Various thicknesses of Al-doped ZnO (AZO) films were deposited on glass substrate using pulsed dcmagnetron sputtering with a cylindrical target designed for large-area high-speed deposition. The structural,electrical, and optical properties of the films of various thicknesses were characterized. All deposited AZO filmshave (0002) preferred orientation with the c-axis perpendicular to the substrate. Crystal quality and surfacemorphology of the films changed according to the film thickness. The samples with higher surface roughnessexhibited lower Hall mobility. Analysis of the measured data of the optical band gap and the carrierconcentration revealed that there were no changes for all the film thicknesses. The optical transmittances weremore than 85% regardless of film thickness within the visible wavelength region. The lowest resistivity,4.13×10-4Ω·cm-1, was found in 750nm films with an electron mobility (µ) of 10.6cm2V-1s-1 and a carrierconcentration (n) of 1.42×1021cm-3.

작물 재배 시 사용되는 유기질비료의 GMO 성분 함유여부를 검정하기 위하여 실험을 수행하였다. 시중에 판매되는 유기질 비료 4가지와 대조군으로 일반콩(non-GMO)과 GMO 콩을 사용하였다. 먼저 간편하게 GMO 여부를 확인할 수 있는 strip test를 실시한 결과 유기질 비료 4종 모두에서 GMO가 분석되어 졌다. 따라서 정밀분석을 위하여 각 시료에서 DNA 추출을 시도한 바 CTAB 및 DNA Purification Kit (Promega)를 사용시 DNA 추출이 가능하였다. 현재 콩, 옥수수의 내재유전자 및 GMO 유전자와 관련된 Primer 7종으로 PCR을 수행한 결과 일부 시료에서 GMO 관련 유전자가 분석되어 졌으며, 추후 유기질 비료의 GMO 유전자가 토양에서 비롯된 것인지 GMO 원료에 기인한 것인지에 대한 확인 실험을 수행할 예정이다.