The microstructure, hardness, and wear behaviors of a High Velocity Oxygen Fuel(HVOF) sprayed WC-CoFe coating are comparatively investigated before and after laser heat treatments of the coating surface. During the spraying, the binder metal is melted and a small portion of WC is decomposed to W2C. A porous coating is formed by evolution of carbon oxide gases formed by the reaction of the free carbon and the sprayed oxygen gas. The laser heat treatment eliminates the porosity and provides a more densified microstructure. After laser heat treatment, the porosity in the coating layer decreases from 1.7% to 1.2 and the coating thickness decreases from 150 μm to 100 μm. The surface hardness increases from 1440 Hv to 1117 Hv. In the wear test, the friction coefficient of coating decreases from 0.45 to 0.32 and the wear resistance is improved by the laser heat treatment. The improvement is likely due to the formation of oxide tribofilms.

WC-CrC-Ni coatings were prepared by nine processes of the Taguchi program with three levels for the four spray parameters: spray distance, flow rates of hydrogen and oxygen, and powder feed rate. The optimal coating process (OCP) was oxygen flow rate of 38 FMR, hydrogen flow rate of 53 FMR, powder feed rate of 25 g/min, and spray distance of 7 inches. Hardness of 1150 Hv and porosity of 1.2 %, were obtained by OCP; these are better results compared with the highest 1033 Hv and the lowest 1.5% porosity obtained by nine processes of the Taguchi program. Friction coefficient of the WC-CrC-Ni coating decreased from 0.36 ± 0.07 at 25 oC to 0.23 ± 0.07 at 450 oC. These values were smaller than those of the EHC (electrolytic hard chrome) plating at both temperatures due to lubrication from the oxide debris. The wear trace and wear depth of the coating are smaller than those of the EHC at both temperatures. Pitting was not found in the WC-CrC-Ni coating sample, while it did appear in the EHC sample.

The effects of coating parameters were investigated in wear resistance coatings of Diamalloy-406 on Inconel 718 to obtain an optimum coating condition by high velocity oxy-fuel spraying. The coating parameters, the flow rates of source gases (hydrogen and oxygen), the powder feed rate, and the spray distance, were designed by the Taguchi method. The optimal conditions were determined: oxygen flow rate 34 FRM, hydrogen flow rate 57 FRM, powder feed rate 35 g/min, and spray distance 7 inch. Friction coefficients of the coating and the substrate decreased with an increasing sliding surface temperature from 25 oC to 450 oC. The friction coefficient of Diamalloy-4006 coating decreased as the sliding surface temperature increased from 0.43 ± 0.01 at 25 oC to 0.29 ± 0.01 at 450 oC. The wear trace and wear depth of the coating were smaller than the substrate at all temperatures tested. The relationship between spray parameters and wear resistance was discussed extensively, based on the measured roughness, hardness, and porosity in each coating.

본 연구는 산학협력단의 리더십역량, 전략역량 등 핵심역량이 기술이전과 교육 성과에 미치는 영향을 분석한 연구이다. 우선, 산학협력단과 관련한 문헌연구를 실시하였고, 전국 산학협력단을 대상으로 설문조사를 실시하였다. 본 연구에서는 산학협력단 주요 경영 성과인 기술이전성과와 교육성과를 종속변수로 설정하였다. 독립변수로는 리더십역량, 전략 역량, 인적자원역량, 연구개발 역량을 설정하고 각각에 대한 조작적 정의를 부여 하였다. 변 수간 인과관계분석을 위한 연구모형을 제시하였으며, 설문대상 간의 차이 분석을 위해 국공 립 대학과 사립대학을 조작변수로 연구모형에 포함하였다. 실증분석 결과, 독립변수로 적용 한 리더십역량은 기술이전성과와 교육성과에 영향을 미치지 않는 것으로 조사되었으며, 마찬 가지로 전략역량은 교육성과에만 영향을 미치는 것으로 검증되었다. 인적자원역량의 경우에 도 종속변수에 미치는 영향이 없었으며, 연구개발 역량의 경우에는 기술이전성과에 영향을 미치는 것으로 분석되었다. 본 연구의 결과가 산학협력단의 경영성과 개선에 도움이 되기를 기대한다.

고흥지역 일대에 분포하는 백악기 화강암을 대상으로 석영내에 발달해 있는 아문미세균열을 측정하여 연구지역의 고응력장을 분석하였다. 5개의 시료(GH-1, GH-3, GH-4, GH-5, GH-8)에서 아문미세균열들의 방향을 측정하여 분석한 결과, GH-1, GH-3, GH-4에서 최대수평주응력은 N60˚W와 N70˚E, N20˚W, N50˚W의 방향성이 가장 우세하였으며, N-S와 N30˚E의 방향성도 미약하게 나타났다. GH-5와 GH-8시료에서는 최대수평주응력의 방향 N40˚E와 N10˚E가 가장 우세하였고, N40˚W의 방향성도 미약하게 나타났다 전체적인 최대수평주응력의 방향은 N60˚W가 가장 우세하였으며, N20˚W, N20˚E, N70˚E등의 방향성도 미약하게 나타났다. 이 연구의 결과와 기존의 고등력장에 관한 연구결과를 종합해 볼 때, 백악기 말에서 신생대 3기 초 사이 연구지역에 작용한 최대수평주응력의 방향은 WNW에서 NE로 변화했을 것으로 판단되며, 그 원인으로는 그 당시 동북아시아 일대에 일어났던 복잡한 지구조운동에 기인한 것으로 사료된다.

본 실험은 1998년 1월부터 2001년 12월가지 4년간 경기도와 인천지역에 납품된 군납 농산물 17종(배추, 무, 오이, 감자, 사과, 양파, 파, 양배추, 고추, 당근, 상추, 호박, 마늘, 미나리, 시금치, 쑥갓, 부추)을 대상으로 유기염소계 농약 10종 (BHC, captafol, captan, chlorobenzilate, chlorothalonil, DDT, dicofol, endosulfan, folpet, tetradifon)을