Highly crosslinked micron-size monodispersed PMMA/PDVB and PS/PDVB particles were prepared using seeded multi-stage emulsion polymerization. PMMA and PS seed particles were synthesized by seeded multi-stage emulsion polymerization and soap-free emulsion polymerization. Then PMMA/PDVB and PS/PDVB particles were obtained using semi-batch type emulsion polymerized using divinyl benzene as a cross-linkable monomer in the presence of seed particles. PMMA particles with size of ca. 730 nm and polydispersity of 1.03 were successfully prepared in this experiment. PS particles with size of ca. 1.5 μm and polydispersity of 1.01 were prepared in this experiment. Highly crosslinked PS/PDVB particles with size of ca. 1.3 μm and polydispersity of 1.00 were obtained.

An acid cleaning agent (AACA) for aluminum was prepared by blending of sorbitol, n-octanoic acid, MJU-100A, Tetronix T-701, PPA-23, C8-83 and phosphoric acid. With the prepared AACA, degreasing, foam height, etching and derusting tests were carried out. As a result, AACA-4 and AACA-7 showed better cleaning ability than commercial acid cleaning agents.

High-solid coatings were prepared by blending of previosly synthesized acrylic resins and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, cross-hatch adhesion, 60˚specular gloss, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. As a result of Rigid-body pendulum visco-elasticity measurement, dynamic Tg values of cured films increased with dynamic Tg values.