Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at 150℃ for 6 hours, and the results were obtained as follows : Mn=1830~2190, Mw 3290~4000, Mw/Mn=1.80~1.83 viscosity=110~352 cps, and conversion=82~92%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

Fatty polyamide that gives softness, lubrication and bulky property and alkyl imidazoline that gives durable softness and antistatic property were synthesized. then, an O/W-type durable softener (DSN) was prepared by the emulsion of the synthesized fatty polyamide and alkyl imidazoline. Emulsion stability of the DSN was good, and the mixed HLB value was 11.2. From the measurement of softness, lubrication, antistatic property, bending resistance, and color fastness, it was proved that the prepared DSN was a good durable softener for nylon.

Two PU flame-retardant coatings, 2,3-DBPO/N-l00 (DBPON) and 2,3-DBPO/IL (DBPOI), were prepared by curing 2,3-dibromo modified polyester (2,3-DBPO) with isocyanate curing agent Desmodur N-l00 (or Desmodur IL) at room temperature. The physical properties and flame-retardancy of the two coatings were tested and compared. As a result, the pot-life, yellowness index, lightness index difference, 60˚ specular gloss, cross-hatch adhesion, viscosity, and accelerated weathering resistance of DBPON were better than those of DBPOI; the fineness of grind of the two coatings were the same; and the drying time, hardness, and abrasion resistance of DBPOI were better than those of DBPON. The flame retardancy of the flame-retardant coatings increased with the content of the flame retarding component, 2,3-dibromopropanoic acid (2,3-DBP); and the LOI values of the two coatings were in a range of 27~29% when the content of 2,3-DBP was 30wt%.

An ACR/HMMM film was prepared by blending high-solid ACR with curing agent, hexamethoxymethyl melamine (HMMM). An active curing reaction was observed at 170℃. The dynamic viscoelastic Tg of the final film increased with the static viscoelastic Tg of the film. The log damp value, which means a viscoelastic ratio, decreased with the increase in the curing temperature of the film. Physical properties of the films were within a suitable range for films, and by an accelerated weathering resistance test the films were proved weather resistible ones.

충북 영동의 감나무 가로수에서 감꼭지나방(Stathmopodamasinissa)을 태집하여 온도 , 광주기 16L:8D,상대습도 85%의 실내조건에서 이들의 발육생태를 조사하였다. 각 충태 별 발육일수는 알기간 7.4일, 유충기간 34.8일, 번데기기간이 15.5일이었다. 1령에서 5령의 영기간 은 각각 3.5일, 4.2일, 5.2일, 6.5일, 15.4일이었으며, 유충의 두폭은 각각 0.20, 0.40, 0.65, 0.87, 1.07mm이었다. 용화율과 우화율은 각각 68.0%, 59.9%이었다. 성충 수명은 수컷이 6.2일, 암컷이 10.1일이며, 암컷 한마리당 평균 산란수는 24.4개였다.