In this study, effects of nutrient and inorganic carbon on single cell emergence during the cultivation of microalgae were observed using colonial green algae, Pediastrum duplex. The concentration of inorganic carbon had significant effect on single cell emergence and its growth, but nitrogen and phosphorus concentration showed minor effects. According to P. duplex cultivation experiment, single cell started to be emerged around 500~750 mg-C/L of inorganic carbon concentration and it was bloomed dramatically at the higher values. And growth of P. duplex was started to be surpressed at the single cell formation concentration. From the results, it could be said that when we operate the microalgae systems for cultivation/harvesting or wastewater treatment, in order to avoid single cell formation, inorganic carbon should be maintained to the proper level

양돈 사료에 발효탄수화물을 첨가하여 돼지의 슬러리에 서 악취물질의 농도를 평가하였다. VFA 분석결과, 분뇨의 SCFA 농도는 대조구, 땅콩껍질, 아몬드피 및 골든화이버 구에서 각각 1,893, 1,591, 1,433 및 1,319 ppm으로 대조구 에서 가장 높았고(p<0.05), 아몬드피와 골든파이버 구에서 가장 낮았다(p<0.05). VFA의 구성을 살펴보면 SCFA 중에 서 아세트산의 비율이 가장 높으며, 다음으로 프로피온산, 부티르산, BCFA 순으로 낮았다. BCFA의 농도는 대조구, 땅콩껍질, 아몬드피 및 골든화이버 구에서 각각 98, 92, 78 및 74 ppm으로 대조구에서 가장 높았고(p<0.05), 골든화이 버 구에서 가장 낮았다(p<0.05). VOC 분석결과, 분뇨의 페 놀류 농도는 대조구, 땅콩껍질, 아몬드피 및 골든화이버 구 에서 각각 97.3, 47.0, 54.3 및 33.3 ppm으로 골든화이버 구 에서 가장 낮았으며, 대조구에서 가장 높았다(p<0.05). 그 리고 p-크레졸 농도가 페놀류 농도의 93~96%를 차지하였 다. 인돌류 농도는 대조구, 땅콩껍질, 아몬드피 및 골든화 이버 구에서 각각 1.8, 1.3, 1.2 및 1.0 ppm으로 발효탄수화 물 처리구간에 차이가 없었으며(p>0.05), 대조구에서 가장 높았다(p<0.05). NH4 +-N의 농도는 대조구, 땅콩껍질, 아몬 드피 및 골든화이버 구에서 각각 1,395, 995, 995 및 836 ppm으로 대조구에서 가장 높았으며, 골든화이버 구에서 가 장 낮았다(p<0.05). 가축의 장내 또는 슬러리에서 발효과정 동안 미생물이 성장을 위해 필요로 하는 에너지가 제한요 소로 작용되면, 미생물은 단백질을 에너지원으로 이용하기 때문에 많은 아미노산이 분해되어 악취물질이 증가 될 수 있다. 따라서 다른 처리구에 비하여 골든화이버 구에서 VOC의 농도가 가장 낮은 것은 골든화이버의 높은 NDF 함량으로(Getachew et al., 2004) 단백질 발효보다 탄수화 물 발효가 활발하게 일어나 악취물질의 농도가 낮았다고 판단된다.

Al-based alloys have recently attracted considerable interest as structural materials and light weight materials due to their excellent physical and mechanical properties. For the investigation of the potential of Al-based alloys, a surface porous Al88Cu6Si6 eutectic alloy has been fabricated through a chemical leaching process. The formation and microstructure of the surface porous Al88Cu6Si6 eutectic alloy have been investigated using X-ray diffraction and scanning electron microscopy. The Al88Cu6Si6 eutectic alloy is composed of an α-Al dendrite phase and a single eutectic phase of Al2Cu and α-Al. We intended to remove only the α-Al phase and then the Al2Cu phase would form a porous structure on the surface with open pores. Both acidic and alkaline aqueous chemical solutions were used with various concentrations to modify the influence on the microstructure and the overall chemical reaction was carried out for 24 hr. A homogeneous open porous structure on the surface was revealed via selective chemical leaching with a H2SO4 solution. Only the α-Al phase was successfully leached while the morphology of the Al2Cu phase was maintained. The pore size was in a range of 1~5μm and the dealloying depth was nearly 3μm. However, under an alkaline NaOH, aqueous solution, an inhomogeneous porous structure on the surface was formed with a 5 wt% NaOH solution and the morphology of the Al2Cu phase was not preserved. In addition, the sample that was leached by using a 7 wt% NaOH solution crumbled. Al extracted from the Al2Cu phase as α-Al phase was dealloyed, and increasing concentration of NaOH strongly influenced the morphology of the Al2Cu phase and sample statement.

This study is conducted to screen compounds affecting ruminal fermentation under in vitro incubation. Saponin, chitosan, metformin, zinc acetate, zinc chloride, zinc oxide, zinc sulfate, ascorbic acid, oil-coated ascorbic acid, nicotinic acid, eastern herb cocktail, charcoal extract and garlic sources (lyophilized and extract) were added to rumen culture fluid at 1.25% of substrate (100% timothy) volume at 24 h incubation. pH, total gas, ammonia, VFAs were measured. Ascorbic acid increased total gas production indicating fermentation level. All zinc compounds significantly decreased (p<0.05) although zinc sulfate increased propionate of volatile fatty acid (p<0.05). In following experiment, ascorbic acid, oil-coated ascorbic acid, garlic lyophilized, herb cocktail and zinc sulfate were added to rumen culture fluid at 2.5% of substrate with 3, 6, 12 and 24 h incubation. Zinc sulfate decreased both ruminal fermentation and VFAs production but ascorbic acid enhanced total gas production. Ascorbic acid increased fermentation regardless of supplement concentration although excessive zinc sulfate decreased fermentation. These results suggest that optimal level of trace compounds might affect ruminal fermentation in ruminant.

미세조류를 activated sludge와 co-culture시켜 N, P 처리효율을 향상시키는 시도가 활발하다. 이에 따라 co-cultrue 상태에서 미세조류의 활성을 평가하기 위한 method가 필요한데, 과거 대부분의 연구에서는 인공폐수성상을 제조 후, organic carbon, nitrogen, phosphorus 제거량을 통한 미세조류의 활성을 평가하였다. 그러나 위 방법으로는 미세조류의 활성도를 정확하게 정량적으로 측정하여 평가하기에는 한계가 있었다. 위문제점을 해결하기 위해 flow cytometry를 이용하여 미세조류와 activated sludge의 co-culture sample을 제조하여 cell counting 및 미세조류의 활성도를 정량적으로 평가 가능한 protocol을 개발하고자 했다. Flow cytometry 란 장치 내에 존재하는 가느다란 관에서 고속으로 흐르는 세포에 레이저 광을 조사하여 각각의 cell에서 발생되는 반사, 산란광을 순간적으로 측정하여 cell을 선별, 수집하는 기능을 갖는 장치를 말한다. 대부분의 cell live, dead 활성도 평가 논문이 flow cytometry로 측정한 data가 활발히 이용되고 있다. 미세조류와 activated sludge cell의 가장 큰 차이점은 cell 내에 chlorophyll 의 포함 여부이며, 위 차이점을 이용하여 flow cytometry를 이용해 cell을 구별했다. Chlorophyll에 630nm 이상의 빛을 조사하게 되면 excited state가 되고, excited electron이 낮은 전위로 이동할 때 fluorescence를 방출한다. 이를 flow cytometry의 fluorescence detector가 인지하여 상대적으로 낮은 fluorescence를 가지는 activated sludge와 높은 fluorescence를 가지는 미세조류를 구분하고, cell membrane이 손상된 dead cell 만을 염색하는 SYTOX Green 염색시약을 sample에 주입하여 live, dead cell을 구별하고 활성도를 평가하는 것이 가능함을 확인하였다.