This study was conducted to evaluate the market potential of 'Hwanggeumsantari', a new oyster mushroom variety developed in Gyeonggi Province in 2019, and to derive effective market entry strategies. To objectively assess the marketability of 'Hwanggeumsantari’ from various perspectives, a panel of 50 consumers was formed, and surveys and interviews were conducted. Additionally, two Focus Group Interviews were held with distributors in the agri-food sector. The results showed that potential consumers were positive about the color and texture of ‘Hwanggeumsantari', but expressed relatively less satisfaction with its shelf life and aroma. Distributors, through tow Focus Group Interviews, evaluated that the product had sufficient market competitiveness, but called for efforts to improve cultivation techniques and enhance price competitiveness. Based on the results of market evaluations by consumers and distributors, a SWOT analysis was conducted. The main strengths identified were its outstanding color and texture, while the main weakness was its freshness issue. Meanwhile, the growing demand for healthy foods and various online sales channels could provide market entry opportunities for ‘Hwanggeumsantari', but high sensitivity to price in the case of premium pricing could pose a threat. Consequently, a market entry strategy for ‘Hwanggeumsantari’ was proposed using a 4P mix approach based on the SWOT analysis results. The product strategy emphasized premium positioning, small packaging, and the development of packaging technology to maintain freshness. The price strategy proposed premium pricing and the operation of incentive programs. The distribution strategy suggested channel diversification, direct stores, or direct sales, while the promotion strategy emphasized storytelling and collaboration with influencers.

Low-density polyethylene (LDPE)와 Styrene-butadiene-styrene (SBS)를 넣은 개질 아스팔트 혼합물은 바인더에 중량 비로 3~6% 첨가하여 여러 가지 특성을 획기적으로 향상시킨 아스팔트 재료이다. 아스팔트 재료의 개질목적은 일반 혼합물의 균 열저항과 소성 변형과 같은 전형적인 약점을 향상시키기 위해서이다. 이 재료들은 많은 장점들을 가지고 있으며 플랜트 적용이 간편하고 현장적용성이 우수한 특정을 가지고 있다. 여러 해 동안의 경험을 통해 습식 개질 아스팔트와 건식 아스팔트 혼합물이 현장에서 실용화할 수 있게 발전되었다. 본 연구에서는 이를 종합적으로 평가하여 그 장단점을 일반 아스팔트 혼합물과 비교 평가하여 LDPE, SBS 개질 아스팔트 혼합물의 특성을 체계적으로 밝히는 것을 본 연구의 목적으로 한다.

본 연구는 국내 현장실정에 적절한 아스팔트 혼합물의 실내노화방법을 개발하기 위한 연구이다. 강제공기순환식 오븐에서 154℃ 2시간의 단기노화를 거친 혼합물로 제작한 공시체를 110℃에서 24, 48, 72, 96시간 동안 장기노화를 시켰다. 또한 노화시간의 증가에 따라 아스팔트 바인더의 노화정도를 측정하기 위하여 GPC 분석을 수행하였다. 본 연구를 통해 노화시간이 길어짐에 따라 대형분자양이 증가하는 것을 확인하였고, 이에 대한 분석으로부터 적절한 인공노화시간의 추정이 가능함을 알 수 있었다. 본 연구에서 수행된 단기노화방법은 다소 과다하나 이를 RTFO와 유사한 수준으로 처리한다면 110℃로 약 48시간 이상 노화를 시키면 PAV 처리와 유사한 수준의 혼합물 노화가능성이 있음을 확인하였다.