To investigate the effect of process parameters on selective laser sintering of Cu/polyamide mixed powder, Cu/polyamide mixed powder was sintered by selective laser with changing laser power and scanning speed. The properties of sintered body were evaluated by measuring the density and tensile strength, and analysis of XRD, FT-Raman and microstructure. With an increase in the laser power, the density and ultimate tensile strength of sintered Cu/polyamide body increase and then decrease. The maximum values of the density and ultimate tensile strength were decreased with increasing laser scanning speed. These changes were concerned with the difference of irradiation energy of laser into the powder layer. It was considered that the change of the mechanical property of the sintered body with irradiation energy of laser is due to the changes of amount of copper particle and property of polyamide.

준안정 Fe-Cr-Ni 3원 오스테나이트 STS강을 90% 냉간압연한 후 여러온도에서 어니링하여 얻은 가공유기 마르텐사이트(α')와 역변태 오스테나이트(γ)와의2상 혼합조직가에 있어서 기게적 성질과 γ안정도와의 관계를 조사하였다. 모든 강들은 90% 냉간압연에 의하여 거의 α'단상조직이 되었고, 변태된 α'는 773~873K의 온도범위에서 급격하게 γ로 역변태하였다. Cr과 Ni함량이 많을수록, 그리고 결정립 미세화에 의해서γ는 더욱 안정화하여 Ms 점의 저하를 초래하였다. Cr량을 적게하여γ를 불안정하게 함으로써 많은 α'를 품는 고강도, 고연성의 초미세립강이 얻어졌다.

Mg-Zn-Ce계 합금에서 비정질 단상 및 hcp-Mg입자분산형 비정질합금이 20-40%, Zn, 0-10%Ce과 5-20%Zn, 0-5%Ce 의 조성범위에서 각각 생성되었다. 초미세 hcp-Mg입자분산형 Mg85Zn12Ce3비정질합금은 급속응고 또는 급속응고리본의 열처리에 의해 Mg입자의 입경을 4-20nm의 범위로 조절할 수 있었으며, 이 범위에서는 밀착굽힘이 가능할 만큼 충분한 인성을 가지고 있었다. 이 합금의 최대인장강도(σB)와 파단 연신율(εf)은 hcp-Mg입자의 체적분율에 따라서 670-930MPa, 5.2-2.0%의 범위였으며, 최대 비강도(σB밀도 =σs)는 3.6 × 105N · m/kg에 달하였다. 이와 같이 Mg입자분산형 비정질 합금의(σB), (σs)그리고 εf의 최대치가 Mg-Zn-Ce계 비정질합금(690MPa, 2.5 × 105N · m/kg, 2.5%)보다 월등하게 높다는 것은 주목할 만 하다. 복합상 조직이 형성됨으로서 기계적 강도가 증가하는 것은 동일 조성의 비정질상보다 강한 hcp과포화 고용체의 분산강화에 기인하는 것이라고 고찰되었다.