In this research we tried to make nano-sized TiNx by using planetary milling, and we made the composites double layered of titanium and nano-sized TiNx by using spark plasma sintering apparatus after mixing with the different ratio of pure titanium powder, and they were heat treated at for 30 minutes. The crystal structures of nano-sized TiNx powders and the composites were analyzed by X-ray diffraction (XRD). The microstructures of the powders were analyzed by using scanning electron microscopy (FESEM) and the 40-50 nm size of nano-sized TiNx particle on the surface of agglomerated particles was investigated. With increasing the ratio of nano-sized TiNx of the composites, the microvickers hardness of the composites was increased.

rf PECVB법을 이용하여 붕규산 유리 기판 위에 diamond like carbon(DLC) 박막을 증착하였다. 메탄(CH4)-수소(H2) 혼합 가스를 전구체 가스로 사용하였다. DLC 박막의 형상, 구조 및 광학적 특성은 SEM, 라만 및 UV 스펙트럼으로 분석하였다. 증착 속도는 혼합 가스의 수소 농도에 따라 증가하다가, 혼합 가스 유량이 25 sccm 이상에서는 일정하게 되었다. UV스펙트럼으로 계산한 박막의 optical band gap은 증착 시간과 DC serf bias의 증가에 따라 감소하는 경향을 나타냈으나, 수소함량에 의해서는 거의 영향이 없었다. 박막의 투과율에 가장 큰 영향을 미치는 인자는, 특히 자외선 영역과 가시광선 영역에서, bias 전압이었다.