Activated carbon (AC) with very large surface area has high capacitance per weight. However, such activation methods tend to suffer from low yields, below 50%, and are low in electrode density and capacitance per volume. Carbon NanoFibers (CNFs) had high surface area polarizability, high electrical conductivity and chemical stability, as well as extremely high mechanical strength and modulus, which make them an important material for electrochemical capacitors. The electrochemical properties of immobilized CNF electrodes were studied for use as in electrical double layer capacitor (EDLC) applications. Immobilized CNFs on Ni foam grown by thermal chemical vapor deposition (CVD) were successfully fabricated. CNFs had a uniform diameter range from 50 to 60 nm. Surface area was 56 m2/g. CNF electrodes were compared with AC and multi wall carbon nanotube (MWNT) electrodes. The electrochemical performance of the various electrodes was examined with aqueous electrolyte of 2M KOH. Equivalent series resistance (ESR) of the CNF electrodes was lower than that of AC and MWNT electrodes. The specific capacitance of 47.5 F/g of the CNF electrodes was achieved with discharge current density of 1 mA/cm2.

Active clays, Diatomite, bentonite and zeolite were used as porous materials for fabricating hygroscopic gypsum boards. Pohang active clay and Cheolwon diatomite showed excellent characteristics of moisture adsorption and desorption. These characteristics were caused by higher surface area and pore volume of porous materials. Moisture adsorption content of gypsum board with 10% active clay(P1) was 62.0 g/m2, and moisture desorption content was 50.2 g/m2. Moisture adsorption content of gypsum board with 10% diatomite(P) was 59.5 g/m2, and moisture desorption content was 49.0 g/m2. Moisture adsorption contents of gypsum boards with porous materials were higher than that moisture desorption contents of gypsum board without porous materials. Correlation coefficient between surface area and moisture adsorption content of gypsum boards was 0.98. Also, correlation coefficient between surface area and moisture desorption content of gypsum boards was 0.97. Moisture adsorption and desorption contents were influenced by surface area and pore volume of the gypsum boards, and surface area had a larger effect on moisture adsorption and desorption.

알루미나 여과막은 boehmite 분말 (-AlOOH)을 이용하여 졸-겔법으로 준비되어졌다. 제조된 여과막은 상전이 온도와 미세구조 변화를 관찰하기 위해 지지체 없이 형성된 여과막을 제조하였다. 여과 공정의 응용에서 균일한 기공크기와 분포를 제어하는 것이 중용하다. 다공성 담체 위에 형성된 여과막과 다공성 담체 없이 형성된 여과막의 θ-to α-AL2O3로의 상전이는 박막 XRD를 이용하여 분석하였고, 미세구조의 변화의 관찰은 주사전자현미경(SEM)을 사용하여 관찰하였다. XRD에서 분석된 결과는 다공성 담체 위에 형성된 여과막이 다공성 담체 없이 형성된 여과막과 비교하여 100˚C 더 높은 상전이 온도를 가지는 것을 보여주었다. 이런 유사한 효과는 여과막의 미세구조 변화에서도 관찰되었다.

To establish the optimal culture systems for production of transferable embryos in Korean Cattle, pregnancy rates of IVF-derived blastocysts according to different culture media, culture method and culture duration were compared. Development of IVF-derived embryos to blastocysts was most effective in YS medium group co-cultre with cumulus cells. Blastocysts cultured for 6 to 8 d in vitro showed higher hatching rate and good quality. Pregnancy rates after transfer of IVF-derived blastocysts cultured for 7 or 8 d were high. Through our experiments, it is considered that improvement of culture media and culture method is necessary for mass production of blastocysts with excellent of good quality in Korean Cattle.

본 연구는 체외에서 생산된 도살장 유래의 한우 배반포를 젖소의 자궁에 이식하여 임신율을 상승시킴으로써 농가의 수정란 이식의 이해 및 그 산업화 촉진의 계기를 마련하고자 실시하였다. 그 결과 배양기간을 단축시키면서도 한꺼번에 많은 양의 배반포를 생산할 수 있는 배양액의 개발이 시급하며, 수정란 이식의 산업화를 위해서는 질 좋은 배반포 생산은 물론이거니와 수란우의 선정을 위한 신기술의 개발 및 숙련된 수정란 이식사의 양성은 대단히 중요하다고 생각한다.

최근 쾌적한 주거환경이 중요시되는 트렌드에 따라 공동주택에서 녹지공간 확보를 위하여 대부분의 주차장이 지하로 옮겨가고 있는 현상을 고려할 때, 공동주택 지하주차장의 건설에 있어 균열에 의한 문제점 발생시 유지보수 관점이 아닌 예방이라는 관점의 새로운 차원에서 연구가 필요했다. 이에 본 연구는 크게 두 가지 취지를 가지고 출발하였다. 먼저 공동주택 지하주차장 균열에 있어 설계 단계와 시공 단계에서의 문제점을 도출하여 전문가 집단에 의한 가중치(중요도) 산정을 통해 실질적인 예방 우선순위를 파악하고, 이에 따른 예방 방안을 제안하고자 하였다. 그 다음으로 지하주차장의 균열을 살펴보고 각 균열 위험의 중요도를 산출하여, 어느 위험이 가장 위험한지를 파악하고, 그것에 중요도를 두어 설계 및 시공시 대처할 수 있는 방안을 제시하고자 하였다. 그러기 위해서 본 연구에서는 선행연구를 통해 균열 요인의 중요성과 균열의 위험도를 도출해 냈으며, 사례를 통해 문제점이 실제로 발생하고 있는 부분을 살펴보았다. 그 다음 도출된 문제점을 전문가를 통한 AHP 기법을 통해 중요도를 산출하였다.