder reduction of conventional micron-sized

The brazing adhesion properties of Ag coated W-Ag electric contact on the Cu substrate have been investigated in therms of microstructure, phase equilibrium and adhesion strength. Precoating of Ag layer ( in thickness) on the contact material was done by electro-plating method. Subsequently the brazing treatment was conducted by inserting BCuP-5 filler metal (Ag-Cu-P alloy) layer between Ag coated W-Ag and Cu substrate and annealing at in atmosphere. The optimum brazing temperature of was semi-empirically calculated on the basis of the Cu atomic diffusion profile in Ag layer of commercial electric contact produced by the same brazing process. As a mechanical test of the electric contact after brazing treatment the adhesion strength between the electric contact and Cu substrate was measured using Instron. The microstructure and phase equilibrium study revealed that the sound interlayer structure was formed by relatively low brazing treatment at . Thin Ag electro-plated layer precoated on the electric contact ( in thickness) is thought to be enough for high adhesion strength arid sound microstructure in interface layer.

산업의 발전과 경제규모의 팽창에 따라 에너지소비가 크게 증가되는 가운데 대기오염물질배출이 크게 늘어나면서 심각한 환경문제를 야기하고 있다. 이중에서 황화수소(H2S)는 계란 썩는 냄새가 나는 무색의 유독한 기체로서 인체의 위장이나 폐에 흡수되어 질식, 폐 질환, 신경중추마비 등을 발생시키고 있다. H2S 가스는 폐기물 매립장, 석유 정제업, 펄프공업, 도시가스 제조업, 암모니아공업, 하수처리장 등 다양한 곳에서 발생하고 있으며, 이를 처리하기 위하여 심냉법, 흡수법, 막분리법, 흡착법 등 여러 가지 처리방법이 제시되었다. 본 연구에서는 실험실규모의 장치를 이용하여 바이오매스 커피부산물을 활용한 악취저감용 흡착소재개발을 위해 커피찌꺼기를 대상으로 탄화, 스팀활성처리등의 과정을 거쳐 흡착제를 제조하였으며, BET분석, SEM 등을 이용한 물성분석과 회분식의 흡착평형실험을 통한 흡착특성을 고찰하였다. 실험결과, 커피찌꺼기를 활용하여 탄화 및 활성처리과정을 거치면서 얻을 수 있는 흡착제의 수율은 15~20%에 해당되는 것으로 밝혀졌다. 또한, 커피부산물은 스팀을 이용한 활성처리 과정에서 온도가 증가할수록. 시간이 증가할수록 스팀-탄소 화학반응에 의해 내부기공이 커지면서 비표면적이 증가되는 것으로 밝혀졌다. 아울러, 커피부산물을 소재로한 흡착제의 황화수소 평형흡착능은 활성탄 대비 60~70%의 우수한 성능을 보임으로써, 악취제거용 흡착소재로 활용성이 클것으로 예상되었다.