Recently, the amount of heat generated in devices has been increasing due to the miniaturization and high performance of electronic devices. Cu-graphite composites are emerging as a heat sink material, but its capability is limited due to the weak interface bonding between the two materials. To overcome these problems, Cu nanoparticles were deposited on a graphite flake surface by electroless plating to increase the interfacial bonds between Cu and graphite, and then composite materials were consolidated by spark plasma sintering. The Cu content was varied from 20 wt.% to 60 wt.% to investigate the effect of the graphite fraction and microstructure on thermal conductivity of the Cu-graphite composites. The highest thermal conductivity of 692 W m−1K−1 was achieved for the composite with 40 wt.% Cu. The measured coefficients of thermal expansion of the composites ranged from 5.36 × 10−6 to 3.06 × 10−6 K−1. We anticipate that the Cu-graphite composites have remarkable potential for heat dissipation applications in energy storage and electronics owing to their high thermal conductivity and low thermal expansion coefficient.

In this research we tried to make nano-sized TiNx by using planetary milling, and we made the composites double layered of titanium and nano-sized TiNx by using spark plasma sintering apparatus after mixing with the different ratio of pure titanium powder, and they were heat treated at for 30 minutes. The crystal structures of nano-sized TiNx powders and the composites were analyzed by X-ray diffraction (XRD). The microstructures of the powders were analyzed by using scanning electron microscopy (FESEM) and the 40-50 nm size of nano-sized TiNx particle on the surface of agglomerated particles was investigated. With increasing the ratio of nano-sized TiNx of the composites, the microvickers hardness of the composites was increased.