Room temperature cure type of acryl-urethane coatings with high solid content were prepared in this study. Acrylic resins with 80% solid content were cured with hexamethylene diisocyanate (Desmodure N-3600). The cure time of prepared coatings BEHCC-84 (BEHC-84 : Tg=0℃) and BEHCC-87 (BEHC-87 : Tg=30℃), measured by rigid-body pendulum method, was recorded 8.3 hours and 3.8 hours, respectively. Dynamic viscoelastic experiment also revealed the glass transition temperature of BEHCC-84 and BEHCC-87 to be Tg=40.3℃ and Tg=43.3℃, respectively. It was found that the adhesion and flexural properties among various propeties of coatings were enhanced by the incorporation of caprolactone acrylate monomer into the acrylic resins.

An acid cleaning agent (AACA) for aluminum was prepared by blending of sorbitol, n-octanoic acid, MJU-100A, Tetronix T-701, PPA-23, C8-83 and phosphoric acid. With the prepared AACA, degreasing, foam height, etching and derusting tests were carried out. As a result, AACA-4 and AACA-7 showed better cleaning ability than commercial acid cleaning agents.

Low foaming scouring agents (LSSA) were prepared by blending of amine salt of dodecylbenzene sulfone, poly (PO-b-EO) glycol, Newpol PP-2000, MJU-100, ethylene glycol and organic solvent. As the results of several tests, LSSA-2 showed good scouring effect, penetrating ability and emulsifiability, and showed not much water pollution. The foaming power of LSSA-2 measured by Ross & Miles method was 11mm foam height immediately after foaming. And the foaming power of LSSA-2 measured by Ross & Clark method were less than 310mm foam height at 30℃, 17mm at 80℃. As a result, LSSA-2 was proved as a good foaming scouring agent.