The purpose of this study is to improve the mechanical properties and develop manufacturing technology through self-soluble alloy powder flame spray coating on the surface of a run-out table roller for hot rolling. The roller surface of the run-out table should maintain high hardness at high temperatures and possess high wear, corrosion, and heat resistances. In addition, sufficient bonding strength between the thermal spray coating layer and base material, which would prevent the peel-off of the coating layer, is also an important factor. In this study, the most suitable powder and process for roll manufacturing technology are determined through the initial selection of commercial alloy powder for roll manufacturing, hardness, component analysis, and bond strength analysis of the powder and thermal spray coating layer according to the powder.

본 연구는 형상기억합금을 이용하여 제조한 신소재 중의 하나인 형상기억복합재료를 소개하고자 한다. 이 복합재료는 TiNi 섬유의 형상기억효과로 금속복합재료의 취약점이라 할 수 있는 기지와 섬유간의 열팽창차이로 인한 인장잔류응력을 제거하고 기지내에 압축잔류응력을 발생시켜 높은 인장강도를 갖는다. 따라서 본 연구에서는 용탕단조법으로 복합재료를 제조한 후 미세조직을 관찰하고 TiNi 섬유의 역변태온도 이상에서 피로실험을 수행하여 복합재료의 피로특성을 검토하였다. 이 결과 363K에서의 피로균열전파제어효과는 섬유체적률과 예변형에 의하여 증가된다.

본 연구는 티타늄과 활성탄소 원료분말을 반응밀링법에 의해 합성시, 밀링시간에 따른 Ti-TiC 복합재료의 미세조직과 기계적 성질에 미치는 TiC vol.% 및 열간압축성형온도의 영향에 관해 조사하였다. 티타늄과 활성 탄소 원료분말을 300시간 밀링 후 5μm이하의 미세한 구형의 Ti-TiC복합분말을 생성시킬 수 있었다. 반응밀링된 분말을 1000˚C이상에서 1시간동안 진공열간압축성형한 경우 이론밀도의 98%에 가까운 우수한 성형체를 얻었으며, TiC입자가 티타늄 기지 전반에 걸쳐 고르게 분산되어 Ti-TiC 복합재료의 기계적 특성을 향상시켰다. Ti-TiC복합재료의 고온안정성을 고찰하기 위해 600˚C등온열처리한 결과 80시간까지는 경도의 큰 변화없이 열적으로 안정하였다. Ti-20vol%TiC 복합재료를 700˚C에서 고온압축시험을 한 경우 330MPa의 높은 항복강도값을 나타내었다.